Next Article in Journal
Ferroelectric Nanoparticles in Liquid Crystals: Recent Progress and Current Challenges
Next Article in Special Issue
Preparation of Nano-TiO2-Coated SiO2 Microsphere Composite Material and Evaluation of Its Self-Cleaning Property
Previous Article in Journal
Influence of Synthesis Temperature on the Growth and Surface Morphology of Co3O4 Nanocubes for Supercapacitor Applications
Previous Article in Special Issue
Ti-Based Biomedical Material Modified with TiOx/TiNx Duplex Bioactivity Film via Micro-Arc Oxidation and Nitrogen Ion Implantation
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 7
Issue 11
10.3390/nano7110359
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Photoelectrochemical Water Splitting Properties of Ti-Ni-Si-O Nanostructures on Ti-Ni-Si Alloy

by
Ting Li
1,
Dongyan Ding
1,*,
Zhenbiao Dong
1 and
Congqin Ning
2
1
Institute of Electronic Materials and Technology, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China
2
State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2017, 7(11), 359; https://doi.org/10.3390/nano7110359
Submission received: 31 August 2017 / Revised: 18 September 2017 / Accepted: 25 September 2017 / Published: 31 October 2017
(This article belongs to the Special Issue ZnO and TiO2 Based Nanostructures)
Browse Figures
Versions Notes

Abstract

:
Ti-Ni-Si-O nanostructures were successfully prepared on Ti-1Ni-5Si alloy foils via electrochemical anodization in ethylene glycol/glycerol solutions containing a small amount of water. The Ti-Ni-Si-O nanostructures were characterized by field-emission scanning electron microscopy (FE-SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and diffuse reflectance absorption spectra. Furthermore, the photoelectrochemical water splitting properties of the Ti-Ni-Si-O nanostructure films were investigated. It was found that, after anodization, three different kinds of Ti-Ni-Si-O nanostructures formed in the α-Ti phase region, Ti2Ni phase region, and Ti5Si3 phase region of the alloy surface. Both the anatase and rutile phases of Ti-Ni-Si-O oxide appeared after annealing at 500 °C for 2 h. The photocurrent density obtained from the Ti-Ni-Si-O nanostructure photoanodes was 0.45 mA/cm2 at 0 V (vs. Ag/AgCl) in 1 M KOH solution. The above findings make it feasible to further explore excellent photoelectrochemical properties of the nanostructure-modified surface of Ti-Ni-Si ternary alloys.

Graphical Abstract

1. Introduction

Titanium dioxide (TiO2) has been intensively investigated as a favorable, eco-friendly photocatalyst owing to its relatively low cost, nontoxicity, and stable chemical properties [1,2]. In 1972, TiO2 was used as a photochemical water splitting catalyst for the first time [3]. Recently, TiO2 was demonstrated to be a promising photocatalyst for photocatalytic water splitting and solar energy conversion with high efficiency and photochemical stability [4,5,6,7,8,9]. However, the wide energy band gap (3.2 eV for anatase and 3.0 eV for rutile) and the fast recombination of photogenerated electrons and holes are the main drawbacks of TiO2-based photoanodes [10]. Therefore, modification strategies including foreign element doping, surface decoration, and sensitization with dye have been adopted to overcome these drawbacks over the last 30 years [11,12,13,14,15,16]. One of the most studied methods is the doping of TiO2 materials with metal ions or nonmetallic elements such as Ni, Ta, Nb, Fe, Zn, C, N, and so on [17,18,19,20,21,22,23,24,25,26].
Ti-alloy-based oxide nanotubes were fabricated through a direct anodization of TiNi binary alloy [17,18]. To date, few studies have been conducted on the anodic fabrication of Ti-Ni-Si-O nanostructures on Ti-Ni-Si alloy substrates. Si has a much lower density than Ti (2.33 g/cm3 for Si vs. 4.54 g/cm3 for Ti) as well as vast natural abundance, and it is environmentally friendly. Zhang et al. [27] found that the presence of Si could impair the recombination of photogenerated electrons and holes effectively. Also, the photocurrent density of Si-doped TiO2 electrodes was 2–3 times higher than that of undoped TiO2 electrodes. In this work, Ti-Ni-Si-O nanostructures were successfully grown on Ti-Ni-Si ternary alloy substrates via electrochemical anodization in ethylene glycol/glycerol solutions containing a small amount of water. The microstructures and photoelectrochemical properties, especially the photochemical water splitting of Ti-Ni-Si-O nanostructures, were investigated.

2. Results and Discussion

Figure 1 presents the typical microstructural features of as-cast Ti-1 wt % Ni-5 wt % Si alloy. Figure 1a shows the presence of multiphase, while Figure 1b shows a higher magnification image of different phases. EDS (energy dispersive spectroscopy) was used to test the compositions in the different phase regions. The EDS results are shown in Table 1. It was found that the gray region was α-Ti matrix, and the average composition of the black network-like region was 76.42 wt % Ti, 0.10 wt % Ni, and 23.48 wt % Si. Combined with the phase diagram calculated by Thermo-Calc software, it could be concluded that they were Ti5Si3 structures. In addition, the bright strip-like region was identified as the Ti2Ni phase [28]. It is noticeable that the quantity of the Ti5Si3 phase was much more than that of the Ti2Ni phase.
For the multi-phase Ti-1Ni-5Si alloy, the anodization process was not a uniform one due to the different anodization characteristics of different phases. Figure 2 shows SEM (scanning electron microscopy) images of different Ti-Ni-Si-O nanostructures grown in the α-Ti phase, Ti2Ni phase, and Ti5Si3 phase regions. Obviously, three kinds of nanostructures formed on the surface of the alloy films. One was a self-organized nanotube array formed in the α-Ti phase region. The second was a nanotube array under the corrosion pits in the Ti2Ni phase region. The third constituted irregular nanopores formed in the Ti5Si3 phase region. The Ti-Ni-Si-O nanotubes formed in the α-Ti phase region and the nanopores formed in the Ti5Si3 phase region had a pore diameter of about 64 nm. Table 2 shows the compositions tested by EDS for the α-Ti phase, Ti2Ni phase, and Ti5Si3 phase regions after anodization. It is noticeable that the Si element was still rich in the Ti5Si3 phase regions while the Ni element was relatively rich in the Ti2Ni phase regions.
The formation of TiO2 nanotubes by anodization can be roughly divided into two steps. In the first step, an initial barrier layer is formed on the electrolyte-metal interface. Then, an oxide barrier layer is randomly distributed by the chemical etching action of fluoride ions, resulting in the growth of nanotubes under the top oxide layer [29,30]. During the final step, the pore growth morphology gradually changes to a homogeneous and self-organized morphology. Thus, a competition between the formation and the dissolution of the oxides always takes place during the anodization process [31]. For the anodization of the Ti-Ni-Si alloy here, the Ti2Ni phase region and Ti5Si3 phase region should have a much quicker dissolution rate in the anodization electrolyte than the α-Ti phase region. For the Ti2Ni phase, the dissolution rate of the oxides was so fast that there was no time to form any nanostructures. Thus, only etching pits were left in this region. In the Ti5Si3 phase region, the dissolution rate was faster than the formation rate of the oxides; thus, it was difficult to form nanotube structures. Instead, nanopores formed in this region. With a slower dissolution rate in the α-Ti phase region, the formation of stable Ti-Ni-Si-O nanotubes became easier than that in the other phase regions. Our previous literature [32] reported the similar phase-dependent anodization of the two-phase Ti6Al4V alloy. Ti-Al-V-O nanotube arrays formed in the α-phase region and irregular Ti-Al-V-O nanopores formed in the V-riched β-phase region of the Ti6Al4V alloy. The solubility of vanadium oxide in the F−-containing electrolyte played an important role in the competition between the formation and dissolution of the oxides. It could be concluded that for the present anodization system, the phase-dependent anodization was hard to control for a uniform formation of nanotube arrays on top of the multiphase substrate.
The as-anodized Ti-Ni-Si-O nanostructures were found to be amorphous, and they could crystallize after the annealing process. XRD was adopted to determine the crystal structure and possible phases during annealing. Figure 3 presents the XRD patterns of the as-anodized and the annealed Ti-Ni-Si-O nanostructures. In the diffraction pattern of the annealed sample, two sharp diffraction peaks centered at 2θ angles of 40.2° and 62.9° were assigned to Ti metal (JCPDS card No. of 65-9622, Jade 5.0) from the substrate. The diffraction peaks at 25.3° and 75.0° could be assigned to the anatase phase (JCPDS card No. 21-1272, Jade 5.0) of TiO2. The peaks at 27.4° and 69.0° represented the rutile phase (JCPDS card No. 21-1276, Jade 5.0) of TiO2. The diffraction peaks at 36.8°, 40.8°, 41.9°, 42.6°, 61.2°, and 66.4° were indexed to the characteristic peaks of Ti5Si3 (JCPDS No. 65-3597, Jade 5.0) from the substrate. No diffraction peaks related to the Ti2Ni phase could be detected by XRD. In the diffraction pattern of the as-anodized sample, neither the anatase phase nor rutile phase could be observed. As shown in Figure 3, the amorphous structure of Ti-Ni-Si-O nanostructures had transformed into both anatase and rutile structures after annealing at 500 °C for 2 h. The anatase phase was found to be the major oxide phase.
Figure 4 shows the UV-Vis diffuse reflectance absorption spectra of the annealed Ti-Ni-Si-O photoanode. The band gap energy of the photoanode was estimated by using Tauc’s method. It was observed that the Ti-Ni-Si-O photoanode showed an absorption edge at 402 nm. The band gap value was 3.08 eV, which was between the anatase band gap (3.2 eV) and the rutile band gap values (3.0 eV). The presence of both the anatase structure and rutile structure was attributed to the obtained band gap value [11].
The photoelectrochemical water splitting behavior of Ti-Ni-Si-O nanostructures is shown in Figure 5. The linear sweep was collected for the Ti-Ni-Si-O photoanodes with a scan rate of 50 mV/s. The photocurrent density was 0.45 mA/cm2 at 0 V (vs. Ag/AgCl). The photocurrent under illumination was distinguishable from the dark current. Figure 4b presents photocurrent density vs. time scans for the Ti-Ni-Si-O photoanodes measured at 0 V (vs. Ag/AgCl). It could be seen that the photocurrent density was 0.45 mA/cm2, which was in accordance to the results of the linear sweep experiment. The samples demonstrated stable and instantaneous changes as well as reproducible responses in the photocurrent after many illumination on/off cycles.
Electrochemical properties for Ti-Ni-Si-O nanostructure photoanodes annealed at 500 °C for 2 h were investigated, and the corresponding results are shown in Figure 6. Figure 6a shows the open-circuit potential (OCP) of Ti-Ni-Si-O photoanodes with time upon turning off the illumination. Without illumination, the OCP was about −0.50 V (vs. Ag/AgCl). As soon as the light was switched on, the OCP rapidly shifted negatively to a value of −0.80 V (vs. Ag/AgCl) due to the photogeneration of electron-hole pairs [33]. When turning off the illumination, the OCP gradually shifted positively to a steady state. These results indicated that the Ti-Ni-Si-O photoanodes had remarkable photoelectric conversion characteristics. The difference between the dark potential and light potential was about 0.3 V, which was the inherent characteristic of TiO2 [34].
The carrier concentration (Nd) and flat-band potential (VFB) can be calculated from the Mott-Schottky equation [35,36]:
1 C 2 = ( 2 e 0 ε ε 0 N d ) [ ( V − V F B ) − k T e 0 ]
where C is the capacitance of the space-charge region, e0 is the electron charge (1.602 × 10−19 C), ε is the dielectric constant of TiO2 (ε = 41.4 for anatase TiO2 and 154.2 for rutile TiO2 [37]), ε0 is the permittivity of free space (8.854 × 10−12 F/m), Nd is the donor density of N-type semiconductor (carriers/cm3), V is the applied potential bias at the electrode, k is the Boltzmann’s constant (1.38 × 10−23 J/K), and T is the absolute temperature. It can be seen that there is a linear relationship between 1/C2 and VFB. Furthermore, the flat-band potential VFB can be calculated from the extrapolation of the line to 1/C2 = 0. Moreover, the carrier concentration can be obtained from the slope of the Mott-Schottky equation. Figure 6b presents Mott-Schottky plots of Ti-Ni-Si-O photoanodes with a frequency of 1000 Hz. It was calculated that the flat-band potential was −0.625 V (vs. Ag/AgCl). The carrier concentration was in the range of 2.13 × 1016/cm3 to 8.57 × 1016/cm3 for Ti-Ni-Si-O photoanodes, which was comparable with those of pure TiO2 photoanodes [23]. Simelys et al. [38] reported that a higher carrier concentration could facilitate the charge separation at the semiconductor-electrolyte interface, and the carrier concentration reached up to 7.05 × 1019/cm3 for the TiO2 nanotubes with a thickness of about 1.5 μm. The samples here showed a positive slope in the Mott-Schottky plots, as expected for an N-type semiconductor.

3. Materials and Methods

Ti-Ni-Si-O oxide films on the alloy substrate were synthesized through a direct anodic oxidation process. Prior to the anodization, the Ti-1Ni-5Si alloy foils with a size of 20 mm × 10 mm × 1 mm were mechanically polished and ultrasonically degreased in acetone and ethanol, rinsed with deionized water, and finally dried in air. The anodization was carried out in a conventional two-electrode electrochemical cell with the alloy foil as a working electrode and the platinum foil as a counter electrode at room temperature. All of the samples were anodized at a pulse voltage of 40 V with a constant frequency of 4000 Hz and a duty cycle of 50% for 90 min in an electrolyte of 5 vol % ethylene glycol/glycerol (Shanghai Lingfeng Chemical Reagent Co., Ltd., Shanghai, China) containing 0.30 M (NH4)2SO4 and 0.4 M NH4F (Sinopharm Chemical Reagent Co., Ltd., Shanghai, China) as well as 3 vol % deionized water. After anodization, the samples were immediately rinsed with deionized water and subsequently dried in air. All of the samples were annealed at 500 °C for 2 h in air to transform amorphous oxide into crystalline phases.
The structure and morphology of the oxide film were characterized through field emission scanning electron microscopy (SEM, FEI SIRION 200, Hillsboro, OR, USA). The chemical compositions were analyzed by energy dispersive spectroscopy (EDS, INCA X-ACT, Oxford, UK). The crystalline phase was characterized with an X-ray diffractometer (Rigaku Ultima IV, Tokyo, Japan) with Cu Kα radiation (λ = 0.15406 nm) at 40 kV and 30 mA with a scan speed of 5°/min over a 2θ range from 10° to 80°. Diffuse reflectance absorption spectra were collected by a UV-visible spectrometer (Perkin Elmer Inc., Lambda 750S, Waltham, MA, USA) with BaSO4 as a reference. The photoelectrochemical measurement of different photoanodes was performed in 1 M KOH solution using a typical three-electrode system with oxide photoanode as a working electrode, Pt as a counter electrode, and Ag/AgCl as a reference electrode. A 150 W Xe lamp (Lanpu XQ350W, Shanghai, China) was used as a light source and the intensity of light illumination was controlled at 100 mW/cm2. The illuminated area of the working electrode was 1 cm2.

4. Conclusions

In summary, Ti-Ni-Si-O nanostructures were successfully fabricated through electrochemical anodization for photoelectrocatalytic water splitting. It was found that after anodization, three kinds of Ti-Ni-Si-O nanostructures grew in the α-Ti phase region, Ti2Ni phase region, and the Ti5Si3 phase region of the alloy surface. Both anatase and rutile structures of Ti-Ni-Si-O oxide appeared after annealing at 500 °C for 2 h. The photocurrent density obtained from the Ti-Ni-Si-O nanostructure photoanodes was 0.45 mA/cm2 at 0 V (vs. Ag/AgCl) in 1 M KOH solution. The above findings make it feasible to further explore the excellent photoelectrochemical properties of the nanostructure-modified surfaces of Ti-Ni-Si ternary alloys.

Acknowledgments

This work was supported by the National Natural Science Foundation of China (No. 51572170). We thank the contribution from the SEM lab at Instrumental Analysis Center of SJTU.

Author Contributions

The experimental design was planned by Dongyan Ding and Ting Li. The manuscript was written with contributions from all authors. All authors have given approval to the final version of the manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Lee, K.; Mazare, A.; Schmuki, P. One-dimensional titanium dioxide nanomaterials: Nanotubes. Chem. Rev. 2014, 114, 9385–9454. [Google Scholar] [CrossRef]
  2. Kudo, A.; Miseki, Y. Heterogeneous photocatalyst materials for water splitting. Chem. Soc. Rev. 2009, 38, 253–278. [Google Scholar] [CrossRef] [PubMed]
  3. Fujishima, A.; Honda, K. Electrochemical photolysis of water at a semiconductor electrode. Nature 1972, 238, 37–38. [Google Scholar] [CrossRef] [PubMed]
  4. Gong, J.; Lai, Y.; Lin, C. Electrochemically multi-anodized TiO2 nanotube arrays for enhancing hydrogen generation by photoelectrocatalytic water splitting. Electrochim. Acta 2010, 55, 4776–4782. [Google Scholar] [CrossRef]
  5. Sreethawong, T.; Junbua, C.; Chavadej, S. Photocatalytic H2 production from water splitting under visible light irradiation using Eosin Y-sensitized mesoporous-assembled Pt/TiO2 nanocrystal photocatalyst. J. Power Sources 2009, 190, 513–524. [Google Scholar] [CrossRef]
  6. Wang, J.; Lin, Z. Freestanding TiO2 nanotube arrays with ultrahigh aspect ratio via electrochemical anodization. Chem. Mater. 2008, 20, 1257–1261. [Google Scholar] [CrossRef]
  7. Wang, J.; Zhao, L.; Lin, V.S.Y.; Lin, Z. Formation of various TiO2 nanostructures from electrochemically anodized titanium. J. Mater. Chem. 2009, 19, 3682–3687. [Google Scholar] [CrossRef]
  8. Ye, M.; Xin, X.; Lin, C.; Lin, Z. High efficiency dye-sensitized solar cells based on hierarchically structured nanotubes. Nano Lett. 2011, 11, 3214–3220. [Google Scholar] [CrossRef] [PubMed]
  9. Xin, X.; Wang, J.; Han, W.; Ye, M.; Lin, Z. Dye-sensitized solar cells based on a nanoparticle/nanotube bilayer structure and their equivalent circuit analysis. Nanoscale 2012, 4, 964–969. [Google Scholar] [CrossRef] [PubMed]
  10. Liu, Q.; Ding, D.Y.; Ning, C.Q.; Wang, X.W. α-Fe2O3/Ti-Nb-Zr-O composite photoanode for enhanced photoelectrochemical water splitting. Mater. Sci. Eng. B 2015, 196, 15–22. [Google Scholar] [CrossRef]
  11. Mohamed, A.E.R.; Rohani, S. Modified TiO2 nanotube arrays (TNTAS): Progressive strategies towards visible light responsive photoanode, a review. Energy Environ. Sci. 2011, 4, 1065. [Google Scholar] [CrossRef]
  12. Yu, K.P.; Yu, W.Y.; Ku, M.C.; Liou, Y.C.; Chien, S.H. Pt/titania-nanotube: A potential catalyst for CO2 adsorption and hydrogenation. Appl. Catal. B 2008, 84, 112–118. [Google Scholar] [CrossRef]
  13. Xing, L.; Jia, J.B.; Wang, Y.Z.; Zhang, B.L.; Dong, S.J. Pt modified TiO2 nanotubes electrode: Preparation and electrocatalytic application for methanol oxidation. Int. J. Hydrog. Energy 2010, 35, 12169–12173. [Google Scholar] [CrossRef]
  14. Gao, Z.D.; Qu, Y.F.; Zhou, X.M.; Wang, L.; Song, Y.Y.; Schmuki, P. Pt-decorated g-C3N4/ TiO2 nanotube arrays with enhanced visible–light photocatalytic activity for H2 evolution. Chem. Open 2016, 5, 197–200. [Google Scholar] [CrossRef]
  15. Lee, W.; Kang, S.H.; Min, S.K.; Sung, Y.E.; Han, S.H. Co-sensitization of vertically aligned TiO2 nanotubes with two different sizes of cdse quantum dots for broad spectrum. Electrochem. Commun. 2008, 10, 1579–1582. [Google Scholar] [CrossRef]
  16. Baker, D.R.; Kamat, P.V. Photosensitization of TiO2 nanostructures with CdS quantum dots: Particulate versus tubular support architectures. Adv. Funct. Mater. 2009, 19, 805–811. [Google Scholar] [CrossRef]
  17. Ding, D.Y.; Ning, C.Q.; Huang, L.; Jin, F.C.; Hao, Y.Q.; Bai, S.; Li, Y.; Li, M.; Mao, D.L. Anodic fabrication and bioactivity of Nb-doped TiO2 nanotubes. Nanotechnology 2009, 20, 305103. [Google Scholar] [CrossRef] [PubMed]
  18. Qin, R.; Ding, D.Y.; Ning, C.Q.; Liu, H.G.; Zhu, B.S.; Li, M.; Mao, D.L. Ni-doped TiO2 nanotube arrays on shape memory alloy. Appl. Surf. Sci. 2011, 257, 6308–6313. [Google Scholar] [CrossRef]
  19. John, K.A.; Naduvath, J.; Mallick, S.; Pledger, J.W.; Remillard, S.K.; DeYoung, P.A.; Thankamoniamma, M.; Shripathi, T.; Philip, R.R. Electrochemical synthesis of novel Zn-doped TiO2 nanotube/ZnO nanoflake heterostructure with enhanced DSSC efficiency. Nano-Micro Lett. 2016, 8, 381–387. [Google Scholar] [CrossRef]
  20. Altomare, M.; Lee, K.; Killian, M.S.; Selli, E.; Schmuki, P. Ta–doped TiO2 nanotubes for enhanced solar-light photoelectrochemical water splitting. Chem.-A Eur. J. 2013, 19, 5841–5844. [Google Scholar] [CrossRef] [PubMed]
  21. Kim, H.I.; Monllor-Satoca, D.; Kim, W.; Choi, W. N-doped TiO2 nanotubes coated with a thin TaOxNy layer for photoelectrochemical water splitting: Dual bulk and surface modification of photoanodes. Energy Environ. Sci. 2015, 8, 247–257. [Google Scholar] [CrossRef]
  22. Ahmed, S.A. Ferromagnetism in Cr-, Fe- and Ni-doped TiO2 samples. J. Magn. Magn. Mater. 2017, 442, 152–157. [Google Scholar] [CrossRef]
  23. Liu, Q.; Ding, D.Y.; Ning, C.Q.; Wang, X.W. Reduced N/Ni-doped TiO2 nanotubes photoanodes for photoelectrochemical water splitting. RSC Adv. 2015, 5, 95478–95487. [Google Scholar] [CrossRef]
  24. Ansari, S.A.; Khan, M.M.; Ansari, M.O.; Cho, M.H. Nitrogen-doped titanium dioxide (N-doped TiO2) for visible light photocatalysis. New J. Chem. 2016, 40, 3000–3009. [Google Scholar] [CrossRef]
  25. Saharudin, K.A.; Sreekantan, S.; Lai, C.W. Fabrication and photocatalysis of nanotubular C-doped TiO2 arrays: Impact of annealing atmosphere on the degradation efficiency of methyl orange. Mater. Sci. Semicond. Process. 2014, 20, 1–6. [Google Scholar] [CrossRef]
  26. Kyeremateng, N.A.; Hornebecq, V.; Martinez, H.; Knauth, P.; Djenizian, T. Electrochemical fabrication and properties of highly ordered Fe-doped TiO2 nanotubes. ChemPhysChem 2012, 13, 3707–3713. [Google Scholar] [CrossRef] [PubMed]
  27. Zhang, Y.; Li, X.; Chen, D.; Ma, N.; Hua, X.; Wang, H. Si doping effects on the photocatalytic activity of TiO2 nanotubes film prepared by an anodization process. Scr. Mater. 2009, 60, 543–546. [Google Scholar] [CrossRef]
  28. Lu, B.C.; Wang, Y.L.; Xu, J. Revisiting the glass-forming ability of Ti-Ni-Si ternary alloys. J. Alloys Compd. 2009, 475, 157–164. [Google Scholar] [CrossRef]
  29. Cai, Q.Y.; Yang, L.X.; Yu, Y. Investigations on the self–organized growth of TiO2 nanotube arrays by anodic oxidization. Thin Solid Film 2006, 515, 1802–1806. [Google Scholar] [CrossRef]
  30. Abdullah, M.; Kamarudin, S.K. Titanium dioxide nanotubes (TNT) in energy and environmental applications: An overview. Renew. Sustain. Energy Rev. 2017, 76, 212–225. [Google Scholar] [CrossRef]
  31. Roy, P.; Berger, S.; Schmuki, P. TiO2 nanotubes: Synthesis and applications. Angew. Chem. Int. Ed. 2011, 50, 2904–2939. [Google Scholar] [CrossRef] [PubMed]
  32. Li, Y.; Ding, D.Y.; Ning, C.Q.; Bai, S.; Huang, L.; Li, M.; Mao, D.L. Thermal stability and in vitro bioactivity of Ti-Al-V-O nanostructures fabricated on Ti6Al4V alloy. Nanotechnology 2009, 20, 065708. [Google Scholar] [CrossRef] [PubMed]
  33. Sun, Y.; Wang, G.X.; Yan, K.P. TiO2 nanotubes for hydrogen generation by photocatalytic water splitting in a two-compartment photoelectrochemical cell. Int. J. Hydrog. Energy 2011, 36, 15502–15508. [Google Scholar] [CrossRef]
  34. Liu, Z.; Pesic, B.; Raja, K.S.; Rangaraju, R.R.; Misra, M. Hydrogen generation under sunlight by self-ordered TiO2 nanotube arrays. Int. J. Hydrog. Energy 2009, 34, 3250–3257. [Google Scholar] [CrossRef]
  35. Kunadian, I.; Lipka, S.M.; Swartz, C.R.; Qian, D.; Andrews, R. Determination of carrier densities of boron–and nitrogen-doped multiwalled carbon nanotubes using Mott–Schottky plots. J. Electrochem. Soc. 2009, 156, K110–K115. [Google Scholar] [CrossRef]
  36. Palmas, S.; Polcaro, A.M.; Ruiz, J.R.; Da Pozzo, A.; Mascia, M.; Vacca, A. TiO2 photoanodes for electrically enhanced water splitting. Int. J. Hydrog. Energy 2010, 35, 6561–6570. [Google Scholar] [CrossRef]
  37. Kim, J.Y.; Jung, H.S.; No, J.H.; Kim, J.R.; Hong, K.S. Influence of anatase–rutile phase transformation on dielectric properties of sol–gel derived TiO2 thin films. J. Electroceram. 2006, 16, 447–451. [Google Scholar] [CrossRef]
  38. Hernández, S.; Hidalgo, D.; Sacco, A.; Chiodoni, A.; Lamberti, A.; Cauda, V.; Tresso, E.; Saracco, G. Comparison of photocatalytic and transport properties of TiO2 and ZnO nanostructures for solar-driven water splitting. Phys. Chem. Chem. Phys. 2005, 17, 7775–7786. [Google Scholar] [CrossRef] [PubMed]
Nanomaterials 07 00359 g001 550
Figure 1. Typical microstructure of Ti-1Ni-5Si alloy: (a) Optical micrograph; (b) SEM image.
Figure 1. Typical microstructure of Ti-1Ni-5Si alloy: (a) Optical micrograph; (b) SEM image.
Nanomaterials 07 00359 g001
Nanomaterials 07 00359 g002 550
Figure 2. SEM images of scratched Ti-Ni-Si-O nanostructures showing: (a) nanotubes grown in the α-Ti phase region and Ti2Ni phase region; (b) nanopores grown in the Ti5Si3 phase region.
Figure 2. SEM images of scratched Ti-Ni-Si-O nanostructures showing: (a) nanotubes grown in the α-Ti phase region and Ti2Ni phase region; (b) nanopores grown in the Ti5Si3 phase region.
Nanomaterials 07 00359 g002
Nanomaterials 07 00359 g003 550
Figure 3. XRD patterns of the as-anodized and the annealed Ti-Ni-Si-O nanostructures.
Figure 3. XRD patterns of the as-anodized and the annealed Ti-Ni-Si-O nanostructures.
Nanomaterials 07 00359 g003
Nanomaterials 07 00359 g004 550
Figure 4. UV-Vis diffuse reflectance absorption spectra of the annealed Ti-Ni-Si-O photoanode.
Figure 4. UV-Vis diffuse reflectance absorption spectra of the annealed Ti-Ni-Si-O photoanode.
Nanomaterials 07 00359 g004
Nanomaterials 07 00359 g005 550
Figure 5. Photoelectrochemical water splitting behavior of Ti-Ni-Si-O nanostructures: (a) I-V curves in dark and under illumination; (b) transient photocurrent responses.
Figure 5. Photoelectrochemical water splitting behavior of Ti-Ni-Si-O nanostructures: (a) I-V curves in dark and under illumination; (b) transient photocurrent responses.
Nanomaterials 07 00359 g005
Nanomaterials 07 00359 g006 550
Figure 6. (a) Open-circuit potential of Ti-Ni-Si-O nanostructure photoanodes; (b) Mott-Schottky plots of Ti-Ni-Si-O nanostructure photoanodes with a frequency of 1000 Hz.
Figure 6. (a) Open-circuit potential of Ti-Ni-Si-O nanostructure photoanodes; (b) Mott-Schottky plots of Ti-Ni-Si-O nanostructure photoanodes with a frequency of 1000 Hz.
Nanomaterials 07 00359 g006
Table
Table 1. Compositions of the α-Ti phase, Ti2Ni phase, and Ti5Si3 phase of the alloy.
Table 1. Compositions of the α-Ti phase, Ti2Ni phase, and Ti5Si3 phase of the alloy.
EDS Testing AreasElements (wt %)
TiNiSi
α-Ti phase 98.810.121.07
Ti2Ni phase 88.0211.890.09
Ti5Si3 phase 76.420.1023.48
Table
Table 2. Compositions in the α-Ti phase, Ti2Ni phase, and Ti5Si3 phase regions after anodization.
Table 2. Compositions in the α-Ti phase, Ti2Ni phase, and Ti5Si3 phase regions after anodization.
EDS Testing AreasElements (wt %)
TiNiSiO
α-Ti phase region56.48–1.0642.46
Ti2Ni phase region66.771.940.8230.47
Ti5Si3 phase region60.35–9.7429.91

Share and Cite

MDPI and ACS Style

Li, T.; Ding, D.; Dong, Z.; Ning, C. Photoelectrochemical Water Splitting Properties of Ti-Ni-Si-O Nanostructures on Ti-Ni-Si Alloy. Nanomaterials 2017, 7, 359. https://doi.org/10.3390/nano7110359

AMA Style

Li T, Ding D, Dong Z, Ning C. Photoelectrochemical Water Splitting Properties of Ti-Ni-Si-O Nanostructures on Ti-Ni-Si Alloy. Nanomaterials. 2017; 7(11):359. https://doi.org/10.3390/nano7110359

Chicago/Turabian Style

Li, Ting, Dongyan Ding, Zhenbiao Dong, and Congqin Ning. 2017. "Photoelectrochemical Water Splitting Properties of Ti-Ni-Si-O Nanostructures on Ti-Ni-Si Alloy" Nanomaterials 7, no. 11: 359. https://doi.org/10.3390/nano7110359

APA Style

Li, T., Ding, D., Dong, Z., & Ning, C. (2017). Photoelectrochemical Water Splitting Properties of Ti-Ni-Si-O Nanostructures on Ti-Ni-Si Alloy. Nanomaterials, 7(11), 359. https://doi.org/10.3390/nano7110359

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop