Next Article in Journal
Rational Fabrication of Benzene-Linked Porous Polymers for Selective CO2 Capture
Next Article in Special Issue
A Cyanoalkyl Silicone GC Stationary-Phase Polymer as an Extractant for Dispersive Liquid–Liquid Microextraction
Previous Article in Journal
Experimental Investigations of the Detachment of Different Particle Structures from a Magnetizable Fiber in the Gas Phase
Previous Article in Special Issue
Fenton Oxidation Combined with Iron–Carbon Micro-Electrolysis for Treating Leachate Generated from Thermally Treated Sludge
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Separations
Volume 10
Issue 12
10.3390/separations10120580
separations-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Upcycling Textile White Mud to Fabricate MIL-125-Derived Amorphous TiO2@C: Effective Electrocatalyst for Cathodic Reduction of Antibiotics

by
Jinmei Zhu
1,
Xiaofei Wen
2,
Yuanhui Feng
2,
Shuaibing Ren
2,
Zimo Lou
1,2,3,* and
Jiansheng Li
3,*
1
Collaborative Innovation Center of Yangtze River Delta Region Green Pharmaceuticals, Zhejiang University of Technology, Hangzhou 310014, China
2
College of Environment, Zhejiang University of Technology, Hangzhou 310014, China
3
Key Laboratory of Jiangsu Province for Chemical Pollution Control and Resources Reuse, School of Environment and Biological Engineering, Nanjing University of Science and Technology, Nanjing 210094, China
*
Authors to whom correspondence should be addressed.
Separations 2023, 10(12), 580; https://doi.org/10.3390/separations10120580
Submission received: 29 October 2023 / Revised: 17 November 2023 / Accepted: 21 November 2023 / Published: 23 November 2023
(This article belongs to the Collection Feature Paper Collection in Section 'Materials in Separation Science')
Browse Figures
Versions Notes

Abstract

:
Cathodic reduction is a green and promising remediation strategy for reducing the antibacterial activity of antibiotic contaminants and increasing their biodegradability. However, the lack of cost-effective electrocatalysts has restricted its application. In this study, we upcycled textile white mud by separating 1,4-dicarboxybenzene (BDC) and fabricating MIL-125(Ti)-derived amorphous TiO2@C (TiO2@C-W) as a functional electrocatalyst. The separated BDC from white mud shows lower crystallinity than BDC chemicals, but the resulting TiO2@C-W features a much higher degree of oxygen vacancies and a 25-fold higher specific surface area than that of TiO2@C derived from BDC chemicals. With florfenicol (FLO) as a probe, TiO2@C-W exhibits similar cathodic reductive activity (0.017 min−1) as commercial Pd(3 wt.%)/C (0.018 min−1) does, which was 1.4 and 3.7 times higher than that of oxygen vacancy-engineered TiO2 and TiO2@C, respectively. The as-fabricated TiO2@C-W could not easily remove FLO via the oxygen reduction reaction-based pathway with the applied bias for cathodic reduction. Though the activity of TiO2@C-W undergoes a slight decline with continuous running, more than 80% of 20 mg L−1 FLO can still be reduced in the eighth run. Water chemistry studies suggest that a lower initial solution pH boosts the cathodic reduction process, while common co-existing anions such as Cl−, NO3−, HCO3−, and SO32− show a limited negative impact. Finally, TiO2@C-W shows reductive activity against several representative antibiotics, including nitrofurazone, metronidazole, and levofloxacin, clarifying its potential scope of application for antibiotics (e.g., molecules with structures like furan rings, nitro groups, and halogens). This study couples the upcycling of textile white mud with the remediation of antibiotics by developing functional electrocatalysts, and offers new insights for converting wastes from the printing and dyeing industry into value-added products.

1. Introduction

The increasing use of antibiotics has brought global health concerns. As reported, more than 50,000 cases of antibiotic-resistant infections occur annually in Europe and the United States [1]. Due to a relatively lower removal efficiency, antibiotics have been continually released into the natural environment (e.g., soil and aquatic ecosystems), and this could result in the evolution of novel antibiotic-resistant genes and bacteria. Therefore, antibiotics have been widely accepted as contaminants of emerging concern (CECs) [2,3]. Florfenicol (FLO) is a fluorinated chloramphenicol antibiotic that has a broad spectrum of antibacterial activity that includes all organisms sensitive to chloramphenicol, Gram-negative bacilli, Gram-positive cocci, and other atypical bacteria such as mycoplasma. It has been used as an antimicrobial agent for the treatment of bovine respiratory disease and foot rot in aquaculture [4,5], and it has been detected in tap water with a median concentration of 8.9 ng L−1 [6]. Water has been recognized as a receptor for mass fluxes of antibiotics with the emission of waste streams [7]. The development of elimination technology for antibiotics in aqueous settings is highly desired. Various treatment strategies for removing aqueous antibiotic contaminants have been proposed [8]. The biological processes, filtration, and coagulation/flocculation/sedimentation are the most used in conventional wastewater treatment plants. However, the application of biological processes is limited by the poor selectivity [8]. Microbial reductive degradation of antibiotics has been reported to be an economic and environmentally-friendly strategy. Nevertheless, complete elimination was shown to be a time-consuming process [9]. Catalytic degradation by nanomaterials is another option with high reaction rates [10,11,12]; however, the drawbacks of nanomaterials, such as aggregation, passivation, and potential environmental risks, are still in suspense [13,14]. Given that traditional biodegradation methods cannot effectively remove antibiotics, it is necessary to reduce antibacterial activity with a feasible pretreatment approach before waste streams enter the biological treatment unit [15,16].
Cathodic reductive remediation refers to the degradation (conversion) process of refractory contaminants triggered by continuous electrons from the cathode, which is effective for numerous pollutants including halogenated aliphatic/aromatic compounds, nitroaromatics, and antibiotics with specific structures [17,18,19,20]. For antibiotic contaminants, this remediation technology can simultaneously achieve the detoxification and reduction of antimicrobial activity via reaction steps such as dehalogenation, nitro group reduction, and ring-opening [18,21]. Electrocatalysts play an essential role in cathodic reductive remediation, and both noble metals and non-noble metal oxides (or sulfides, phosphides, etc.) have shown their catalytic potentials for this application up to now [22,23,24,25]. Recently, we reported that titanium oxide as a semiconducting material could be engineered with vacancies to effectively catalyze the cathodic reductive degradation of florfenicol (a typical wide-spectrum antibiotic agent) [26]. This strategy overcomes the intrinsic poor conductivity and rare active sites of transition metal oxides, and is expected to convert these inert materials into high-performance electrocatalysts.
Metal–organic frameworks (MOFs) are a class of crystalline micro/mesoporous hybrid materials composed of metal ions or metal clusters interconnected by organic linkers. MOF-derived metal oxides can inherit abundant pore structures, large surface areas, and active sites in MOF, and feature high electrical conductivity and thermal stability [27,28]. Therefore, MOF-derived electrocatalysts have shown their excellent performance in different electrocatalytic reactions such as oxygen evolution, hydrogen evolution, CO2 reduction, and nitrogen reduction reactions [29,30,31,32]. However, to the best of our knowledge, the application of electrocatalysts with MOFs as sacrificial templates for cathodic reduction remediation has rarely been reported.
Textile white mud is a typical industrial waste generated during the alkali weight-reduction process in printing and dyeing plants, which aims at hydrolyzing the ester bond of terylene (polyethylene terephthalate, PET) using alkali liquor to make the fiber relaxed and light [33]. From the perspective of chemical composition, textile white mud contains a majority of 1,4-dicarboxybenzene, followed by a minority of ethylene glycol, oligomers, and some Fe- or Al-based salts (which are used as reagents for coagulation). Indeed, 1,4-dicarboxybenzene (BDC) is a valuable monomer that meets the required criteria as organic linkers in synthesizing a large number of MOFs (e.g., MIL-88B(Fe), MIL-125(Ti), Co-MOF-74) (Figure 1) [34,35,36]. Hence, the recovery of 1,4-dicarboxybenzene from textile white mud for fabricating MOFs and their derivatives can mitigate rising textile sludge wastes while developing a cost-effective synthetic process.
Considering the above, we propose a hydrothermal-based roadmap for the separation of 1,4-dicarboxybenzene from textile white mud and the subsequent fabrication of amorphous MIL-125(Ti)-W, along with its derived TiO2@C-W. Owing to the abundant heteroatoms brought by the co-existing components for BDC separated from textile white mud, TiO2@C-W derived from MIL-125(Ti)-W is expected to show enriched vacancies and an enhanced surface area. Following this hypothesis, TiO2@C-W is predicted to exhibit satisfactory cathodic reduction activity, according to our previous study [26]. In the later sections, the physicochemical characterization of the fabricated MIL-125(Ti)-W and TiO2@C-W, including morphology, crystalline structure, oxygen vacancy, and surface area analysis, is conducted. The effect of water chemistry on FLO removal by TiO2@C-W was investigated. Antibiotics with specific structures including nitrofurazone, metronidazole, and levofloxacin were tested to verify the broad application of TiO2@C-W.

2. Materials and Methods

2.1. Textile White Mud and Chemicals

Textile white mud was collected from a printing and dyeing plant located in Jiaxing City, China. The wet white mud sample was vacuum-dried at 40 °C, crushed, and screened by an 80-mesh sieve, and stored for further use.
Tetrabutyl titanate (C16H36O4Ti, Ti(OBu)4, 98%), 1,4-dicarboxybenzene(C8H6O4, BDC, 99%), hydrofluoric acid (HF, ≥40%), sodium borohydride (NaBH4, 98%), sodium sulfate (Na2SO4, ≥99%), sodium chloride (NaCl, ≥99.8%), sodium bicarbonate (NaHCO3, ≥99.5%), sodium sulfite (Na2SO3, ≥97%), sulfuric acid (H2SO4, 95~98%), and sodium hydroxide (NaOH, ≥96%) were obtained by Sinopharm Chemical Reagent Co., Ltd (Shanghai, China). N,N-dimethylformamide (C3H7NO, DMF, ≥99.5%) and isopropanol (C3H8O, ≥99.7%) were provided by Aladdin Reagent Inc. Florfenicol (FLO, C12H14Cl2FNO4S, 98%) was purchased from Shanghai Ruichu Biotech Co., Ltd., Shanghai, China. Methanol (CH3OH, MeOH, for HPLC, ≥99.9%) and Nafion® solution (5 wt.%) were supplied by Sigma-Aldrich. Toray 090 carbon paper was obtained from the Fuel Cell Store. All aqueous solutions were prepared using Milli-Q DI water (18.2 MΩ cm−1).

2.2. Fabrication of MIL-125(Ti) and TiO2@C Derived from Textile White Mud

Four samples involving MIL-125(Ti) (denoted as MIL-125(Ti)-W) and TiO2@C (denoted as TiO2@C-W) derived from textile white mud, and MIL-125(Ti) and TiO2@C derived from BDC chemicals, were fabricated and compared in this study.
The purification and separation of BDC from textile white mud are discussed in detail in Section 3.1. For the fabrication of MIL-125(Ti)-W, 2.492 g of separated BDC was first dissolved in a mixture of 40 mL of DMF and 10 mL of MeOH in a Teflon autoclave with a capacity of 100 mL. The mixture was sonicated for 20 min to ensure the dissolution of BDC. Then 1.3 mL Ti(OBu)4 was added dropwise with vigorous stirring for 2 h, and the mixture was then maintained at 150 °C for 15 h. After cooling to an ambient temperature, the as-prepared MIL-125(Ti)-W powders were washed and centrifuged by DI water and ethanol several times and dried at 60 °C overnight. For the derived TiO2@C-W, 0.5 g MIL-125(Ti)-W was calcined at 350 °C for 1 h in N2, with the temperature increasing at a rate of 5 °C min−1.
For comparison, MIL-125(Ti) was fabricated using a protocol similar to that used to fabricate MIL-125(Ti)-W, except that the separated BDC was replaced by BDC chemicals. TiO2@C was derived from MIL-125(Ti).
To prepare the working electrode, all the samples were coated onto carbon papers (20 × 20 mm), as described in Text S1.

2.3. Experimental Seup of Cathodic Reduction Test

A cathodic reduction test was performed in an H-type cell, separated by a Grion 0011 cation-exchange membrane (Figure S1). For a typical process, both compartments were filled with 100 mL of Na2SO4 (50 mM) electrolytes, and a target contaminant was added to the catholyte to achieve a certain concentration. Both the working electrode and reference electrode (Ag/AgCl, saturated with 3.0 M KCl solution) were placed into the cathodic chamber, while the counter electrode was placed into the anodic chamber. The cell was controlled by an electrochemical workstation (CHI 650D, Chenhua Co., Shanghai, China) at a constant driving bias. All batch experiments were carried out in triplicate.

2.4. Characterizations and Analytical Methods

Techniques involving X-ray diffraction (XRD, Rigaku Geigerflex with Cu Kα X-ray source), scanning electron microscopy (SEM, Hitachi S-3000N) with an energy dispersive spectrum (EDS), transmission electron microscopy (TEM, JEM-1230 JEOL), Fourier transform infrared spectroscopy (FTIR, PerkinElmer Spectrum Two FT-IR), electron paramagnetic resonance (EPR, Bruker EMXplus X-band), and X-ray photoelectron spectroscopy (XPS, ESCALAB 250Xi, Thermo scientific, Waltham, MA, USA) were used to characterize the powder samples. Total organic carbon (TOC) was measured using a Shimadzu TOC-L analyzer (Kyoto, Japan).
The concentration of aqueous FLO was measured by a high-performance liquid chromatography (HPLC, LC-20AT, Shimadzu, Tokyo, Japan) equipped with an ODS-SP C18 column (150 × 4.6 mm, filler particles with 5 μm size) and a UV detector at 210 nm. The injection volume was 20 μL. The mobile phase was a mixture of 60% methanol and 40% water (containing 0.5% formic acid) at a constant flow rate of 0.8 mL min−1, and the column temperature was maintained at 30 °C. The calibration curve of the tested compound was determined using the HPLC method. The LOD and LOQ of this HLPC method for FLO were measured using a diluting method, and determined to be 40 μg L−1 and 200 μg L−1.

3. Results and Discussion

3.1. Separation of 1,4-Dicarboxybenzene from Textile White Mud

Given that textile white mud consists of not only BDC, but also ethylene glycol, oligomers, and inorganic salts, we first analyzed the elemental components of the dried white mud samples using an elemental analyzer (for C, H, N, and S) and an ICP-OES (for Fe, Si, P, Al, Ca, Mg, Zn, Cr, Cu, and Pb). Despite the main elements like C and H, the content of metal impurities contained in the sample was extremely low, except for Fe and Al, which probably originated from the coagulants used during the precipitation of white mud (Figure 2A). Figure 2B displays a typical SEM image of the sample with its corresponding EDS. Only C and O elements were observed based on the area scan, and the distribution of the O element was even on the solid massive, corresponding to the BDC component.
To separate BDC from textile white mud, a multi-step protocol was adopted on the premise of the physicochemical properties of the impurities, as described in Figure 2C. To remove ethylene glycol and soluble inorganic salts (e.g., Fe and Al-based salts), ~10 g of white mud samples was immersed into 0.5 M H2SO4, fully mixed, and filtered to obtain the filtered cake. Then, to facilitate the hydrolysis of oligomers and promote the crystallization of BDC, a solvothermal process was conducted by re-dispersing the filtered cake into DI water and the pH adjustment to neutral. Finally, the resulting solid–liquid mixture was centrifuged and separated to obtain purified BDC via vacuum filtration. The yield of BDC was approximately 30%, which was consistent with the measurement by high-performance liquid chromatography for the DMF extraction of white mud samples (30.8%).
To identify the separated BDC, we compared its XRD pattern with that of BDC chemicals. Since all the typical peaks in the BDC standard card (PDF# 31-1916) can be observed on both samples in Figure 2D, the feasibility of the separation protocol was verified. Notably, the peak intensity for the separated BDC was remarkably lower than that for BDC chemicals, which is probably due to its relatively low crystallinity. Moreover, Figure 2E shows the FTIR spectra of the BDC samples. In the spectrum of BDC chemicals, the absorption bands at 1575 and 1424 cm−1 belong to COO antisymmetric and symmetric stretching vibrations, respectively. The bands at 568, 733, and 1510 cm−1 were attributed to the vibrations of the phenyl ring [37]. In the spectrum of BDC separated from textile white mud, absorption bands at 1573, 1422, 568, 732, and 1510 cm−1 were found. FT-IR spectrum results indicate that the separated BDC powder shows similar characteristic peaks as BDC chemicals do, again confirming the successful separation of BDC from textile white mud.

3.2. Fabrication and Structural Characterization

Subsequently, we performed different characterization techniques on MIL-125(Ti)-W and TiO2@C-W to understand their structural information, with MIL-125(Ti) and TiO2@C as references, respectively. Figure 3 suggests that carbonization significantly affected the morphologies of materials. MIL-125(Ti)-W features a cake-shaped morphology with a particle size of around 1 μm (Figure 3A), similar to MIL-125 (Figure 3D). The only significant difference is that MIL-125(Ti)-W attained a rougher surface, likely due to the residual impurities inherited from textile white mud. After carbonization, the original morphology of MIL-125(Ti)-W was heavily damaged, and TiO2@C-W was mainly composed of incomplete and porous cake-like structures (Figure 3B). On the contrary, TiO2@C maintained maximally the original appearance of MIL-125 (Figure 3E). This observation agrees with the hypothesis that TiO2@C-W may have more structural defects than TiO2@C does, due to the large numbers of heteroatoms coming from the impurities in BDC separated from white mud. The comparison of TEM images shows that TiO2@C-W (Figure 3C) should possess a much higher specific surface area than TiO2@C (Figure 3F) because hollow structures were constructed during the carbonization of MIL-125(Ti)-W.
XRD patterns of MIL-125(Ti), MIL-125(Ti)-W, TiO2@C, and TiO2@C-W are compared in Figure 4A. The pattern of MIL-125(Ti) fabricated from BDC chemicals was in good accordance with the simulated XRD from the cif-file of CCDC 220475 (the crystallographic data for MIL-125(Ti)) [38]. The main peaks were assigned to the (011), (002), and (121) planes [39]. No sharp peak was found on that of MIL-125(Ti)-W, suggesting that MIL-125(Ti) was present in a highly crystalline state, while MIL-125(Ti)-W was amorphous. After carbonization, both TiO2@C-W and TiO2@C appeared as amorphous forms, suggesting the highly disordered atom arrangement. The building of surface oxygen vacancies (OVs) over the TiO2 catalyst was deemed to increase the electric conductivity and reduce the charge transfer resistance, thus resulting in good electrocatalytic activity [40]. The OVs of TiO2@C and TiO2@C-W were characterized by EPR. As shown in Figure 4B, the field signal at g = 2.003 can be attributed to the defects related to oxygen vacancies [41]. Notably, TiO2@C-W displayed stronger signals than those of TiO2@C, indicating a far higher OV content of TiO2@C-W, though both TiO2@C-W and TiO2@C are disorganized solids. To clarify the state of Ti on the TiO2@C and TiO2@C-W electrodes, a high-resolution XPS of Ti 2p was measured and is illustrated in Figure 4C. The Ti element had two valence states: In the XPS of the Ti2p spectrum of TiO2@C, peaks at a high-binding energy of 458.7 and 465.4 eV were assigned to Ti4+2p3/2 and Ti4+2p1/2, respectively, and the two peaks at 460.3 and 464.3 eV were ascribed to the binding energy of Ti3+2p3/2 and Ti3+2p1/2, respectively. Peaks at a high binding energy of 458.5, 465.2, 459.7, and 464.1 eV were assigned to Ti4+2p3/2, Ti4+2p1/2, Ti3+2p3/2, and Ti3+2p1/2, respectively, in that of TiO2@C-W. The Ti3+/Ti4+ molar ratio of TiO2@C-W (2.0) was significantly higher than that of TiO2@C (0.6). The specific surface area of TiO2@C and TiO2@C-W was determined using a specific surface area analyzer by means of the nitrogen adsorption–desorption isotherm method, calculated with the Brunauer–Emmet–Teller equation. As shown in Figure 4D, the specific surface area of TiO2@C-W was 247.8 m2g−1, which was 25-fold that of TiO2@C (9.9 m2g−1). Collectively, the much-enhanced oxygen vacancy content and specific surface area suggest the elevated cathodic reduction performance of TiO2@C-W.

3.3. Cathodic Reduction Performance of TiO2@C-W

Before evaluating TiO2@C-W, it was essential to distinguish between the contribution of cathodic reduction and electro-Fenton (refers to the selective electrocatalytic reduction of O2 to reactive oxygen species) in this system, because the abundant carbonaceous components in TiO2@C-W may be conducive to an oxygen reduction reaction (ORR). Figure S2 compares the cathodic reduction test of FLO under different atmospheres. Note that the continuous influx of O2 greatly inhibits the FLO removal, and the exclusion of O2 by N2 purging can somehow benefit this process. The participation of ORR was limited in this case. This was probably because the working potential window of the ORR pathway was far from −1.2 V vs. Ag/AgCl.
Secondly, the role of adsorption in FLO removal was addressed by performing a pre-adsorption test without bias. As illustrated in Figure S3, the reduction of FLO by adsorption over different electrocatalysts can be neglected, though the carbonaceous component was included in TiO2@C-W and TiO2@C.
To compare the reaction rate of FLO by different electrocatalysts, the removal kinetic data were described with the classical pseudo-first-order model:
ln(Ct/C0) = −kobs∙t
where Ct (mg L−1) and C0 (mg L−1) are the concentrations of FLO at t and 0 min, and kobs (min −1) refers to the observed rate constant.

3.3.1. Screening of BDC:Ti Molar Ratio and Carbonization Temperature

To determine the optimum fabrication protocol for TiO2@C-W, we sequentially investigated the molar ratio of BDC to Ti during the preparation of the MIL-125(Ti)-W template and the carbonization temperature during the preparation of the derived TiO2@C-W.
As shown in Figure S4A, the FLO reduction efficiency of TiO2@C-W at 180 min achieved 78.4%, with a BDC:Ti molar ratio of 3:0.5. With the decrease of the BDC:Ti molar ratio to 3:1, the FLO reduction efficiency could be elevated to 95.2%. Interestingly, a further decrease in BDC:Ti failed to further increase the performance of TiO2@C-W for FLO reduction. Figure S4B illustrates this phenomenon. Indeed, the BDC:Ti molar ratio during MIL-125(Ti) fabrication was always set as 3:1 in most of the reports [42,43,44]. If the 3:1 molar ratio was enough to construct the framework structure of MIL-125(Ti)-W, then a BDC:Ti molar ratio less than 3:1 may result in a mixture of MIL-125(Ti)-W and an unbound BDC ligand. However, the carbonization process may decompose the unbound BDC, which is probably why the batches with a decreased BDC:Ti molar ratio showed neglected differences for FLO reduction. In contrast, the 3:0.5 molar ratio would lead to a mixture of MIL-125(Ti)-W and extra-hydrolyzed Ti(OH)4 gels. After carbonization, the as-prepared mixture of TiO2@C-W and TiO2 exhibited a poorer performance for FLO reduction than TiO2@C-W alone did. Hence, the BDC:Ti molar ratio of 3:1 enabled good FLO reduction and thus was selected as the appropriate proportion.
The carbonization temperature may simultaneously affect the decomposition extent of MIL-125(Ti)-W and the physicochemical properties of the derived TiO2@C-W. The decomposition temperature of MIL-125(Ti) was reported to be around 350 °C. As shown in Figure S5A,B, the incomplete carbonization temperature (200 °C) would reduce the catalytic activity of TiO2@C-W, while the further increased carbonization temperature (400 °C) showed almost no impact.

3.3.2. Comparison with Other Electrocatalysts

The performance of TiO2@C-W was compared with that of several reference and benchmark electrocatalysts including TiO2@C derived from MIL-125(Ti) fabricated by reagents, pristine TiO2, oxygen vacancy-engineered TiO2 as reported in our previous study (TiO2−x) [26], and commercial Pd(3 wt.%)/C. Figure 5A indicates that TiO2@C-W showed similar catalytic activity for FLO reduction as Pd(3 wt.%)/C did, which was substantially higher than that of TiO2−x, TiO2, and TiO2@C. Figure 5B further quantifies the reaction rate for FLO reduction, which followed an order of Pd(3 wt.%)/C (0.018 min−1)~TiO2@C-W (0.017 min−1) > TiO2−x (0.012 min−1) > TiO2 (0.009 min−1) > TiO2@C (0.005 min−1). The high activity of TiO2@C-W corresponded to its abundant oxygen vacancies (Figure 4B) and large surface area (Figure 4D). This result suggests that TiO2@C-W is a promising electrocatalyst for cathodic reductive remediation.
In addition, we tested the reusability of TiO2@C-W by performing eight consecutive runs, with TiO2@C as a reference. Figure 6 suggests that although the activity of TiO2@C-W underwent a decrease with the increasing number of runs, it was still more reactive than that of TiO2@C. The gradual decreasing activity of TiO2@C-W is likely to be attributed to the partial detachment of powder catalysts from the electrode. Fortunately, the downward trend of activity was alleviated in the final five runs, suggesting that the mechanical stability of TiO2@C-W was acceptable.

3.4. Effect of Solution pH and Co-Existing Ions on Performance of TiO2@C-W

The effect of the solution pH was also studied because it always plays an important role in electrocatalytic reductive dehalogenation reactions [45,46]. Figure 7A presents the cathodic reduction of FLO by TiO2@C-W as a function of time under acidic (pH 3.9), weak acidic (pH 5.6), neutral (pH 7.1), and basic (pH 9.7) conditions, suggesting that TiO2@C-W showed FLO reduction efficiency (95.2%, 180 min) at acidic conditions, which was substantially higher than that at weak acidic (74.1%), neutral (63.0%), and basic conditions (59.9%). These data were fitted with Equation (1). Figure 7B shows that kobs, FLO (0.017 min−1) of TiO2@C-W for FLO reduction was 2.2, 3.0, and 3.3 times higher than that at weak acidic, neutral, and basic conditions, respectively. Indeed, our previous study suggests that the solution could significantly affect the reductive degradation of FLO, mainly because (I) sufficient H+ in the solution could boost the proton transfer during dehalogenation and thus enhance the reaction rate, and (II) overdosed H+ in the solution may inhibit FLO reduction by accelerating the hydrogen evolution reaction (HER) as a side reaction [47]. Since the oxygen vacancy-engineered molecular-imprinted TiO2 prepared in our previous study showed an obvious activity decline when the initial solution pH is lower than 4.0, TiO2@C-W proposed in this study may own a wider pH working range.
Water chemistry can also affect the cathodic reduction of pollutants, because the co-existing ions may adsorb onto the active sites, therefore preventing the pollutants from moving closer to the surface of the electrode. For instance, the presence of co-existing anions such as Cl−, NO3−, and HCO3− has been proven to disturb the catalytic activity of Pd-based cathodes [48]. To elucidate the effect of typical co-existing anions on the reduction of FLO by TiO2@C-W, we repeated the cathodic reduction test in the presence of 2 mM Cl−, 2 mM HCO3−, 2 mM NO3−, and 1 mM SO32−, respectively. Figure 7C suggests that all the selected anions show negligible negative impacts on FLO reduction. Figure 7D confirms the result and the slightly decreased kobs, FLO may be attributed to the fact that the presence of co-existing anions increases the ionic conductivity of the electrolyte and thereby accelerates the HER side reaction [49].

3.5. Cathodic Reduction Performance for Other Antibiotics by TiO2@C-W

We also tested the cathodic reduction performance of TiO2@C-W for other antibiotic contaminants with specific structures including nitrofurazone (NFZ), metronidazole (MNZ), and levofloxacin (LFX). NFZ contains a nitro group and a furan ring in its molecular structure. MNZ features a nitro group and an imidazole ring. LFX is one of the third-generation quinolone antibiotics, containing a fluorine atom in its structure. As shown in Figure 8A, approximately 95% NFZ and 93% MNZ can be removed at 180 min, while the removal efficiency for LFX is relatively low (~68%). Further analysis based on the pseudo-first-order kinetic model indicates that the kobs value of these contaminants follows an order of NFZ (0.019 min−1) > FLO (0.017 min−1) > MNZ (0.015 min−1) > LFX (0.007 min−1) (Figure 8B), which is presumably due to their various moieties. Kong et al. [18] conducted cyclic voltammetry to study the electro-reductive behavior of a series of antibiotics, and found that NFZ is more easily reduced than that of MNZ and FLO. The reduction in TiO2@C-W shows a higher removal efficiency and kobs of the degradation of MNZ, NFZ, and LFX compared with reductions in the previous reports. Furthermore, the toxicity assessment of cathodic reduction degradation products of NFZ and MNZ to selected bacterial strains by Deyong Kong and his co-workers revealed the reduced toxicity of degradation products compared to the parent antibiotics [18]. Generally, the dehalogenation reaction makes halogenated and nitro group reduction compounds less toxic and more readily biodegradable as the addition [50,51].
The total organic carbon (TOC) removal of four antibiotics by TiO2@C-W was investigated. As shown in Figure S6, the TOC removal percentages of FLO and LFX after 2 h were 7% and 15%, respectively, suggesting the two antibiotics were degraded mainly through a reduction pathway along with a slight oxidation reaction. The pathway of the cathodic degradation of NFZ was proposed (Figure S7). The main reaction was the nitro group reduction, and the C-N unsaturated bond and N-N bond were also attacked. Specifically, the cleavage of the N-N bond resulted in the split of a moiety containing organic carbon. Finally, the amine-containing furan ring was degraded to generate two linear chain products. The high TOC removal percentages of the NFZ (48%) could both be attributed to the cleavage of the N-N bond, and the electro-Fenton oxidation (mineralization). Compared to the NFZ degradation, only the nitro group reduction occurred during the MNZ cathodic reduction. A moderate TOC removal (54%) of MNZ was mainly attributed to the electro-Fenton oxidation. The reductive degradation of LFX by TiO2@C-W was out of expectations because LFX degradation is well-known for the oxidation pathway [52], while the less common reduction pathway (e.g., defluorination) requires noble metals [53]. The degradation pathway of LFX in this system will be reported in a follow-up study that is underway.

4. Conclusions

Developing cost-effective, high-performance electrocatalysts is one of the keys to tackling the challenge while promoting the popularization of cathodic remediation. In this study, we propose a novel strategy for upcycling textile white mud, a typical waste from the printing and dyeing industry, to fabricate amorphous TiO2@C for highly efficient cathodic reduction. TiO2@C-W fabricated from separated BDC from white mud features displays a higher degree of oxygen vacancies and a 25-fold higher specific surface area than that of TiO2@C derived from BDC chemicals. TiO2@C-W shares similar cathodic reductive activity as commercial Pd(3 wt.%)/C to antibiotic florfenicol (FLO), and shows acceptable mechanical stability. A lower initial solution pH boosts the cathodic reduction process, while common co-existing anions show limited negative impact. Finally, TiO2@C-W shows reductive activity for several representative antibiotics. The findings from this study obey the “waste control by waste” approach and furnish further directives for the design of electrocatalysts for electro-reductive remediation. The cathode material TiO2@C-W with high reduction efficiency could be potentially applied to the pretreatment of various antibiotics before the biodegradation approach, and the separation of BDC from textile white mud provides a cost-effective raw material for the fabrication of other MOFs (e.g., MIL-88B(Fe), Co-MOF-74). Furthermore, the species of impurities in the separated BDC from white mud and the impacts on TiO2@C could be studied in more depth in future research.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/separations10120580/s1, Text S1. Working electrode preparation. Figure S1: H-type cell for cathodic reduction test. Figure S2: Cathodic reduction test of FLO under different atmospheres. Figure S3: Adsorption of FLO by different electrocatalysts. Figures S4–S5: Effect of molar ratio of BDC:Ti and temperature calcination on the electro-reductive degradation efficiency of FLO. Figure S6: Evolution of solution TOC removal (as mineralization efficiency) as a function of treatment time in cathodic reduction process for florfenicol (FLO), nitrofurazone (NFZ), metronidazole (MNZ) and levofloxacin (LFX) removal by TiO2@C-W. Figure S7: Proposed pathways of the cathodic degradation of nitrofurazone (NFZ) and metronidazole (MNZ). Table S1: Comparison of removal efficiency and kobs with the previous reports. Refs. [54,55,56,57,58,59,60,61] are cited in Supplementary Materials.

Author Contributions

J.Z.: conceptualization, methodology, data curation. X.W.: data curation, formal analysis. Y.F.: validation, investigation. S.R.: software, formal analysis. Z.L.: conceptualization, investigation, funding acquisition, writing—original draft. J.L.: supervision, funding acquisition, writing—review & editing. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by Zhejiang Provincial Natural Science Foundation of China (LQ21B070002), the National Natural Science Foundation of China (U22A20433) and the Funda-mental Research Funds for the Provincial Universities of Zhejiang (RF-A2023010).

Data Availability Statement

The data that support the findings of the study are available from the corresponding author upon request.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. O’Neill, J. Review on Antimicrobial Resistance. In Antimicrobial Resistance: Tackling a Crisis for the Health and Wealth of Nations; The Wellcome Trust and UK Government: London, UK, 2014. [Google Scholar]
  2. Jechalke, S.; Heuer, H.; Siemens, J.; Amelung, W.; Smalla, K. Fate and effects of veterinary antibiotics in soil. Trends Microbiol. 2014, 22, 536–545. [Google Scholar] [CrossRef] [PubMed]
  3. Michael, I.; Rizzo, L.; McArdell, C.S.; Manaia, C.M.; Merlin, C.; Schwartz, T.; Dagot, C.; Fatta-Kassinos, D. Urban wastewater treatment plants as hotspots for the release of antibiotics in the environment: A review. Water Res. 2013, 47, 957–995. [Google Scholar] [CrossRef] [PubMed]
  4. Sapkota, A.; Sapkota, A.R.; Kucharski, M.; Burke, J.; McKenzie, S.; Walker, P.; Lawrence, R. Aquaculture Practices and Potential Human Health Risks: Current Knowledge and Future Priorities. Environ. Int. 2008, 34, 1215–1226. [Google Scholar] [CrossRef]
  5. Cabello, F.C.; Godfrey, H.P.; Tomova, A.; Ivanova, L.; Dölz, H.; Millanao, A.; Buschmann, A.H. Antimicrobial Use in Aquaculture Re-Examined: Its Relevance to Antimicrobial Resistance and to Animal and Human Health. Environ. Microbiol. 2013, 15, 1917–1942. [Google Scholar] [CrossRef]
  6. Wang, H.; Wang, N.; Wang, B.; Zhao, Q.; Fang, H.; Fu, C.; Tang, C.; Jiang, F.; Zhou, Y.; Chen, Y.; et al. Antibiotics in Drinking Water in Shanghai and Their Contribution to Antibiotic Exposure of School Children. Environ. Sci. Technol. 2016, 50, 2692–2699. [Google Scholar] [CrossRef]
  7. Chen, H.; Jing, L.; Teng, Y.; Wang, J. Multimedia fate modeling and risk assessment of antibiotics in a water-scarce megacity. J. Hazard. Mater. 2018, 348, 75–83. [Google Scholar] [CrossRef] [PubMed]
  8. Homem, V.; Santos, L. Degradation and removal methods of antibiotics from aqueous matrices--a review. J. Environ. Manag. 2011, 92, 2304–2347. [Google Scholar] [CrossRef]
  9. Fagervold, S.K.; Watts, J.E.M.; May, H.D.; Sowers, K.R. Effects of bioaugmentation on indigenous PCB dechlorination activity in sediment microcosms. Water Res. 2011, 45, 3899–3907. [Google Scholar] [CrossRef]
  10. Agarwal, S.; Al-Abed, S.R.; Dionysiou, D.D.; Graybill, E. Reactivity of substituted chlorines and ensuing dechlorination pathways of select PCB congeners with Pd/Mg bimetallics. Environ. Sci. Technol. 2009, 43, 915–921. [Google Scholar] [CrossRef]
  11. Agarwal, S.; Al-Abed, S.R.; Dionysiou, D.D. A feasibility study on Pd/Mg application in historically contaminated sediments and PCB spiked substrates. J. Hazard. Mater. 2009, 172, 1156–1162. [Google Scholar] [CrossRef]
  12. Han, Y.L.; Yan, W.L. Reductive dechlorination of trichloroethene by zero-valent iron nanoparticles: Reactivity enhancement through sulfidation treatment. Environ. Sci. Technol. 2016, 50, 12992–13001. [Google Scholar] [CrossRef] [PubMed]
  13. Phenrat, T.; Saleh, N.; Sirk, K.; Tilton, R.D.; Lowry, G.V. Aggregation and sedimentation of aqueous nanoscale zerovalent iron dispersions. Environ. Sci. Technol. 2007, 41, 284–290. [Google Scholar] [CrossRef] [PubMed]
  14. Xu, J.; Tan, L.S.; Baig, S.A.; Wu, D.L.; Lv, X.S.; Xu, X.H. Dechlorination of 2,4-dichlorophenol by nanoscale magnetic Pd/Fe particles: Effects of pH, temperature, common dissolved ions and humic acid. Chem. Eng. J. 2013, 231, 26–35. [Google Scholar] [CrossRef]
  15. Wu, S.; Qi, Y.; Fan, C.; Dai, B.; Huang, J.; Zhou, W.; He, S.; Gao, L. Improvement of anaerobic biological treatment effect by catalytic micro-electrolysis for monensin production wastewater. Chem. Eng. J. 2016, 296, 260–267. [Google Scholar] [CrossRef]
  16. Belkheiri, D.; Fourcade, F.; Geneste, F.; Floner, D.; Aït-Amar, H.; Amrane, A. Feasibility of an electrochemical pre-treatment prior to a biological treatment for tetracycline removal. Sep. Purif. Technol. 2011, 83, 151–156. [Google Scholar] [CrossRef]
  17. Radjenović, J.; Farré, M.J.; Mu, Y.; Gernjak, W.; Keller, J. Reductive electrochemical remediation of emerging and regulated disinfection byproducts. Water Res. 2012, 46, 1705–1714. [Google Scholar] [CrossRef]
  18. Kong, D.; Liang, B.; Yun, H.; Cheng, H.; Ma, J.; Cui, M.; Wang, A.; Ren, N. Cathodic degradation of antibiotics: Characterization and pathway analysis. Water Res. 2015, 72, 281–292. [Google Scholar] [CrossRef]
  19. Kong, D.; Liang, B.; Yun, H.; Ma, J.; Li, Z.; Wang, A.; Ren, N. Electrochemical degradation of nitrofurans furazolidone by cathode: Characterization, pathway and antibacterial activity analysis. Chem. Eng. J. 2015, 262, 1244–1251. [Google Scholar] [CrossRef]
  20. Deng, J.; Hu, X.M.; Gao, E.; Wu, F.; Yin, W.; Huang, L.Z.; Dionysiou, D.D. Electrochemical reductive remediation of trichloroethylene contaminated groundwater using biomimetic iron-nitrogen-doped carbon. J. Hazard. Mater. 2021, 419, 126458. [Google Scholar] [CrossRef]
  21. Lou, Z.; Yu, C.; Wen, X.; Xu, Y.; Yu, J.; Xu, X. Construction of Pd nanoparticles/two-dimensional Co-MOF nanosheets heterojunction for enhanced electrocatalytic hydrodechlorination. Appl. Catal. B Environ. 2022, 317, 121730. [Google Scholar] [CrossRef]
  22. Yang, L.; Chen, Z.; Cui, D.; Luo, X.; Liang, B.; Yang, L.; Liu, T.; Wang, A.; Luo, S. Ultrafine palladium nanoparticles supported on 3D self-supported Ni foam for cathodic dechlorination of florfenicol. Chem. Eng. J. 2019, 359, 894–901. [Google Scholar] [CrossRef]
  23. Yang, L.; Chen, Z.; Ma, T.; Zhang, S.; Dai, W.; Xiao, X.; Luo, X.; Zou, J.; Tu, X.; Yang, L.; et al. Efficient electrochemical dehalogenation of florfenicol without discharging toxic intermediates via direct electron transfer over electrochromic WO3. Chem. Eng. J. 2021, 412, 127481. [Google Scholar] [CrossRef]
  24. Liu, H.; Han, J.; Yuan, J.; Liu, C.; Wang, D.; Liu, T.; Liu, M.; Luo, J.; Wang, A.; Crittenden, J.C. Deep Dehalogenation of Florfenicol Using Crystalline CoP Nanosheet Arrays on a Ti Plate via Direct Cathodic Reduction and Atomic H. Environ. Sci. Technol. 2019, 53, 11932–11940. [Google Scholar] [CrossRef]
  25. Yang, J.; Jiang, S.-F.; Hu, W.-F.; Jiang, H. Highly efficient electrochemical dechlorination of florfenicol by an ultrathin molybdenum disulfide cathode. Chem. Eng. J. 2022, 427, 131600. [Google Scholar] [CrossRef]
  26. Lou, Z.; Wen, X.; Song, L.; Yan, C.; Chen, H.; Lu, T.; Yu, J.; Xu, X.; Li, J. Oxygen vacancy engineered molecular imprinted TiO2 for preferential florfenicol remediation by electro-reductive approach: Enhanced dehalogenation performance and elimination of antibiotic resistance genes. Appl. Catal. B Environ. 2023, 336, 122923. [Google Scholar] [CrossRef]
  27. Xiao, L.; Wang, Z.; Guan, J. 2D MOFs and their derivatives for electrocatalytic applications: Recent advances and new challenges. Coord. Chem. Rev. 2022, 472, 214777. [Google Scholar] [CrossRef]
  28. Munawar, T.; Bashir, A.; Nadeem, M.S.; Mukhtar, F.; Manzoor, S.; Ashiq, M.N.; Khan, S.A.; Koc, M.; Iqbal, F. Scalable synthesis of MOF-derived Nd2O3@C and V2O5@C nanohybrid: Efficient electrocatalyst for OER in alkaline medium. Fuel 2024, 355, 129485. [Google Scholar] [CrossRef]
  29. Hyoun Ahn, C.; Seok Yang, W.; Jae Kim, J.; Sudha Priyanga, G.; Thomas, T.; Deshpande, N.G.; Seong Lee, H.; Koun Cho, H. Design of hydrangea-type Co/Mo bimetal MOFs and MOF-derived Co/Mo2C embedded carbon composites for highly efficient oxygen evolution reaction. Chem. Eng. J. 2022, 435, 134815. [Google Scholar] [CrossRef]
  30. Wang, X.; He, J.; Yu, B.; Sun, B.; Yang, D.; Zhang, X.; Zhang, Q.; Zhang, W.; Gu, L.; Chen, Y. CoSe2 nanoparticles embedded MOF-derived Co-N-C nanoflake arrays as efficient and stable electrocatalyst for hydrogen evolution reaction. Appl. Catal. B Environ. 2019, 258, 117996. [Google Scholar] [CrossRef]
  31. Wang, X.; Fan, M.; Guan, Y.; Liu, Y.; Liu, M.; Karsili, T.N.V.; Yi, J.; Zhou, X.-D.; Zhang, J. MOF-based electrocatalysts for high-efficiency CO2 conversion: Structure, performance, and perspectives. J. Mater. Chem. A 2021, 9, 22710. [Google Scholar] [CrossRef]
  32. Liu, P.-Y.; Shi, K.; Chen, W.-Z.; Gao, R.; Liu, Z.-L.; Hao, H.; Wang, Y.-Q. Enhanced electrocatalytic nitrogen reduction reaction performance by interfacial engineering of MOF-based sulfides FeNi2S4/NiS hetero-interface. Appl. Catal. B Environ. 2021, 287, 119956. [Google Scholar] [CrossRef]
  33. Fan, L.; Zhang, L.; Shen, J.; Wang, S.; Chen, H. Study on recovery and refining of TA from alkali reduction wastewater. Desalination 2007, 206, 353–357. [Google Scholar] [CrossRef]
  34. Hu, S.; Xie, C.; Xu, Y.P.; Chen, X.; Gao, M.L.; Wang, H.; Yang, W.; Xu, Z.N.; Guo, G.C.; Jiang, H.L. Selectivity Control in the Direct CO Esterification over Pd@UiO-66: The Pd Location Matters. Angew. Chem. Int. Ed. 2023, 62, e202311625. [Google Scholar] [CrossRef] [PubMed]
  35. Hendon, C.H.; Tiana, D.; Fontecave, M.; Sanchez, C.; D’arras, L.; Sassoye, C.; Rozes, L.; Mellot-Draznieks, C.; Walsh, A. Engineering the optical response of the titanium-MIL-125 metal-organic framework through ligand functionalization. J. Am. Chem. Soc. 2013, 135, 10942–10945. [Google Scholar] [CrossRef]
  36. Wang, D.; Wu, G.; Zhao, Y.; Cui, L.; Shin, C.H.; Ryu, M.H.; Cai, J. Study on the copper(II)-doped MIL-101(Cr) and its performance in VOCs adsorption. Environ. Sci. Pollut. Res. 2018, 25, 28109–28119. [Google Scholar] [CrossRef] [PubMed]
  37. Yang, Z.; Gao, L.; Li, J.; Lin, J.; Wang, J. Facile synthesis of Cu-BDC/Poly(N-methylol acrylamide) HIPE monoliths via CO2-in-water Emulsion stabilized by metal-organic framework. Polymer 2018, 153, 17–23. [Google Scholar] [CrossRef]
  38. Jeremias, F.; Lozan, V.; Henninger, S.K.; Janiak, C. Programming MOFs for water sorption: Amino-functionalized MIL-125 and UiO-66 for heat transformation and heat storage applications. Dalton Trans. 2013, 42, 15967–15973. [Google Scholar] [CrossRef]
  39. Friebe, S.; Mundstock, A.; Unruh, D.; Renz, F.; Caro, J. NH2-MIL-125 as membrane for carbon dioxide sequestration: Thin supported MOF layers contra Mixed-Matrix-Membranes. J. Membr. Sci. 2016, 51, 185–193. [Google Scholar] [CrossRef]
  40. Liu, C.; Zhang, A.; Pei, D.; Yu, H. Efficient electrochemical reduction of nitrobenzene by defect-engineered TiO2–x single crystal, Environ. Sci. Technol. 2016, 50, 5234–5242. [Google Scholar] [CrossRef]
  41. Wang, Z.; Wang, K.; Wang, H.; Chen, X.; Dai, W.; Fu, X. The correlation between surface defects and the behavior of hydrogen adsorption over ZnO under UV light irradiation. Catal. Sci. Technol. 2018, 8, 3260–3277. [Google Scholar] [CrossRef]
  42. Oveisi, M.; Asli, M.A.; Mahmoodi, N.M. MIL-Ti metal-organic frameworks (MOFs) nanomaterials as superior adsorbents: Synthesis and ultrasound-aided dye adsorption from multicomponent wastewater systems. J. Hazard. Mater. 2018, 347, 123–140. [Google Scholar] [CrossRef]
  43. Abdul Mubarak, N.S.; Foo, K.Y.; Schneider, R.; Abdelhameed, R.M.; Sabar, S. The chemistry of MIL-125 based materials: Structure, synthesis, modification strategies and photocatalytic applications. J. Environ. Chem. Eng. 2022, 10, 106883. [Google Scholar] [CrossRef]
  44. Yue, K.; Zhang, X.; Jiang, S.; Chen, J.; Yang, Y.; Bi, F.; Wang, Y. Recent advances in strategies to modify MIL-125 (Ti) and its environmental applications. J. Mol. Liq. 2021, 335, 116108. [Google Scholar] [CrossRef]
  45. Wu, Y.; Gan, L.; Zhang, S.; Jiang, B.; Song, H.; Li, W.; Pan, Y.; Li, A. Enhanced electrocatalytic dechlorination of para-chloronitrobenzene based on Ni/Pd foam electrode. Chem. Eng. J. 2017, 316, 146–153. [Google Scholar] [CrossRef]
  46. Mao, Z.; Liu, L.; Yang, H.B.; Zhang, Y.; Yao, Z.; Wu, H.; Huang, Y.; Xu, Y.; Liu, B. Atomically dispersed Pd electrocatalyst for efficient aqueous phase dechlorination reaction. Electrochim. Acta 2021, 391, 138886. [Google Scholar] [CrossRef]
  47. Jiang, G.; Lan, M.; Zhang, Z.; Lv, X.; Lou, Z.; Xu, X.; Dong, F.; Zhang, S. Identification of Active Hydrogen Species on Palladium Nanoparticles for an Enhanced Electrocatalytic Hydrodechlorination of 2,4-Dichlorophenol in Water. Environ. Sci. Technol. 2017, 51, 7599–7605. [Google Scholar] [CrossRef] [PubMed]
  48. Lowry, G.V.; Reinhard, M. Pd-Catalyzed TCE Dechlorination in Groundwater:  Solute Effects, Biological Control, and Oxidative Catalyst Regeneration. Environ. Sci. Technol. 2000, 34, 3217–3223. [Google Scholar] [CrossRef]
  49. Wang, H.; Gao, L. Recent developments in electrochemical hydrogen evolution reaction. Curr. Opin. Electrochem. 2018, 7, 7–14. [Google Scholar] [CrossRef]
  50. Brown, D.; Laboureur, P. The aerobic biodegradability of primary aromatic amines. Chemosphere 1983, 12, 405–414. [Google Scholar] [CrossRef]
  51. Donlon, B.A.; RazoFlores, E.; Lettinga, G.; Field, J.A. Continuous detoxification, transformation, and degradation of nitrophenols in upflow anaerobic sludge blanket (UASB) reactors. Biotechnol. Bioeng. 1996, 51, 439–449. [Google Scholar] [CrossRef]
  52. Tazwar, G.; Jain, A.; Devra, V. Oxidative degradation of levofloxacin by water-soluble manganese dioxide in aqueous acidic medium: A kinetic study. Chem. Pap. 2017, 71, 1749–1758. [Google Scholar] [CrossRef]
  53. Liu, H.; Ding, Y.; Tang, H.; Du, Y.; Zhang, D.; Tang, Y.; Liu, C. Electrocatalytic deep dehalogenation of florfenicol using Fe-doped CoP nanotubes array for blocking resistance gene expression and microbial inhibition during biochemical treatment. Water Res. 2021, 201, 117361. [Google Scholar] [CrossRef]
  54. Kong, D.; Yun, H.; Cui, D.; Qi, M.; Shao, C.; Cui, D.; Ren, N.; Liang, B.; Wang, A. Response of antimicrobial nitrofurazone-degrading biocathode communities to different cathode potentials. Bioresour. Technol. 2017, 241, 951–958. [Google Scholar] [CrossRef]
  55. Wang, B.; Lv, X.; Feng, D.; Xie, L.; Zhang, J.; Li, M.; Xie, Y.; Li, J.; Zhou, H. Highly Stable Zr(IV)-Based Metal-Organic Frameworks for the Detection and Removal of Antibiotics and Organic Explosives in Water. J. Am. Chem. Soc. 2016, 138, 6204–6216. [Google Scholar] [CrossRef]
  56. Chen, J.; Qiu, X.; Fang, Z.; Yang, M.; Pokeung, T.; Gu, F.; Cheng, W.; Lan, B. Removal mechanism of antibiotic metronidazole from aquatic solutions by using nanoscale zero-valent iron particles. Chem. Eng. J. 2012, 181–182, 113–119. [Google Scholar] [CrossRef]
  57. Forouzesh, M.A.; Ebadi, A.; Aghaeinejad-Meybodi, A. Degradation of metronidazole antibiotic in aqueous medium using activated carbon as a persulfate activator. Purif. Technol. 2019, 240, 145–151. [Google Scholar] [CrossRef]
  58. Tran, M.; Fu, C.; Juang, R. Effects of water matrix components on degradation efficiency and pathways of antibiotic metronidazole by UV/TiO2 photocatalysis. J. Mol. Liq. 2019, 276, 32–38. [Google Scholar] [CrossRef]
  59. Guo, W.; Shi, Y.; Wang, H.; Yang, H.; Zhang, G. Intensification of sonochemical degradation of antibiotics levofloxacin using carbon tetrachloride. Ultrason Sonochem. 2010, 17, 680–684. [Google Scholar] [CrossRef]
  60. Kansal, S.; Kundu, P.; Sood, S.; Lamba, R.; Umar, A.; Mehta, S.K. Photocatalytic degradation of antibiotic levofloxacin using well-crystalline TiO2 nanoparticles. New J. Chem. 2014, 38, 3220–3226. [Google Scholar]
  61. Xia, Y.; Dai, Q. Electrochemical degradation of antibiotic levofloxacin by PbO2 electrode: Kinetics, energy demands and reaction pathways. Chemosphere 2018, 205, 215–222. [Google Scholar] [CrossRef]
Separations 10 00580 g001
Figure 1. The polyhedral structure of MIL-88B(Fe), MIL-125(Ti), and Co-MOF-74.
Figure 1. The polyhedral structure of MIL-88B(Fe), MIL-125(Ti), and Co-MOF-74.
Separations 10 00580 g001
Separations 10 00580 g002aSeparations 10 00580 g002b
Figure 2. (A) Elemental components of textile white mud; (B) SEM image, dark field image, corresponding EDS spectra, and elemental mapping of textile white mud; (C) scheme of separation of BDC from textile white mud; (D) XRD patterns of BDC separated from textile white mud and BDC chemicals; (E) FTIR spectra of BDC separated from textile white mud and BDC chemicals.
Figure 2. (A) Elemental components of textile white mud; (B) SEM image, dark field image, corresponding EDS spectra, and elemental mapping of textile white mud; (C) scheme of separation of BDC from textile white mud; (D) XRD patterns of BDC separated from textile white mud and BDC chemicals; (E) FTIR spectra of BDC separated from textile white mud and BDC chemicals.
Separations 10 00580 g002aSeparations 10 00580 g002b
Separations 10 00580 g003
Figure 3. SEM images of (A) MIL-125(Ti)-W (inset: corresponding TEM image) and (B) TiO2@C-W; (C) TEM image of TiO2@C-W; SEM images of (D) MIL-125(Ti) (inset: corresponding TEM image) and (E) TiO2@C; (F) TEM image of TiO2@C.
Figure 3. SEM images of (A) MIL-125(Ti)-W (inset: corresponding TEM image) and (B) TiO2@C-W; (C) TEM image of TiO2@C-W; SEM images of (D) MIL-125(Ti) (inset: corresponding TEM image) and (E) TiO2@C; (F) TEM image of TiO2@C.
Separations 10 00580 g003
Separations 10 00580 g004
Figure 4. (A) XRD patterns of MIL-125(Ti), MIL-125(Ti)-W, TiO2@C, and TiO2@C-W; (B) EPR spectra of TiO2@C and TiO2@C-W; (C) Ti 2p XPS of TiO2@C and TiO2@C-W; (D) N2 adsorption–desorption isotherm of TiO2@C and TiO2@C-W.
Figure 4. (A) XRD patterns of MIL-125(Ti), MIL-125(Ti)-W, TiO2@C, and TiO2@C-W; (B) EPR spectra of TiO2@C and TiO2@C-W; (C) Ti 2p XPS of TiO2@C and TiO2@C-W; (D) N2 adsorption–desorption isotherm of TiO2@C and TiO2@C-W.
Separations 10 00580 g004
Separations 10 00580 g005
Figure 5. (A) Ct/C0 and (B) pseudo-first-order kinetic rate constants for FLO reduction by TiO2@C-W, TiO2@C, TiO2, TiO2−x, and Pd(3 wt.%)/C (reaction conditions: [FLO]0 = 20 mg L−1, applied bias = −1.2 V, [Na2SO4] = 50 mM).
Figure 5. (A) Ct/C0 and (B) pseudo-first-order kinetic rate constants for FLO reduction by TiO2@C-W, TiO2@C, TiO2, TiO2−x, and Pd(3 wt.%)/C (reaction conditions: [FLO]0 = 20 mg L−1, applied bias = −1.2 V, [Na2SO4] = 50 mM).
Separations 10 00580 g005
Separations 10 00580 g006
Figure 6. Evolution of Ct, FLO/C0, FLO in each run during a consecutive 8-run reusability test of TiO2@C and TiO2@C-W, (reaction conditions: [FLO]0 = 20 mg L−1, applied bias = −1.2 V, [Na2SO4] = 50 mM).
Figure 6. Evolution of Ct, FLO/C0, FLO in each run during a consecutive 8-run reusability test of TiO2@C and TiO2@C-W, (reaction conditions: [FLO]0 = 20 mg L−1, applied bias = −1.2 V, [Na2SO4] = 50 mM).
Separations 10 00580 g006
Separations 10 00580 g007
Figure 7. Effect of initial solution pH on (A) reduction efficiency (Ct,FLO/C0,FLO) and (B) pseudo-first-order kinetic rate constants kobs,FLO by TiO2@C-W; effect of co-existing anions on (C) reduction efficiency (Ct,FLO/C0,FLO) and (D) pseudo-first-order kinetic rate constants kobs,FLO by TiO2@C-W (reaction conditions: [FLO]0 = 20 mg L−1, applied bias = −1.2 V, [Na2SO4] = 50 mM).
Figure 7. Effect of initial solution pH on (A) reduction efficiency (Ct,FLO/C0,FLO) and (B) pseudo-first-order kinetic rate constants kobs,FLO by TiO2@C-W; effect of co-existing anions on (C) reduction efficiency (Ct,FLO/C0,FLO) and (D) pseudo-first-order kinetic rate constants kobs,FLO by TiO2@C-W (reaction conditions: [FLO]0 = 20 mg L−1, applied bias = −1.2 V, [Na2SO4] = 50 mM).
Separations 10 00580 g007
Separations 10 00580 g008
Figure 8. (A) Ct/C0 and (B) pseudo-first-order kinetic rate constants for nitrofurazone (NFZ), metronidazole (MNZ) and levofloxacin (LFX) removal by TiO2@C-W (reaction conditions: [NFZ]0 = [MNZ]0 = [FLO]0 = 20 mg L−1, applied bias = −1.2 V, [Na2SO4] = 50 mM).
Figure 8. (A) Ct/C0 and (B) pseudo-first-order kinetic rate constants for nitrofurazone (NFZ), metronidazole (MNZ) and levofloxacin (LFX) removal by TiO2@C-W (reaction conditions: [NFZ]0 = [MNZ]0 = [FLO]0 = 20 mg L−1, applied bias = −1.2 V, [Na2SO4] = 50 mM).
Separations 10 00580 g008
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Zhu, J.; Wen, X.; Feng, Y.; Ren, S.; Lou, Z.; Li, J. Upcycling Textile White Mud to Fabricate MIL-125-Derived Amorphous TiO2@C: Effective Electrocatalyst for Cathodic Reduction of Antibiotics. Separations 2023, 10, 580. https://doi.org/10.3390/separations10120580

AMA Style

Zhu J, Wen X, Feng Y, Ren S, Lou Z, Li J. Upcycling Textile White Mud to Fabricate MIL-125-Derived Amorphous TiO2@C: Effective Electrocatalyst for Cathodic Reduction of Antibiotics. Separations. 2023; 10(12):580. https://doi.org/10.3390/separations10120580

Chicago/Turabian Style

Zhu, Jinmei, Xiaofei Wen, Yuanhui Feng, Shuaibing Ren, Zimo Lou, and Jiansheng Li. 2023. "Upcycling Textile White Mud to Fabricate MIL-125-Derived Amorphous TiO2@C: Effective Electrocatalyst for Cathodic Reduction of Antibiotics" Separations 10, no. 12: 580. https://doi.org/10.3390/separations10120580

APA Style

Zhu, J., Wen, X., Feng, Y., Ren, S., Lou, Z., & Li, J. (2023). Upcycling Textile White Mud to Fabricate MIL-125-Derived Amorphous TiO2@C: Effective Electrocatalyst for Cathodic Reduction of Antibiotics. Separations, 10(12), 580. https://doi.org/10.3390/separations10120580

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop