Next Article in Journal
Chitlac-Coated Thermosets Enhance Osteogenesis and Angiogenesis in a Co-culture of Dental Pulp Stem Cells and Endothelial Cells
Next Article in Special Issue
Structural Characterization of Graphene Oxide: Surface Functional Groups and Fractionated Oxidative Debris
Previous Article in Journal
Uncooled Short-Wave Infrared Sensor Based on PbS Quantum Dots Using ZnO NPs
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 9
Issue 7
10.3390/nano9070927
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Nanocomposite Synthesis of Nanodiamond and Molybdenum Disulfide

by
Youngjun Kim
,
Dukhee Lee
,
Soo Young Kim
,
Eunah Kang
* and
Chang Keun Kim
*
School of Chemical Engineering and Material Science, Chung-Ang University, Seoul 06974, Korea
*
Authors to whom correspondence should be addressed.
Nanomaterials 2019, 9(7), 927; https://doi.org/10.3390/nano9070927
Submission received: 7 June 2019 / Revised: 23 June 2019 / Accepted: 26 June 2019 / Published: 27 June 2019
(This article belongs to the Special Issue Characterization, Synthesis and Applications of 2D Nanomaterials)
Browse Figures
Review Reports Versions Notes

Abstract

:
A chemically conjugated nanodiamond (ND)/MoS2 nanocomposite was synthesized with amine-functionalized MoS2 and acyl chloride-coordinated ND. The chemical structure and morphology of the nanocomposite were characterized to examine the dispersion of MoS2 on the ND platform. The results revealed that the degree of dispersion was enhanced with increasing ratio of MoS2 nanosheets to ND. Moreover, the nanosheets consisted of several molecular interlayers that were well-dispersed on the ND platform, thereby forming a nanophase. The efficient electrocapacity of the ND/MoS2 nanocomposite was considerably greater than that of the MoS2 electrode alone. Furthermore, the nanophase distribution of MoS2 on ND with a graphitic shell provided a large surface area and reduced the diffusion distance of ions and electrons. Therefore, the nanophase electrode showed higher electrochemical capacitance than that of the MoS2 electrode alone.

1. Introduction

Numerous novel materials and composites including two-dimensional (2D) materials have been exploited with the aim of enhancing electrocapacity, which can be applied for biosensing platforms and electrocatalytic performance. A 2D layered material can be defined as an unsupported crystalline solid with molecular layer thickness characterized by intralayer storage for heat, charge, and light transport [1,2,3,4]. This transport occurs in the presence of intralayer covalent bonds and intercalation-based interaction [5]. Specifically, MoS2 as a 2D transition metal dichalcogenide (TMD) exhibits the unique characteristic of charge confinement in the 2D layer in the absence of interlayer interaction along the z-axis [6]. Functional features of 2D MoS2 layers include high thermal and chemical stability for functionalization [7,8], large surface area [4], good mobility [9], and intercalation-based physical interaction [10,11]. For final functional performance, the construction of an electrode and nanophase distribution of an aggregation-free 2D MoS2 molecular layer are critical to induce maximal functional features.
Carbon-based materials including fullerenes, graphene, and carbon nanotubes, are considered as fundamental platform materials of energy conversion and storage, owing to their thermal stability, conductivity, and mechanical properties [12,13,14,15]. Furthermore, the electron buffering capability of these materials stems from their high surface-to-volume ratio and the unsaturated carbon ᴨ bonds. Physicochemical characteristics can reduce oxygen adsorption on a catalyst surface, thereby improving the material performance. In general, the porous structure of carbon materials is characterized by a multiscale nanocage and a high surface-to-volume ratio that provide electron transfer and electrocatalytic active sites. These advantages have often been applied to nanocomposites with metal to induce synergistic functional effects, including solar cells, batteries, and supercapacitors [16,17,18,19,20].
Nanodiamonds (NDs) among carbon platforms have received less attention than some of the other carbon materials due to the high costs and low conductivity of these materials as electric functional materials [21,22]. However, NDs possess excellent physical properties, including high adsorption [23], high surface-to-volume ratio [24], chemical modality on the graphitic shell surface [25], and a nanocage within agglutinate [26]. Moreover, the dispersive capability of NDs in aqueous environments makes it possible to integrate and to extend materials to other functional employment, including biomedical applications as well as electronic functions [27]. NDs serve as a supporting platform that can augment the functional efficiency of the other incorporated pair of 2D materials.
Therefore, in this study a ND/MoS2 nanocomposite by subsequent functionalization was synthesized and characterized. An ND with a graphitic shell around its surface provides stable sites for chemical modification. Immediate chemical reaction between the acyl chloride of NDs and amine-functionalized MoS2 was intended to form aggregation-free MoS2 nanosheet dispersion on the ND support (Scheme 1). This nanophase dispersion of MoS2 in several interlayers on the ND platform was examined from the viewpoint of physical characteristics and potential electrofunctionality.

2. Experimental Methods

2.1. Nanocomposite Formation of MoS2 and Nanodiamonds

ND-COOHs (40 mg) gifted from Nanoresource (Seoul, Korea) were mixed with 100 mL of thionyl chloride (Samcheon Chemical Co., Seoul, Korea) and 0.5 mL of dimethylformamide anhydrous (DMF) in a 250 mL round-bottomed flask. The ND-COOHs were well-dispersed for 15 min of bath sonication under an ice bath. The ND dispersion for acylation was stirred for 24 h at 70 °C under a N2 purge. After reaction, the dispersion was washed repeatedly five times with tetrahydrofuran anhydrous (THF) and the NDs, separated by centrifugation, were dried at 60 °C in an air-circulated oven.
For exfoliation, the mixture of pristine MoS2 (120 mg, <2 μm; Sigma-Aldrich Chemicals, St Louis, MO, USA) and N-vinyl-2-pyrrolidone (60 mL) was sonicated with condition of 55% power amplitude and 3 s pulse (VC750, Sonics Vibra-cell) for 8 h under circulation at 7 °C [28]. After exfoliation, the large MoS2 was separated by centrifugation (4000 rpm, 5 min), and the supernatant was extracted. This supernatant was then filtered through a syringe filter (0.45 µm, HP045AN, Advantec, Taipei, Taiwan) and centrifuged (14,600 rpm, 10 min). Afterward, the settled MoS2 nanosheets were washed with isopropanol and centrifuged repeatedly until the yellow color of N-vinyl-2-pyrrolidone became colorless. The nanosheets were then dried for 24 h at 40 °C under vacuum.
The MoS2 nanosheets (1 mg/mL) were dispersed in DMF. For chemical conjugation, 200 μL of cystamine (5 mg/mL) in DMF was added to 1 mL of the MoS2 dispersion. This dispersion mixture was then sonicated for 1 h under an ice bath. After sonication, the mixture was left to stand at room temperature for 24 h. Then, functionalized MoS2 was washed repeatedly three times with DMF, separated by centrifugation at 14,600 rpm, and completely dried at 60 °C in a vacuum oven.
Acylated NDs (1 mg/mL) and amine-functionalized MoS2 nanosheets in DMF were dispersed with 5 min of bath sonication. The dispersion of acylated ND and amine-functionalized MoS2 with desired ratios (1:1, 1:2, 1:4, and 1:8) was mixed by sonication under an ice bath for 30 min, and shaken with a vortex for 24 h. After the reaction, the composite was washed and completely dried at 60 °C in a vacuum oven.

2.2. Characterization of ND/MoS2 Nanocomposites

The ultraviolet (UV) absorption of ND-COCl, MoS2 nanosheet, and ND/MoS2 nanocomposite was measured with a V-670 UV-Vis/NIR spectrophotometer (JASCO Corp., Tokyo, Japan). These measurements were performed under the following conditions: scanning speed: 200 nm/min, data interval: 1 nm, UV-Vis bandwidth: 1.0 nm, near-infrared (NIR) bandwidth: 2.0 nm, and wavelength: 350–900 nm [29]. The dispersions (0.2 mg/2 mL) of the nanosheets and the nanocomposite in deionized (DI) water were placed, respectively, in a synthetic quartz cuvette (light path: 1 cm, Hellma Analytics, Müllheim, Germany). Measurement of Fourier transform infrared spectroscopy (FT-IR; Nicolet 6700, Thermo Scientific., Waltham, MA, USA) ranged from 4000–500 cm−1 of wavelength and was performed subsequently on the chemical reactant, ND, and MoS2. IR samples were prepared using the standard method of KBr pellet (7 mm in diameter). The materials of 0.5–1 mg were added with a portion of KBr (7 mg).
X-ray photoeletron spectroscopy (XPS; ThermoFisher Scientific Co., Waltham, MA, USA) measurements were also conducted with an Al Kα energy source. The spectra were analyzed using Avantage software (version 1.6, Thermo Fisher Scientific, Waltham, MA, USA). Transmission electron microscopy (TEM) images were obtained with a JEM-2100F electron microscope (JEOL, Tokyo, Japan). For sample preparation, 10 μL each of ND, MoS2, and ND/MoS2 nanocomposite was dropped on Formvar/Carbon on a 200 mesh grid (TED PELLA Co., Redding, CA, USA.) and dried for 10 min at 60 °C in an oven.

2.3. Cyclic Voltammetry (CV) Measurements

A dispersion of ND/MoS2 nanocomposite (1 mg/mL) was prepared in Nafion solution (0.5% in DI water) for electrode fabrication. Droplets of the dispersion (10 μL) were placed on the glassy carbon working electrode (diameter 3 mm) and dried at 80 °C for 1 h. Cyclic voltammetry (CV) measurements (potential: −0.8 to 0.2 V, scan rate: −0.2 to 1.0 V) were performed using a three-electrode system (reference electrode: Ag/AgCl, counter electrode: platinum wire (57 mm in length, OD 0.5 mm), working electrode: ND/MoS2 or MoS2 deposited glassy carbon electrode). Two sets of measurements using a potensiostat (DY2322, Digi-Ivy, Austin, TX, USA) were also performed at potentials ranging from 0.05 to 0.5 V·s−1 and scan rates of 0.05, 0.1, and 0.5 V/s. The corresponding CV plots were recorded in a 0.1 M KOH solution (15 ml). Five cycles in 2 sets were performed to obtain a voltamogram. After stabilization from repeated cycles, an oxidation and reduction curve in each second set of a working electrode was shown for data presentation.

3. Results and Discussion

UV–vis absorption spectra were obtained for the MoS2 nanosheets, ND-COCl, and ND/MoS2 nanocomposite with ratios of 1:1, 1:2, 1:4, and 1:8 (Figure 1). Typical MoS2 excitation absorption peaks, which occurred at 630 and 690 nm, were attributed to the direct gap transitions at the K point [30,31,32]. These indicate the lowest optical band gap of the MoS2 nanosheets (i.e., ~1.8 eV) that were changed, owing to the quantum confinement in the sheets. Changes in the UV absorbance were evaluated for the MoS2/ND nanocomposite with ratios of 1:1 to 1:8. The optical absorbance peaks of MoS2/ND nanocomposite appeared in the same region as those of the MoS2 nanosheets. It was indicated that chemically conjugated MoS2/ND nanocomposite maintained the optical characteristics of the nanosheets. The intensity of the bands in the spectra were augmented with the increasing ratio of the nanocomposite, as shown in Figure 1 [33].
Chemical conjugation of the nanocomposite and functional groups of intermediate products was characterized via FT-IR spectroscopy to identify sequential chemical modification of the acyl chloride comprising ND (ND–COCl), MoS2-NH2, and MoS2/ND nanocomposites (Figure 2). The oxidative treatment formed a carbonyl group (C=O) and a hydroxyl group (-OH), occurring as absorption peaks at 1718 and 3400 cm−1 on the surface of the carboxylated ND, respectively. The graphitic shell around the crystalline ND was attributed to the absorption bands associated with C=C bond bending at 1625 cm−1. After acyl chlorination, ND with an acyl chloride bond (C-Cl) was formed, corresponding to the stretching peak at 593 cm−1, whereas no peak for ND-COOH was observed [34]. The results indicated that the carboxylated ND surface was activated by the acyl chloride group for an amine reactive reaction. The functionalization of MoS2 with cysteamine hydrochloride was characterized with comparison of the cysteamine hydrochloride. For the amine-functionalized MoS2, an N−H deformation vibration peak and an NH2 stretching vibration peak, derived from the chemical conjugation with cysteamine hydrochloride, occurred at 1604 and 3390 cm−1, respectively [35]. This indicated the successful modification of amine-functionalized MoS2, where amine groups were positioned on the surface of MoS2 nanosheets. The formation of an amide bond (NHCO) between the acyl chloride of ND and the functionalized MoS2 nanosheets was confirmed via FT-IR spectroscopy of the ND/MoS2 nanocomposites. The spectra obtained for the nanocomposites exhibited characteristics of both ND-COCl and the functionalized nanosheets. The absorption bands associated with the ND/MoS2 peak were attributed to hydroxyl bond stretching and an amide bond (NHCO) at 3400 cm−1 and 1632 cm−1, respectively. Furthermore, the relatively strong absorbance band region resulted probably from the overlapping of bands associated with C=C vibration and C=O stretching [36,37].
The chemical structure of the ND/MoS2 nanocomposite, compared with that of ND-COCl, was determined from the measured XPS spectra, as shown in Figure 3a–f. The C1s peaks of ND-COCl and ND/MoS2 were decon-voluted into four component peaks using Gaussian fitting at 284.8 (C-C), 286.0 (C-O), 287.2 (C=O), and 289 (-COOH) eV, respectively [38,39]. The C=O peak at 287.2 eV for ND-COCl was generated from both acyl chloride and some portion of the carboxyl group. The C=O peak at 287.2 eV arose from the amide group after chemical conjugation of ND/ND/MoS2 nanocomposites. After chemical conjugation between ND-COCl and amine-functionalized MoS2, the intensity of the peak at 286.0 V (C-O) increased significantly relative to that of the peak at 287.2 V (C=O). The results indicate that unreacted acyl chloride would decompose into carboxyl groups during the washing process and from contact with moisture. The O1 peaks of ND-COCl and ND/MoS2 at 531.8 and 533.1 eV were attributed to C=O and COC/COH, respectively. The intensity of the ND/MoS2 peak increased relative to that of the ND-COCl peak, indicating that the unreacted acyl chloride group was converted to the carboxyl group after chemical conjugation with the MoS2 nanosheets (Figure 3b,e). The Cl 2p peaks of the ND-COCl were deconvoluted into two conventional binding energies of 200.3 eV (Cl 2p 3/2) and 201.9 eV (Cl 2p 1/2). This indicated that ND-COOH was functionalized by an acyl chloride group on the surface [36]. Deconvolution of the Cl 2p peaks, corresponding to ND/MoS2 generated peaks at 200.3 eV (Cl 2p 3/2) and 201.9 eV (Cl 2p 1/2), have resulted from the physical adsorption of remnant chloride ions onto the ND surface and nanocage [34,36].
Figure 4 shows the XPS spectra of the MoS2 and ND/MoS2 nanocomposite. Two strong peaks for the Mo 3d peak of MoS2 are observed at 229.85 for doublet Mo 3d5/2 and 232.98 eV for and Mo 3d3/2 (Figure 4a). The peaks, corresponding to the S 2p1/2 and S 2p3/2 orbital of divalent sulfide ions (S2−) occur at binding energies of 163.85 and 162.65 eV, respectively, as shown in Figure 4b. The results are consistent with the values reported for a MoS2 crystal [35,40,41,42]. The XPS spectra of ND/MoS2 also revealed typical MoS2 crystalline characteristics with chemically induced shifting. Furthermore, the peak position moved from 229.85 to 229.53 eV for Mo 3d5/2 and from 232.98 to 232.64 eV for Mo 3d3/2, respectively. Chemically induced shifts were also observed for ND/MoS2 S 2p, with the peaks shifting from 162.65 to 162.44 eV for S 2p3/2 and 163.85 to 163.71 eV for S 2p1/2 peaks [43]. This indicated that the chemical shift of the ND/MoS2 nanocomposite to lower binding energy than that of MoS2 resulted from chemical conjugation with ND.
The morphologies of MoS2, ND, and ND/MoS2 nanocomposites (Figure 5) were evaluated with TEM. The MoS2 nanosheets was featured as average size of 300–400 nm along the long axis (Figure 5a,b). The MoS2 nanosheets had a crystalline structure, and several molecular layers were stacked or folded in a planar form [44]. Furthermore, the NDs were well-dispersed with small agglutinins ranging from 80 to 200 nm (Figure 5c,d). The ND/MoS2 nanocomposite with chemical conjugation showed morphological features that several molecular layers of thin MoS2 nanosheet enveloped ND agglutinins (Figure 5e–h). Amine-functionalized MoS2 nanosheets and NDCOCls were chemically reacted through surface contact, suggesting that the ND/MoS2 nanocomposite was successfully synthesized (Figure 5e–h).
Cyclic voltammograms of the MoS2 nanosheet and ND/MoS2 are shown in Figure 6a–f. For both electrodes, the rectangularity of the CV plots decreased slightly, corresponding to the reversible reactions of Mo2+/Mo3+ associated with OH- anions [45]. The possible redox reaction is given as follows [46]:
ND/MoS2 + OH- ↔ ND/MoSOH + e-
ND/MoSOH + OH- ↔ ND/MoSO + H2O + e-
On the same material set, scan rates of 0.05, 0.1, and 0.5 V/s, respectively, and range of potential voltage was differently applied to −0.8 to −0.2 V and −0.2 to 1.0 V. The shape and magnitude of the voltamogram was transitioned from a peak-like shape (Figure 6a–c) to quasi-rectangular shape (Figure 6d–f) depending on the scan rate and potential voltage. The quasi-rectangular shape typically indicates constant and time dependent concentration gradient of an electroactive surface where the electrode radius was typically smaller than diffusion layer [47]. Each CV graph is characterized by a quasi-rectangular shape, consistent with dual behavior, such as the electrical double layer capacitance [48]. MoS2 nanosheets constitute the minimum area of the CV plot, whereas 1:8 and 1:6 ND/MoS2 constitutes the maximum area, which corresponds to the enhanced capacitance. The CV curve of the ND/MoS2 nanocomposites reveals the higher current response and large working area of these composites, compared with those of the MoS2 nanosheet only (Figure 6). The results suggest that the addition of nanodiamonds enhances the electrochemical activity and increases the specific capacitance of MoS2 electrode alone [29,35].
The superior electrical performance of the ND/MoS2 nanocomposite electrode, compared with that of the MoS2 electrode alone, resulted from the unique nanostructure of the composite electrode. Moreover, the large surface area and the nanosized MoS2 phase of the ND/MoS2 composites may have resulted in significant reduction of the diffusion length associated with ion and electron transfer during the oxidation/reduction process. The electrode nanoscale phase makes these composites promising for various applications. Specifically, the NDs acted as nanoscale supports to functionalize synergistically the MoS2 sheets, which served as a three-dimensional highly conductive current collector. The featured architecture of the ND/MoS2 nanocomposites possessing a large specific surface of the electrode enables rapid and simultaneous electron and ion transport, thereby leading to excellent electrochemical capacitive performance [42].

4. Conclusions

A chemically conjugated ND/MoS2 nanocomposite was synthesized with amine-functionalized MoS2 and acyl chloride-coordinated NDs. The chemical structure and morphology of the nanocomposite were characterized, and the results revealed that the MoS2 nanosheets were well-distributed on the ND platform, thereby forming a nanophase. Nanophase distribution of MoS2 on ND with a graphitic shell may provide a large surface area and reduce the diffusion distance of ions and electrons. Therefore, the augmented electrochemical capacitance of the nanophase electrode was induced, compared to that of the MoS2 electrode alone.

Author Contributions

For research articles was prepared and supported by conceptualization. S.Y.K.; data curation, D.L.; writing—original draft preparation, Y.K.; and supervision, E.K. and C.K.K.

Funding

This research was supported by Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education (NRF-2018R1D1A1B07042982). This research was supported by the Chung-Ang University Research Scholarship Grants in 2018.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Qiu, H.; Xu, T.; Wang, Z.L.; Ren, W.; Nan, H.Y.; Ni, Z.H.; Chen, Q.; Yuan, S.J.; Miao, F.; Song, F.Q.; et al. Hopping transport through defect-induced localized states in molybdenum disulphide. Nat. Commun. 2013, 4, 2642. [Google Scholar] [CrossRef] [PubMed]
  2. Wu, S.F.; Huang, C.M.; Aivazian, G.; Ross, J.S.; Cobden, D.H.; Xu, X.D. Vapor-Solid Growth of High Optical Quality MoS2 Monolayers with Near-Unity Valley Polarization. Acs Nano 2013, 7, 2768–2772. [Google Scholar] [CrossRef] [PubMed]
  3. Song, H.S.; Li, S.L.; Gao, L.; Xu, Y.; Ueno, K.; Tang, J.; Cheng, Y.B.; Tsukagoshi, K. High-performance top-gated monolayer SnS2 field-effect transistors and their integrated logic circuits. Nanoscale 2013, 5, 9666–9670. [Google Scholar] [CrossRef] [PubMed]
  4. Xia, D.; Gong, F.; Pei, X.D.; Wang, W.B.; Li, H.; Zeng, W.; Wu, M.Q.; Papavassiliou, D.V. Molybdenum and tungsten disulfides-based nanocomposite films for energy storage and conversion: A review. Chem. Eng. J. 2018, 348, 908–928. [Google Scholar] [CrossRef]
  5. Huang, L.F.; Gong, P.L.; Zeng, Z. Correlation between structure, phonon spectra, thermal expansion, and thermomechanics of single-layer MoS2. Phys. Rev. B 2014, 90, 045409. [Google Scholar] [CrossRef]
  6. Sorkin, V.; Pan, H.; Shi, H.; Quek, S.Y.; Zhang, Y.W. Nanoscale Transition Metal Dichalcogenides: Structures, Properties, and Applications. Crit. Rev. Solid State 2014, 39, 319–367. [Google Scholar] [CrossRef]
  7. Yang, X.; Meng, N.N.; Zhu, Y.C.; Zhou, Y.F.; Nie, W.W.; Chen, P.P. Greatly improved mechanical and thermal properties of chitosan by carboxyl-functionalized MoS2 nanosheets. J. Mater. Sci. 2016, 51, 1344–1353. [Google Scholar] [CrossRef]
  8. Cheng, Y.; Pang, K.L.; Wu, X.; Zhang, Z.G.; Xu, X.H.; Ren, J.K.; Huang, W.; Song, R. In Situ Hydrothermal Synthesis MoS2/Guar Gum Carbon Nanoflowers as Advanced Electrocatalysts for Electrocatalytic Hydrogen Evolution. Acs Sustain. Chem. Eng. 2018, 6, 8688–8696. [Google Scholar] [CrossRef]
  9. Haynes, K.; Murray, R.; Weinrich, Z.; Zhao, X.; Chiappe, D.; Sutar, S.; Radu, I.; Hatem, C.; Perry, S.S.; Jones, K.S. Modulating the resistivity of MoS2 through low energy phosphorus plasma implantation. Appl. Phys. Lett. 2017, 110, 262102. [Google Scholar] [CrossRef]
  10. Wang, X.H.; Ding, J.J.; Yao, S.W.; Wu, X.X.; Feng, Q.Q.; Wang, Z.H.; Geng, B.Y. High supercapacitor and adsorption behaviors of flower-like MoS2 nanostructures. J. Mater. Chem. A 2014, 2, 15958–15963. [Google Scholar] [CrossRef]
  11. Jing, Y.; Ortiz-Quiles, E.O.; Cabrera, C.R.; Chen, Z.F.; Zhou, Z. Layer-by-Layer Hybrids of MoS2 and Reduced Graphene Oxide for Lithium Ion Batteries. Electrochim. Acta 2014, 147, 392–400. [Google Scholar] [CrossRef]
  12. Allen, M.J.; Tung, V.C.; Kaner, R.B. Honeycomb Carbon: A Review of Graphene. Chem. Rev. 2010, 110, 132–145. [Google Scholar] [CrossRef] [PubMed]
  13. Jiang, H.J. Chemical Preparation of Graphene-Based Nanomaterials and Their Applications in Chemical and Biological Sensors. Small 2011, 7, 2413–2427. [Google Scholar] [CrossRef] [PubMed]
  14. Lee, J.H.; Park, S.J.; Choi, J.W. Electrical Property of Graphene and Its Application to Electrochemical Biosensing. Nanomaterials 2019, 9, 297. [Google Scholar] [CrossRef] [PubMed]
  15. Yang, J.; Ma, M.Z.; Li, L.Q.; Zhang, Y.F.; Huang, W.; Dong, X.C. Graphene nanomesh: New versatile materials. Nanoscale 2014, 6, 13301–13313. [Google Scholar] [CrossRef]
  16. Polcar, T.; Nossa, A.; Evaristo, M.; Cavaleiro, A. Nanocomposite coatings of carbon-based and transition metal dichalcogenides phases: A review. Rev. Adv. Mater. Sci. 2007, 15, 118–126. [Google Scholar]
  17. Mohamed, M.M.; Ghanem, M.A.; Reda, S.M.; Khairy, M.; Naguib, E.M.; Alotaibi, N.H. Photovoltaic and capacitance performance of low-resistance ZnO nanorods incorporated into carbon nanotube-graphene oxide nanocomposites. Electrochim. Acta 2019, 307, 430–441. [Google Scholar] [CrossRef]
  18. Suriyakumar, S.; Gopi, S.; Kathiresan, M.; Bose, S.; Gowd, B.; Nair, J.R.; Angulakshmi, N.; Meligrana, G.; Bella, F.; Gerbaldi, C.; et al. Metal organic framework laden poly(ethylene oxide) based composite. electrolytes for all-solid-state Li-S and Li-metal polymer batteries. Electrochim. Acta 2018, 285, 355–364. [Google Scholar] [CrossRef]
  19. Shanker, G.S.; Markad, G.B.; Jagadeeswararao, M.; Bansode, U.; Nag, A. Colloidal Nanocomposite of TiN and N-Doped Few-Layer Graphene for Plasmonics and Electrocatalysis. Acs Energy Lett. 2017, 2, 2251–2256. [Google Scholar] [CrossRef]
  20. Fu, W.B.; Zhao, E.B.; Ren, X.L.; Magasinski, A.; Yushin, G. Hierarchical Fabric Decorated with Carbon Nanowire/Metal Oxide Nanocomposites for 1.6 V Wearable Aqueous Supercapacitors. Adv. Energy Mater. 2018, 8, 1703454–1703462. [Google Scholar] [CrossRef]
  21. Mochalin, V.N.; Shenderova, O.; Ho, D.; Gogotsi, Y. The properties and applications of nanodiamonds. Nat. Nanotechnol. 2011, 7, 11–23. [Google Scholar] [CrossRef] [PubMed]
  22. Lim, D.G.; Prim, R.E.; Kim, K.H.; Kang, E.; Park, K.; Jeong, S.H. Combinatorial nanodiamond in pharmaceutical and biomedical applications. Int. J. Pharmaceut. 2016, 514, 41–51. [Google Scholar] [CrossRef]
  23. Mochalin, V.N.; Pentecost, A.; Li, X.M.; Neitzel, I.; Nelson, M.; Wei, C.Y.; He, T.; Guo, F.; Gogotsi, Y. Adsorption of Drugs on Nanodiamond: Toward Development of a Drug Delivery Platform. Mol. Pharmaceut. 2013, 10, 3728–3735. [Google Scholar] [CrossRef] [PubMed]
  24. Yuan, T.; Larsson, K. Theoretical Study of Size Effects on Surface Chemical Properties for Nanoscale Diamond Particles. J. Phys. Chem. C 2014, 118, 26061–26069. [Google Scholar] [CrossRef]
  25. Duffy, E.; He, X.Y.; Nesterenko, P.N.; Paull, B. Hierarchical porous graphitic carbon monoliths with detonation nanodiamonds: synthesis, characterisation and adsorptive properties. J. Mater. Sci. 2015, 50, 6245–6259. [Google Scholar] [CrossRef]
  26. Lim, D.G.; Jung, J.H.; Ko, H.W.; Kang, E.; Jeong, S.H. Paclitaxel-Nanodiamond Nanocomplexes Enhance Aqueous Dispersibility and Drug Retention in Cells. Acs Appl. Mater. Interfaces 2016, 8, 23558–23567. [Google Scholar] [CrossRef] [PubMed]
  27. Agarwal, V.; Chatterjee, K. Recent advances in the field of transition metal dichalcogenides for biomedical applications. Nanoscale 2018, 10, 16365–16397. [Google Scholar] [CrossRef]
  28. Kim, C.; Nguyen, T.P.; Le, Q.V.; Jeon, J.-M.; Jang, H.W.; Kim, S.Y. Performances of Liquid-Exfoliated Transition Metal Dichalcogenides as Hole Injection Layers in Organic Light-Emitting Diodes. Adv. Funct. Mater. 2015, 25, 4512–4519. [Google Scholar] [CrossRef]
  29. Azhagan, M.V.K.; Vaishampayan, M.V.; Shelke, M.V. Synthesis and electrochemistry of pseudocapacitive multilayer fullerenes and MnO2 nanocomposites. J. Mater. Chem. A 2014, 2, 2152–2159. [Google Scholar] [CrossRef]
  30. Zhao, W.J.; Ghorannevis, Z.; Chu, L.Q.; Toh, M.L.; Kloc, C.; Tan, P.H.; Eda, G. Evolution of Electronic Structure in Atomically Thin Sheets of WS2 and WSe2. Acs Nano 2013, 7, 791–797. [Google Scholar] [CrossRef]
  31. Muscuso, L.; Cravanzola, S.; Cesano, F.; Scarano, D.; Zecchina, A. Optical, Vibrational, and Structural Properties of MoS2 Nanoparticles Obtained by Exfoliation and Fragmentation via Ultrasound Cavitation in Isopropyl Alcohol. J. Phys. Chem. C 2015, 119, 3791–3801. [Google Scholar] [CrossRef]
  32. Rao, C.N.R.; Maitra, U.; Waghmare, U.V. Extraordinary attributes of 2-dimensional MoS2 nanosheets. Chem. Phys. Lett. 2014, 609, 172–183. [Google Scholar] [CrossRef]
  33. Mishra, A.K.; Lakshmi, K.V.; Huang, L.P. Eco-friendly synthesis of metal dichalcogenides nanosheets and their environmental remediation potential driven by visible light. Sci. Rep.-Uk 2015, 5, 15718. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  34. Lim, D.G.; Kim, K.H.; Kang, E.; Lim, S.H.; Ricci, J.; Sung, S.K.; Kwon, M.T.; Jeong, S.H. Comprehensive evaluation of carboxylated nanodiamond as a topical drug delivery system. Int. J. Nanomed. 2016, 11, 2381–2395. [Google Scholar] [Green Version]
  35. Ramadoss, A.; Kim, T.; Kim, G.S.; Kim, S.J. Enhanced activity of a hydrothermally synthesized mesoporous MoS2 nanostructure for high performance supercapacitor applications. New J. Chem. 2014, 38, 2379–2385. [Google Scholar] [CrossRef]
  36. Lim, D.G.; Rajasekaran, N.; Lee, D.; Kim, N.A.; Jung, H.S.; Hong, S.; Shin, Y.K.; Kang, E.; Jeong, S.H. Polyamidoamine-Decorated Nanodiamonds as a Hybrid Gene Delivery Vector and siRNA Structural Characterization at the Charged Interfaces. Acs Appl. Mater. Interfaces 2017, 9, 31543–31556. [Google Scholar] [CrossRef]
  37. Shenderova, O.; Panich, A.M.; Moseenkov, S.; Hens, S.C.; Kuznetsov, V.; Vieth, H.M. Hydroxylated Detonation Nanodiamond: FTIR, XPS, and NMR Studies. J. Phys. Chem. C 2011, 115, 19005–19011. [Google Scholar] [CrossRef]
  38. Choi, E.Y.; Kim, C.K. Fabrication of nitrogen-doped nano-onions and their electrocatalytic activity toward the oxygen reduction reaction. Sci. Rep.-Uk 2017, 7, 4178. [Google Scholar] [CrossRef]
  39. Kamila, S.; Mohanty, B.; Samantara, A.K.; Guha, P.; Ghosh, A.; Jena, B.; Satyam, P.V.; Mishra, B.K.; Jena, B.K. Highly Active 2D Layered MoS2-rGO Hybrids for Energy Conversion and Storage Applications. Sci. Rep.-Uk 2017, 7, 8378. [Google Scholar] [CrossRef]
  40. Minakshi, M.; Barmi, M.J.; Jones, R.T. Rescaling metal molybdate nanostructures with biopolymer for energy storage having high capacitance with robust cycle stability. Dalton Trans. 2017, 46, 3588–3600. [Google Scholar] [CrossRef]
  41. Barmi, M.J.; Minakshi, M. Tuning the Redox Properties of the Nanostructured CoMoO4 Electrode: Effects of Surfactant Content and Synthesis Temperature. Chempluschem 2016, 81, 964–977. [Google Scholar] [CrossRef]
  42. Ganguly, A.; Sharma, S.; Papakonstantinou, P.; Hamilton, J. Probing the Thermal Deoxygenation of Graphene Oxide Using High-Resolution In Situ X-ray-Based Spectroscopies. J. Phys. Chem. C 2011, 115, 17009–17019. [Google Scholar] [CrossRef] [Green Version]
  43. Gao, D.Q.; Si, M.S.; Li, J.Y.; Zhang, J.; Zhang, Z.P.; Yang, Z.L.; Xue, D.S. Ferromagnetism in freestanding MoS2 nanosheets. Nanoscale Res. Lett. 2013, 8, 129–136. [Google Scholar] [CrossRef] [PubMed]
  44. Lee, H.; Kim, H.; Nguyen, T.P.; Chang, J.H.; Kim, S.Y.; Kim, H.; Kang, E. Nanocomposites of Molybdenum Disulfide/Methoxy Polyethylene Glycol-co-Polypyrrole for Amplified Photoacoustic Signal. Acs Appl. Mater. Interfaces 2016, 8, 29213–29219. [Google Scholar] [CrossRef] [PubMed]
  45. Cheng, Q.; Tang, J.; Ma, J.; Zhang, H.; Shinya, N.; Qin, L.C. Graphene and nanostructured MnO2 composite electrodes for supercapacitors. Carbon 2011, 49, 2917–2925. [Google Scholar] [CrossRef]
  46. Kumuthini, R.; Ramachandran, R.; Therese, H.A.; Wang, F. Electrochemical properties of electrospun MoS2@C nanofiber as electrode material for high-performance supercapacitor application. J. Alloys Compd. 2017, 705, 624–630. [Google Scholar] [CrossRef]
  47. Mircˇeski, V.; Tomovski, Z. Voltammetry Based on Fractional Diffusion. J. Phys. Chem. B 2009, 113, 2794–2799. [Google Scholar] [CrossRef]
  48. Ramkumar, R.; Sundaram, M.M. Electrochemical synthesis of polyaniline crosslinked NiMoO4 nanofibre dendrites for energy storage devices. New J. Chem. 2016, 40, 7456–7464. [Google Scholar] [CrossRef]
Nanomaterials 09 00927 sch001 550
Scheme 1. Schematic showing conformation of the nanodiamond (ND)/MoS2 nanocomposites.
Scheme 1. Schematic showing conformation of the nanodiamond (ND)/MoS2 nanocomposites.
Nanomaterials 09 00927 sch001
Nanomaterials 09 00927 g001 550
Figure 1. UV−vis absorbance spectra of MoS2 nanosheets, ND, and ND/MoS2 nanocomposites with ratios of 1:1, 1:2, 1:4, and 1:8.
Figure 1. UV−vis absorbance spectra of MoS2 nanosheets, ND, and ND/MoS2 nanocomposites with ratios of 1:1, 1:2, 1:4, and 1:8.
Nanomaterials 09 00927 g001
Nanomaterials 09 00927 g002 550
Figure 2. FT-IR spectra of the MoS2 bulk, cysteamine, amine-functionalized MoS2 (MoS2-NH2), carboxylated ND, acyl chloride of ND, and ND/MoS2 nanocomposite with ratio of 1:1.
Figure 2. FT-IR spectra of the MoS2 bulk, cysteamine, amine-functionalized MoS2 (MoS2-NH2), carboxylated ND, acyl chloride of ND, and ND/MoS2 nanocomposite with ratio of 1:1.
Nanomaterials 09 00927 g002
Nanomaterials 09 00927 g003 550
Figure 3. Spectra obtained via X-ray photoelectron spectroscopy. The spectra show the C1s peaks, O1s peaks, and Cl2p peaks, respectively, of the (a)–(c) ND-COCl and (d)–(f) ND/MoS2 nanocomposites.
Figure 3. Spectra obtained via X-ray photoelectron spectroscopy. The spectra show the C1s peaks, O1s peaks, and Cl2p peaks, respectively, of the (a)–(c) ND-COCl and (d)–(f) ND/MoS2 nanocomposites.
Nanomaterials 09 00927 g003
Nanomaterials 09 00927 g004 550
Figure 4. Spectra obtained via X-ray photoelectron spectroscopy. The spectra show Mo 3d peaks and S 2p peaks of the (a)–(b) MoS2 nanosheets and (c)–(d) ND/MoS2 nanocomposites.
Figure 4. Spectra obtained via X-ray photoelectron spectroscopy. The spectra show Mo 3d peaks and S 2p peaks of the (a)–(b) MoS2 nanosheets and (c)–(d) ND/MoS2 nanocomposites.
Nanomaterials 09 00927 g004
Nanomaterials 09 00927 g005 550
Figure 5. FE-TEM image of (a)–(b) MoS2 nanosheet, (c)–(d) ND, and (e)–(h) ND/MoS2 nanocomposites.
Figure 5. FE-TEM image of (a)–(b) MoS2 nanosheet, (c)–(d) ND, and (e)–(h) ND/MoS2 nanocomposites.
Nanomaterials 09 00927 g005
Nanomaterials 09 00927 g006 550
Figure 6. Cyclic voltammograms of the MoS2 nanosheet and ND/MoS2 nanocomposite with ratio of 1:1, 1:2, 1:4, and 1:8. Scan rates of 0.05, 0.1, and 0.5 V/s were employed for potentials ranging from (a)–(c) −0.8 to 0.2 V and (d)–(f) −0.2 to 1.0 V.
Figure 6. Cyclic voltammograms of the MoS2 nanosheet and ND/MoS2 nanocomposite with ratio of 1:1, 1:2, 1:4, and 1:8. Scan rates of 0.05, 0.1, and 0.5 V/s were employed for potentials ranging from (a)–(c) −0.8 to 0.2 V and (d)–(f) −0.2 to 1.0 V.
Nanomaterials 09 00927 g006

Share and Cite

MDPI and ACS Style

Kim, Y.; Lee, D.; Kim, S.Y.; Kang, E.; Kim, C.K. Nanocomposite Synthesis of Nanodiamond and Molybdenum Disulfide. Nanomaterials 2019, 9, 927. https://doi.org/10.3390/nano9070927

AMA Style

Kim Y, Lee D, Kim SY, Kang E, Kim CK. Nanocomposite Synthesis of Nanodiamond and Molybdenum Disulfide. Nanomaterials. 2019; 9(7):927. https://doi.org/10.3390/nano9070927

Chicago/Turabian Style

Kim, Youngjun, Dukhee Lee, Soo Young Kim, Eunah Kang, and Chang Keun Kim. 2019. "Nanocomposite Synthesis of Nanodiamond and Molybdenum Disulfide" Nanomaterials 9, no. 7: 927. https://doi.org/10.3390/nano9070927

APA Style

Kim, Y., Lee, D., Kim, S. Y., Kang, E., & Kim, C. K. (2019). Nanocomposite Synthesis of Nanodiamond and Molybdenum Disulfide. Nanomaterials, 9(7), 927. https://doi.org/10.3390/nano9070927

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop