Next Article in Journal
Cobalt-Catalyzed Cyclization of 2-Bromobenzamides with Carbodiimides: A New Route for the Synthesis of 3-(Imino)isoindolin-1-ones
Next Article in Special Issue
Investigation of Metastable Low Dimensional Halometallates
Previous Article in Journal
Elucidating the Glucokinase Activating Potentials of Naturally Occurring Prenylated Flavonoids: An Explicit Computational Approach
Previous Article in Special Issue
A Metastable p-Type Semiconductor as a Defect-Tolerant Photoelectrode
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 26
Issue 23
10.3390/molecules26237210
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Study of Integer Spin S = 1 in the Polar Magnet β-Ni(IO3)2

by
Ebube E. Oyeka
1,
Michał J. Winiarski
2 and
Thao T. Tran
1,*
1
Department of Chemistry, Clemson University, Clemson, SC 29634, USA
2
Advanced Materials Center, Faculty of Applied Physics and Mathematics, Gdansk University of Technology, ul. Narutowicza 11/12, 80-233 Gdansk, Poland
*
Author to whom correspondence should be addressed.
Molecules 2021, 26(23), 7210; https://doi.org/10.3390/molecules26237210
Submission received: 1 October 2021 / Revised: 23 November 2021 / Accepted: 26 November 2021 / Published: 28 November 2021
(This article belongs to the Special Issue Emerging Frontiers in Metastable Crystalline Solids)
Browse Figures
Versions Notes

Abstract

:
Polar magnetic materials exhibiting appreciable asymmetric exchange interactions can potentially host new topological states of matter such as vortex-like spin textures; however, realizations have been mostly limited to half-integer spins due to rare numbers of integer spin systems with broken spatial inversion lattice symmetries. Here, we studied the structure and magnetic properties of the S = 1 integer spin polar magnet β-Ni(IO3)2 (Ni2+, d8, 3F). We synthesized single crystals and bulk polycrystalline samples of β-Ni(IO3)2 by combining low-temperature chemistry techniques and thermal analysis and characterized its crystal structure and physical properties. Single crystal X-ray and powder X-ray diffraction measurements demonstrated that β-Ni(IO3)2 crystallizes in the noncentrosymmetric polar monoclinic structure with space group P21. The combination of the macroscopic electric polarization driven by the coalignment of the (IO3)− trigonal pyramids along the b axis and the S = 1 state of the Ni2+ cation was chosen to investigate integer spin and lattice dynamics in magnetism. The effective magnetic moment of Ni2+ was extracted from magnetization measurements to be 3.2(1) µB, confirming the S = 1 integer spin state of Ni2+ with some orbital contribution. β-Ni(IO3)2 undergoes a magnetic ordering at T = 3 K at a low magnetic field, μ0H = 0.1 T; the phase transition, nevertheless, is suppressed at a higher field, μ0H = 3 T. An anomaly resembling a phase transition is observed at T ≈ 2.7 K in the Cp/T vs. T plot, which is the approximate temperature of the magnetic phase transition of the material, indicating that the transition is magnetically driven. This work offers a useful route for exploring integer spin noncentrosymmetric materials, broadening the phase space of polar magnet candidates, which can harbor new topological spin physics.

1. Introduction

The lack of spatial inversion symmetry can stabilize asymmetric exchange interactions in systems with unpaired electrons, giving rise to novel physical phenomena such as multiferroics and topological spin textures [1,2,3,4,5,6]. However, engineering noncentrosymmetric (NCS) polar crystal structures for magnetic materials remains difficult, owing to a combination of several factors such as dipole-dipole interaction, steric effect, and thermodynamic effects, which often yield centrosymmetric lattices in transition metal complexes [7,8,9,10]. Polar asymmetric anions with stereo-active lone-pair electrons such as (SeO3)2− and (IO3)− trigonal pyramids provide avenues for accessing NCS polar structures, facilitated by the second-order Jahn–Teller distortion [6,11,12,13,14,15]. The presence of stereo-active lone-pair electrons and strong spin-orbit coupling from the heavy element (Se, I) in these asymmetric units have been shown to enhance Dzyaloshinskii-Moriya (DM) interaction [3,16].
Increased asymmetric exchange interactions in polar magnets with half-integer spins such as Cu2OSeO3 (Cu2+, d9, 2D), Fe(IO3)3 (Fe3+, d5, 6S), and VOSe2O5 (V4+, d1, 2D) have been demonstrated [2,16,17]; however, studies in integer spin systems featuring the DM interaction have been left unexplored. This is, in part, because there are relatively few integer spin magnets to investigate that have NCS polar lattice symmetries. It has been shown that half-integer and integer spin systems have different magnetic ground states, that is, the former favors a gapless state while the latter has an excitation gap (Haldane gap) between the singlet ground state and the first excited triplet state [18,19,20,21]. An excitation would cost energy in the order of the nearest-neighbor exchange interaction. Here, we study the effects of integer spin in the presence of asymmetric exchange interaction on magnetic properties by looking into the S = 1 polar magnet β-Ni(IO3)2 (Ni2+, d8, 3F).
β-Ni(IO3)2 crystals are twinned by pseudo-merohedry, challenging its structural modelling as well as interpretation of its structure-property relationships [22]. In addition, Ni(IO3)2 is polymorphic and can condense in hydrate forms depending on atmospheric and synthetic conditions, adding an extra layer of efforts that need to be invested in selectively synthesizing β-Ni(IO3)2 as well as characterizing the structural and physical properties of this polymorph. The crystal structure of β-Ni(IO3)2 was previously reported [22]; however, no connections between its chemistry, crystal structure, and physical properties have been established. In this study, we developed a method for synthesizing single crystals and bulk-polycrystalline samples of β-Ni(IO3)2 that exhibit NCS polar structure with integer spin S = 1. We demonstrate that the synthetic chemistry can be used to prepare high-quality bulk polycrystals and single crystalline sample of transition-metal iodates. Furthermore, we probed spin and orbital contribution to the effective magnetic moment of β-Ni(IO3)2 by performing magnetization measurements. We supplement magnetic properties with specific heat characterization to solidify the thermodynamic signature of the phase transition in this material. This work represents a step forward in accessing atomic engineering of integer spin and breaking inversion symmetry in polar magnets.

2. Materials and Methods

Reagents. NiCl2 (Alfa Aesar, Tewksbury, MA, USA, 99%), ZnCl2 (Alfa Aesar, Tewksbury, MA, UAS, 99.95%), HIO3 (Alfa Aesar, Tewksbury, MA, USA, 99.5%), Li2CO3 (Alfa Aesar, Tewksbury, MA, USA, 99%), and HNO3 (BDH, Radnor, OH, USA, 67%) were used as starting materials.
Synthesis of β-Ni(IO3)2. Polycrystalline β-Ni(IO3)2 was obtained by heating a mixture of β-Ni(IO3)2 and Ni(IO3)2.2H2O at 300 °C for 8 h (Figure 1). For β-Ni(IO3)2/Ni(IO3)2.2H2O mixture, NiCl2 (2.5 mmol) was dissolved in HNO3 (1 M, 25 mL), an aqueous solution of HIO3 (5 mmol, 10 mL) was added, and the solution was stirred at 80 °C for 1 h. A green solution was obtained and allowed to evaporate completely in a fume hood. A yellow-brown solid, subsequently determined to be β-Ni(IO3)2, was obtained after 4 days (Yield, 68%).
β-Ni(IO3)2 single crystals were grown by hydrothermal reaction. Li2CO3 (1 mmol), NiCl2 (1 mmol), and H2O (4 mL) were placed in a 23 mL Teflon-lined autoclave. The autoclave was heated at 200 °C for 96 h and cooled slowly to 25 °C at a rate of 5 °C/h. β-Ni(IO3)2 yellowish crystals of were isolated by filtration and washed with deionized water.
Synthesis of Zn(IO3)2. ZnCl2 (2.5 mmol) was dissolved in HNO3 (1 M, 25 mL). An aqueous solution of HIO3 (5 mmol, 10 mL) was added, and the mixture was stirred at 80 °C for 1 h to give a colorless solution. Zn(IO3)2 white solid precipitated from the solution after 3 days and was collected by filtration and dried in air (yield of Zn(IO3)2, 65%; based on Zn).
Single Crystal X-ray Diffraction. Single crystal diffraction experiments were performed on β-Ni(IO3)2 using a Bruker D8 Venture diffractometer with Mo Kα radiation (λ = 0.71073 Å) and a Photon 100 detector at T = 300 K. Data processing (SAINT) and scaling (SADABS) were performed using the Apex3 software system. The structure was solved by intrinsic phasing (SHELXT) and refined by full matrix least-squares techniques on F2 (SHELXL) using the SHELXTL software suite. All atoms were refined anisotropically.
Powder X-ray diffraction. Powder X-ray diffraction (PXRD) measurements on polycrystalline β-Ni(IO3)2 and β-Ni(IO3)2/Ni(IO3)2.2H2O mixture were performed using the Rigaku Ultima IV diffractometer equipped with Cu Kα radiation (λ = 1.5406 Å). Data were collected in the 2θ range of 5–90° at 0.2°/min scan rate. Rietveld refinement of XRD pattern was performed using TOPAS Academic V6. Vesta software was used for crystal structure visualization [23].
Synchrotron X-ray Diffraction. Synchrotron XRD patterns of β-Ni(IO3)2/Ni(IO3)2.2H2O mixture were collected using the 11-BM beamline at Advanced Photon Source, Argonne National Laboratory. Data were collected at T = 295 K and λ = 0.45789 Å.
Thermal analysis. A TA SDT Q600 Instrument was used in the thermogravimetry (TG) and differential scanning calorimetry (DSC) measurements. Approximately 10 mg of the solid was isolated from the synthesis, and the β-Ni(IO3)2/Ni(IO3)2.2H2O mixture was placed in an alumina crucible and heated at a rate of 20 °C/min from room temperature to 1000 °C under flowing nitrogen (flow rate: 100 mL/min).
Infrared spectroscopy. The attenuated total reflection Fourier transform infrared (ATR-FTIR) spectrum for β-Ni(IO3)2 was collected using a Shimadzu IR Affinity-1S in 400 to 4000 cm−1 frequency range.
UV-Vis spectroscopy. Optical reflectance was measured on β-Ni(IO3)2 bulk powder using Agilent Cary UV–Vis (NIR) 7000 Universal Measurement Spectrophotometer from 2500 nm to 350 nm. A mixture of approximately 20 mg of β-Ni(IO3)2 and 100 mg of BaSO4 was pelletized and used for the measurement.
Magnetization and specific heat. Magnetization measurements on β-Ni(IO3)2 powder were performed with the vibrating sample magnetometer (VSM) option of a Quantum Design Physical Properties Measurement System (PPMS). Data were collected under the applied magnetic fields of μ0H = 0.1 T and 3 T from T = 2 K–340 K. Magnetic susceptibility was approximated as magnetization divided by the applied magnetic field: χ ≈ M/H. Heat capacity was measured using the PPMS, employing the semiadiabatic pulse technique from T = 2 K–300 K.

3. Results and Discussion

Polycrystalline anhydrous β-Ni(IO3)2 has a brownish color, which is distinct from the green color of hydrated Ni(IO3)2.2H2O, while β-Ni(IO3)2 single crystals have a yellow color. The β-Ni(IO3)2:Ni(IO3)2.2H2O ratio of the precursor mixture was determined to be 71%:29% by Rietveld refinements of powder XRD data (Figure S1). Pure β-Ni(IO3)2 powder was obtained by heating β-Ni(IO3)2/Ni(IO3)2.2H2O mixture at T = 300 °C. The annealing temperature was determined from the thermogravimetry (TG) and differential scanning calorimetry (DSC) experiment (Figure 1a). In TG/DSC analysis, the mass reduction of 2.8% at T ≈ 60–200 °C corresponds to the loss of ~3/5H2O. β-Ni(IO3)2 is thermodynamically stable at T = 220–350 °C, suggesting that T = 300 °C is an appropriate reaction temperature for the synthesis. The decomposition of β-Ni(IO3)2 starts at T = 523 °C, accompanied by a strong endothermic transition in the DSC curve. The mass reduction is attributed to the loss of I2 and 2.5O2 (experimental mass loss = 79.4%; calculated mass loss = 79.6%). The polymorphic behavior of Ni(IO3)2 was previously studied by Raman and FTIR spectroscopy [24]. Based on the spectroscopic evidence, β-Ni(IO3)2 can be converted to α-Ni(IO3)2 or Ni(IO3)2.2H2O, depending on temperature, time, and atmospheric condition. We observed the conversion of ~23% of β-Ni(IO3)2 to Ni(IO3)2.2H2O over the course of approximately 6 months. This transition was confirmed by the synchrotron X-ray diffraction experiment (Figure S2).

3.1. Crystal Structure

To confirm the reported structure of β-Ni(IO3)2 [22] and evaluate its phase purity, we performed single-crystal and powder X-ray diffraction experiments. Details of the crystal structure of β-Ni(IO3)2 derived from single crystal X-ray diffraction are summarized in Table 1. The room-temperature powder XRD pattern of β-Ni(IO3)2 is in excellent agreement with the structure obtained from single crystal X-ray diffraction (Figure 2).
β-Ni(IO3)2 crystallizes in the NCS polar monoclinic structure with space group P21. The crystal structure of β-Ni(IO3)2 can be described as a 3D network of corner-sharing NiO6 octahedra and (IO3)− trigonal pyramids. The unit cell of this material comprises two nonequivalent Ni2+ positions, and each Ni2+ cation is bonded to six oxygen in a slightly distorted octahedra, with Ni–O bond lengths ranging from 2.03(3) Å to 2.16(4) Å. Each I5+ in (IO3)− unit is bonded to three oxygen atoms in a trigonal pyramidal geometry, induced by the stereo-active lone-pair electrons of the I5+ cation (s2) [12,13]. The I–O bond lengths range from 1.76(3) Å–1.85(4) Å. The subtle distortion of NiO6 octahedra is likely induced by the packing effect of the (IO3)− asymmetric building units [7,12,16].
The polar symmetry of β-Ni(IO3)2 results largely from the alignment and addition of the (IO3)− local dipole along the b axis (Figure 2a) [12,13]. FTIR spectra of β-Ni(IO3)2 show four absorption bands corresponding to four fundamental I–O vibrations expected for the (IO3)− group in C3v symmetry Γvib = 2A1 + 2E (Figure 1b). The combined effect of the broken inversion symmetry, macroscopic polarization, stereo-active lone-pair electrons, and triangular sub-lattice of the Ni2+ cations can facilitate competing magnetic exchange interactions in β-Ni(IO3)2 [25,26,27].
Ni(IO3)2.2H2O crystallizes in the centrosymmetric orthorhombic lattice with Pbca space group, and the crystal structure comprises a 2D network of corner-sharing trans-NiO4(H2O)2 octahedra and (IO3)− trigonal pyramids [28]. Unlike in β-Ni(IO3)2, the (IO3)− trigonal pyramids in Ni(IO3)2.2H2O are arranged in opposite directions along the b axis, giving rise to the centrosymmetric structure with zero polarization.

3.2. UV–Vis Spectra

To study the electronic transitions and estimate the optical bandgap of this material, we performed UV–Vis reflectance measurement on β-Ni(IO3)2 powder. Figure 3 shows features of three characteristic bands associated with d → d electronic transitions of a d8 metal cation in octahedral geometry. Energy states for a d8 ion in Oh symmetry is presented in Figure 4. The bands at 0.85, 1.6, and 1.8 eV are ascribed to 3T2g ← 3A2g, 3T1g(F) ← 3A2g and 3T1g(P) ← 3A2g electronic transitions, respectively. The optical bandgap was estimated from the linear region of the Tauc plot of [F(R) × hν] versus hν to be 2.3(1) eV (Figure 3) [29]. This is consistent with the brown-yellow color (2.1–2.3 eV) of the compound.

3.3. Magnetization

To evaluate the magnetic properties of β-Ni(IO3)2, we performed temperature-dependent magnetization measurement from T = 2 K–300 K at different magnetic fields μ0H = 0.1 T and 3 T (Figure 5). High density data of dc magnetization were collected using the VSM option of PPMS to enable accurate estimation of magnetic transition temperature and phase change. β-Ni(IO3)2 exhibits field-dependent magnetic behavior. At low magnetic field μ0H = 0.1 T, β-Ni(IO3)2 undergoes a phase transition at T = 3 K, while at high magnetic field μ0H = 3 T, no magnetic phase transition was observed. Magnetic susceptibility curve above the magnetic phase transition was fit to the Curie–Weiss equation (Equation (1)):
χ ( T ) = C T − θ C W + χ 0 ,
where C is the Curie constant, θCW is the Curie–Weiss temperature, and χ0 is the temperature-independent contribution to the susceptibility, which includes the small diamagnetic signals of the electron core and the sample holder [30].
The effective magnetic moment µeff per Ni2+ cation was estimated using the relation (Equation (2))
µ eff = ( 3 k B N A ) C ,
where NA is the Avogadro number, and kB is the Boltzmann constant. The obtained effective magnetic moment of β-Ni(IO3)2 at both magnetic fields is 3.2(1) µB, which is slightly higher than the ideal spin-only magnetic moment g(S(S+1))1/2 = 2.83 μB expected for a free spin S = 1. This result is consistent with the S = 1 integer spin state with some orbital magnetic moment. Unlike the pseudo 1D Haldane SrNi2V2O8 [21], the χ(T) plots of this material do not show a typical signature of low dimensional magnetic systems (a broad hump over a wide temperature range); these curves nevertheless exhibit a rather flat feature at 100 K < T < 350 K. This suggests that the magnetic exchange interactions of β-Ni(IO3)2 are not 1D but in higher dimensions of spin communication network. This observation is supported by the proposed 3D orbital overlap of β-Ni(IO3)2 (Figure 2c), which pertains to its electronic dimensionality and thus its magnetic interactions. Neutron diffraction experiments would provide additional insights into these magnetic exchange couplings.
An inverse susceptibility vs. temperature plot highlights the Curie–Weiss character of the magnetic susceptibility of β-Ni(IO3)2 (Figure 5a,b). The Curie–Weiss temperature θCW of β-Ni(IO3)2 was extracted from the intercept of the linear fit to be −2.1 K and −3.7 K at μ0H = 0.1 T and 3 T, respectively. The negative values of the Curie–Weiss temperature signify antiferromagnetic (AFM) exchange interaction [31], and the small values can indicate either weak AFM coupling or competing exchange interactions. The zero-field-cooled (ZFC) and field-cooled (FC) magnetic susceptibilities as a function of temperature measured at applied magnetic fields μ0H = 0.1 T and 3 T are presented in Figure 5c. ZFC and FC susceptibilities show a bifurcation below the transition temperature and a downturn at ~2.5 K, demonstrating the possibility of competing AFM-FM interactions at low magnetic field [31,32].
The field-dependent magnetic properties of β-Ni(IO3)2 can be further illustrated in the plot of first-derivative of magnetization as a function of temperature dM/dT vs. T at different fields (Figure 5d). An apparent peak is observed at T = 3 K and μ0H = 0.1 T, indicating magnetic phase transition from a paramagnetic state to a magnetically ordered state. At μ0H = 3 T, no phase magnetic phase transition is observed.
To gain more insight into the nature of the magnetic phase transition, we measured the evolution of magnetization as a function of magnetic field at T = 2 K (Figure 6). The nonlinear character of the M(H) curve cannot be simply described. In Figure 6a, Brillouin function (blue) describes magnetization of non-interacting paramagnetic spins, and the M(H) data of β-Ni(IO3)2 are shown in μB for comparison. The M(H) curve should saturate at around 2(g*J), but instead, it crosses the 2.0 limit and reaches a higher saturation moment at a higher field, indicating orbital contribution to the magnetic moment. This is consistent with the results extracted from the Curie–Weiss analysis illustrated above. In addition, the deviation from the Brillouin function curvature likely suggests some AFM interactions present in the system. A critical field of ~3 T is observed in the dM/dH curve as a function of magnetic field (Figure 6b). dM/dH declines and approaches zero at high magnetic fields, suggesting either saturation of magnetization or formation of a singlet state. Nevertheless, additional studies are needed to provide better understanding of the magnetic ground state of the material.

3.4. Heat Capacity

To investigate the thermodynamic properties of the ground state of this S = 1 integer spin polar magnet, we performed a zero-field specific heat capacity measurement over a temperature range of 2 K ≤ T ≤ 300 K (Figure 7).
An anomaly is observed at T ≈ 2.7 K in the Cp/T vs. T plot, which is approximately the temperature of the magnetic phase transition in β-Ni(IO3)2. The entropy recovered ∆S from this transition can be estimated from Equation (3):
Δ S = ∫ 0 T C v T d T ,
where Cv is the heat capacity at constant volume, which is approximated as Cp—heat capacity at constant pressure—for solid at low temperatures, and T is the temperature. Phonon contribution to specific heat entropy can be accurately estimated using appropriate nonmagnetic isostructural material. The heat capacity of nonmagnetic isostructural Zn(IO3)2 was used to subtract the phonon contribution. The entropy recovered from the specific heat data at 2 K ≤ T ≤ 300 K was estimated to be 3.3(1) J mol f.u.−1 K−1, which is ~36% of the expected value of Rln(3) for S = 1 (Figure S3). The entropy change accompanying the magnetic phase transition in β-Ni(IO3)2 was underestimated because the transition was not complete down to T = 2 K. Further specific heat measurements at T < 2 K in the presence of applied magnetic fields will enable a more complete elucidation of the thermodynamic properties of the magnetic ground state of β-Ni(IO3)2.

4. Conclusions

Studies in polar magnetic materials possessing asymmetric exchange interactions, which are relevant to possible emergence of topological spin physics, have been in a rather confined space of half-integer spins attributed to the scarcity of integer spin systems with broken spatial inversion symmetry. β-Ni(IO3)2 was selected for the focus of this work due to its combined integer spin S = 1 and NCS polar lattice components. The synthetic approach for both single crystal and polycrystalline form of β-Ni(IO3)2 developed in this study provides facile chemistry for preparing new polar magnetic compounds. The magnetic behavior of β-Ni(IO3)2 is field-dependent, i.e., the material undergoes a phase transition at T = 3 K at low magnetic field, but the transition is suppressed at higher fields. The phase transition is magnetically driven, as evident by an anomaly observed at approximately the same temperature in the specific heat data. Taken together, the results provide us with an avenue for expanding the phase space of polar magnets to integer spins. Additional ac magnetization, specific heat measurements, and neutron diffraction could help further demonstrate the magnetic ground state at zero filed and magnetic states at finite fields, as well as determine whether integer spins in a polar crystal lattice have any impact on tuning asymmetric exchange interactions and thus potential vortex-like spin textures.

Supplementary Materials

The following are available online, Figure S1: Rietveld fit of powder XRD pattern of the bulk polycrystalline β-Ni(IO3)2 precursor-β-Ni(IO3)2/Ni(IO3)2.2H2O mixture. Figure S2: Rietveld fit of synchrotron XRD pattern of the bulk polycrystalline β-Ni(IO3)2 after 6 months in air. Figure S3: (a) Molar heat capacity over temperature (Cp/T) vs. temperature for β-Ni(IO3)2, (b) Magnetic entropy change from 2 K to 300 K, ∆Smag (2 K ≤ T ≤ 300 K) = 3.3(1) J mol−1 K−1~36% of expected value for S = 1 spins (Rln3). Table S1: Crystal structure information and refinement parameters for β-Ni(IO3)2 obtained by Rietveld refinement of powder X-ray diffraction patterns. Table S2: Atomic positions for β-Ni(IO3)2 obtained from the single crystal XRD. Table S3: Bond lengths and bond angles of β-Ni(IO3)2. Table S4: Calculated bond valence sum (Vi) of β-Ni(IO3)2.

Author Contributions

Conceptualization, E.E.O., M.J.W. and T.T.T.; methodology, E.E.O., M.J.W. and T.T.T.; software, E.E.O., M.J.W. and T.T.T.; validation, E.E.O., M.J.W. and T.T.T.; formal analysis, E.E.O., M.J.W. and T.T.T.; investigation, E.E.O., M.J.W. and T.T.T.; resources, E.E.O., M.J.W. and T.T.T.; data curation, E.E.O., M.J.W. and T.T.T.; writing—original draft preparation, E.E.O., M.J.W. and T.T.T.; writing—review and editing, E.E.O., M.J.W. and T.T.T.; visualization, E.E.O., M.J.W. and T.T.T.; supervision, T.T.T.; project administration, M.J.W. and T.T.T.; funding acquisition, M.J.W. and T.T.T. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Clemson University. Research at Gdansk University of Technology was supported by the National Science Center (Poland) under SONATA-15 grant (no. 2019/35/D/ST5/03769).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data supporting reported results can be sourced directly from the authors.

Acknowledgments

This work was supported by Clemson University, College of Science, Department of Chemistry. E.E.O. acknowledges the COSSAB-GIAR Grant from College of Science, Clemson University. T.T.T. thanks the 2021 Support for Early Exploration and Development (SEED) Grant. Research at Gdansk University of Technology was supported by the National Science Center (Poland) under SONATA-15 grant (no. 2019/35/D/ST5/03769). M.J.W. gratefully acknowledges the Ministry of Science and Higher Education scholarship for young scientists. Use of the Advanced Photon Source at Argonne National Laboratory was supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract No. DE-AC02-06CH11357.

Conflicts of Interest

The authors declare no conflict of interest.

Sample Availability

Samples of the compounds β-Ni(IO3)2 and Zn(IO3)2 are available from the authors.

References

  1. Spaldin, N.A.; Ramesh, R. Advances in magnetoelectric multiferroics. Nat. Mater. 2019, 18, 203–212. [Google Scholar] [CrossRef]
  2. Seki, S.; Yu, X.Z.; Ishiwata, S.; Tokura, Y. Observation of skyrmions in a multiferroic material. Science 2012, 336, 198. [Google Scholar] [CrossRef] [Green Version]
  3. Kanazawa, N.; Seki, S.; Tokura, Y. Noncentrosymmetric magnets hosting magnetic skyrmions. Adv. Mater. 2017, 29, 1603227. [Google Scholar] [CrossRef]
  4. Ruff, E.; Widmann, S.; Lunkenheimer, P.; Tsurkan, V.; Bordacs, S.; Kezsmarki, I.; Loidl, A. Multiferroicity and skyrmions carrying electric polarization in GaV4S8. Sci. Adv. 2015, 1, e1500916. [Google Scholar] [CrossRef] [Green Version]
  5. Araki, Y.; Sato, T.; Fujima, Y.; Abe, N.; Tokunaga, M.; Kimura, S.; Morikawa, D.; Ukleev, V.; Yamasaki, Y.; Tabata, C.; et al. Metamagnetic transitions and magnetoelectric responses in the chiral polar helimagnet Ni2InSbO6. Phys. Rev. B 2020, 102, 054409. [Google Scholar] [CrossRef]
  6. Oyeka, E.E.; Winiarski, M.J.; Sorolla, M., II; Taddei, K.M.; Scheie, A.; Tran, T.T. Spin and orbital effects on asymmetric exchange interaction in polar magnets: M(IO3)2 (M = Cu and Mn). Inorg. Chem. 2021, 60, 16544–16557. [Google Scholar] [CrossRef]
  7. Qian, Z.; Wu, H.; Yu, H.; Hu, Z.; Wang, J.; Wu, Y. Synthesis, structure, and characterization of d0 transition-metal iodate: BaTi(IO3)6·0.5H2O. Inorg. Chem. 2020, 59, 15430–15437. [Google Scholar] [CrossRef]
  8. Luo, M.; Liang, F.; Hao, X.; Lin, D.; Li, B.; Lin, Z.; Ye, N. Rational design of the nonlinear optical response in a tin iodate fluoride Sn(IO3)2F2. Chem. Mater. 2020, 32, 2615–2620. [Google Scholar] [CrossRef]
  9. Nguyen, S.D.; Halasyamani, P.S. Synthesis, structure, and characterization of new Li+-d0-lone-Pair-oxides: Noncentrosymmetric polar Li6(Mo2O5)3(SeO3)6 and Centrosymmetric Li2(MO3)(TeO3) (M = Mo6+ or W6+). Inorg. Chem. 2012, 51, 9529–9538. [Google Scholar] [CrossRef] [PubMed]
  10. Donakowski, M.D.; Gautier, R.; Yeon, J.; Moore, D.T.; Nino, J.C.; Halasyamani, P.S.; Poeppelmeier, K.R. The role of polar, lamdba (Λ)-shaped building units in noncentrosymmetric inorganic structures. J. Am. Chem. Soc. 2012, 134, 7679–7689. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  11. Kim, S.-H.; Yeon, J.; Halasyamani, P.S. Noncentrosymmetric polar oxide material, Pb3SeO5: Synthesis, characterization, electronic structure calculations, and structure-property relationships. Chem. Mater. 2009, 21, 5335–5342. [Google Scholar] [CrossRef]
  12. Nguyen, S.D.; Yeon, J.; Kim, S.-H.; Halasyamani, P.S. BiO(IO3): A new polar iodate that exhibits an aurivillius-type (Bi2O2)2+ layer and a large SHG response. J. Am. Chem. Soc. 2011, 133, 12422–12425. [Google Scholar] [CrossRef] [PubMed]
  13. Chang, H.-Y.; Kim, S.-H.; Halasyamani, P.S.; Ok, K.M. Alignment of lone pairs in a new polar material: Synthesis, characterization, and functional properties of Li2Ti(IO3)6. J. Am. Chem. Soc. 2009, 131, 2426–2427. [Google Scholar] [CrossRef]
  14. Ok, K.M. Toward the rational design of novel noncentrosymmetric materials: Factors influencing the framework structures. Acc. Chem. Res. 2016, 49, 2774–2785. [Google Scholar] [CrossRef] [PubMed]
  15. Chen, J.; Hu, C.-L.; Zhang, X.-H.; Li, B.-X.; Yang, B.-P.; Mao, J.-G. CsVO2F(IO3): An excellent SHG material faturing an unprecedented 3D [VO2F(IO3)]− anionic framework. Angew. Chem. Int. Ed. 2020, 59, 5381–5384. [Google Scholar] [CrossRef]
  16. Oyeka, E.E.; Winiarski, M.J.; Błachowski, A.; Taddei, K.M.; Scheie, A.; Tran, T.T. Potential skyrmion host Fe(IO3)3: Connecting stereoactive lone-pair electron effects to the Dzyaloshinskii-Moriya interaction. Chem. Mater. 2021, 33, 4661–4671. [Google Scholar] [CrossRef]
  17. Kurumaji, T.; Nakajima, T.; Ukleev, V.; Feoktystov, A.; Arima, T.H.; Kakurai, K.; Tokura, Y. Neel-type skyrmion lattice in the tetragonal polar magnet VOSe2O5. Phys. Rev. Lett. 2017, 119, 237201. [Google Scholar] [CrossRef] [Green Version]
  18. Buyers, W.J.L.; Morra, R.M.; Armstrong, R.L.; Hogan, M.J.; Gerlach, P.; Hirakawa, K. Experimental evidence for the Haldane gap in a spin-1 nearly isotropic, antiferromagnetic chain. Phys. Rev. Lett. 1986, 56, 371–374. [Google Scholar] [CrossRef]
  19. Cubitt, T.S.; Perez-Garcia, D.; Wolf, M.M. Undecidability of the spectral gap. Nature 2015, 528, 207–211. [Google Scholar] [CrossRef] [Green Version]
  20. Kelly, Z.A.; Tran, T.T.; McQueen, T.M. Nonpolar-to-polar trimerization transitions in the S = 1 Kagomé magnet Na2Ti3Cl8. Inorg. Chem. 2019, 58, 11941–11948. [Google Scholar] [CrossRef] [PubMed]
  21. Bera, A.K.; Lake, B.; Islam, A.T.M.N.; Klemke, B.; Faulhaber, E.; Law, J.M. Field-induced magnetic ordering and single-ion anisotropy in the quasi-one-dimensional Haldane chain compound SrNi2V2O8: A single-crystal investigation. Phys. Rev. B 2013, 87, 224423. [Google Scholar] [CrossRef] [Green Version]
  22. Phanon, D.; Bentria, B.; Jeanneau, E.; Benbertal, D.; Mosset, A.; Gautier-Luneau, I. Crystal structure of M(IO3)2 metal iodates, twinned by pseudo-merohedry, with MII: MgII, MnII, CoII, NiII and ZnII. Z. Kristallogr. Cryst. Mater. 2006, 221, 635–642. [Google Scholar] [CrossRef]
  23. Momma, K.; Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 2011, 44, 1272–1276. [Google Scholar] [CrossRef]
  24. Pracht, G.; Lange, N.; Lutz, H.D. High-temperature Raman spectroscopic studies on nickel iodates. Thermochim. Acta 1997, 293, 13–24. [Google Scholar] [CrossRef]
  25. Ideue, T.; Kurumaji, T.; Ishiwata, S.; Tokura, Y. Giant thermal Hall effect in multiferroics. Nat. Mater. 2017, 16, 797–802. [Google Scholar] [CrossRef]
  26. Peng, L.; Takagi, R.; Koshibae, W.; Shibata, K.; Nakajima, K.; Arima, T.-h.; Nagaosa, N.; Seki, S.; Yu, X.; Tokura, Y. Controlled transformation of skyrmions and antiskyrmions in a non-centrosymmetric magnet. Nat. Nanotechnol. 2020, 15, 181–186. [Google Scholar] [CrossRef] [PubMed]
  27. Halder, M.; Chacon, A.; Bauer, A.; Simeth, W.; Mühlbauer, S.; Berger, H.; Heinen, L.; Garst, M.; Rosch, A.; Pfleiderer, C. Thermodynamic evidence of a second skyrmion lattice phase and tilted conical phase in Cu2OSeO3. Phys. Rev. B 2018, 98, 144429. [Google Scholar] [CrossRef]
  28. Abrahams, S.C.; Bernstein, J.L.; Elemans, J.B.A.A.; Verschoor, G.C. Paramagnetic Ni(IO3)2·2H2O. Crystal structure of the transition-metal iodates. I. J. Chem. Phys. 1973, 59, 2007–2018. [Google Scholar] [CrossRef]
  29. Makuła, P.; Pacia, M.; Macyk, W. How to correctly determine the band gap energy of modified semiconductor photocatalysts based on UV-Vis spectra. J. Phys. Chem. Lett. 2018, 9, 6814–6817. [Google Scholar] [CrossRef] [Green Version]
  30. Winiarski, M.J.; Tran, T.T.; Chamorro, J.R.; McQueen, T.M. (CsX)Cu5O2(PO4)2 (X = Cl, Br, I): A family of Cu2+ S = 1/2 compounds with capped-Kagome networks composed of OCu4 units. Inorg. Chem. 2019, 58, 4328–4336. [Google Scholar] [CrossRef]
  31. Fritsch, V.; Moreno, N.O.; Thompson, J.D.; Sarrao, J.L.; Bobev, S. Antiferromagnetic order and evolution of magnetic entropy in RE4Zn5Ge6 (RE = Y, Gd-Lu). J. Magn. Magn. Mater. 2005, 299, 87–93. [Google Scholar] [CrossRef]
  32. Fita, I.; Wisniewski, A.; Puzniak, R.; Iwanowski, P.; Markovich, V.; Kolesnik, S.; Dabrowski, B. Competing exchange bias and field-induced ferromagnetism in La-doped BaFeO3. Phys. Rev. B 2017, 95, 134428. [Google Scholar] [CrossRef]
Molecules 26 07210 g001 550
Figure 1. (a) Thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) of β-Ni(IO3)2/Ni(IO3)2.2H2O showing loss of 3/5H2O of crystallization at T ≈ 60–200 °C and a decomposition temperature of 523 °C accompanied by the loss of I2 and 2.5O2. (b) FTIR of β-Ni(IO3)2 showing four absorption bands corresponding to four fundamental I–O vibrations expected for IO3 group in C3v symmetry Γvib = 2A1 + 2E.
Figure 1. (a) Thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) of β-Ni(IO3)2/Ni(IO3)2.2H2O showing loss of 3/5H2O of crystallization at T ≈ 60–200 °C and a decomposition temperature of 523 °C accompanied by the loss of I2 and 2.5O2. (b) FTIR of β-Ni(IO3)2 showing four absorption bands corresponding to four fundamental I–O vibrations expected for IO3 group in C3v symmetry Γvib = 2A1 + 2E.
Molecules 26 07210 g001
Molecules 26 07210 g002 550
Figure 2. (a,b) Crystal structure of β-Ni(IO3)2 consisting of corner-sharing NiO6 octahedra and IO3 trigonal pyramid; the polar symmetry of β-Ni(IO3)2 results from the alignment of (IO3)− local dipole along the b axis. (c) Atomic connectivity and orbital overlap in β-Ni(IO3)2. (d) Rietveld refinements of XRD data of polycrystalline β-Ni(IO3)2.
Figure 2. (a,b) Crystal structure of β-Ni(IO3)2 consisting of corner-sharing NiO6 octahedra and IO3 trigonal pyramid; the polar symmetry of β-Ni(IO3)2 results from the alignment of (IO3)− local dipole along the b axis. (c) Atomic connectivity and orbital overlap in β-Ni(IO3)2. (d) Rietveld refinements of XRD data of polycrystalline β-Ni(IO3)2.
Molecules 26 07210 g002
Molecules 26 07210 g003 550
Figure 3. Tauc plot for β-Ni(IO3)2 showing characteristics of the electronic transitions and estimated optical bandgap of 2.3(1) eV.
Figure 3. Tauc plot for β-Ni(IO3)2 showing characteristics of the electronic transitions and estimated optical bandgap of 2.3(1) eV.
Molecules 26 07210 g003
Molecules 26 07210 g004 550
Figure 4. Energy states for a d8 ion in Oh symmetry based on the ligand field theory.
Figure 4. Energy states for a d8 ion in Oh symmetry based on the ligand field theory.
Molecules 26 07210 g004
Molecules 26 07210 g005 550
Figure 5. (a,b) (Black) magnetic susceptibility of β-Ni(IO3)2 measured from T = 2 K–300 K at (a) μ0H = 0.1 T and (b) μ0H = 3 T. (red) Curie–Weiss fitting of 1/(χ − χ0) against temperature for the paramagnetic phase. (c) Zero-field-cooled (ZFC) and field-cooled (FC) magnetic susceptibilities of β-Ni(IO3)2 as a function of temperature at different magnetic field. (d) First derivative of magnetization with respect to the temperature, dM/dT vs. T for β-Ni(IO3)2.
Figure 5. (a,b) (Black) magnetic susceptibility of β-Ni(IO3)2 measured from T = 2 K–300 K at (a) μ0H = 0.1 T and (b) μ0H = 3 T. (red) Curie–Weiss fitting of 1/(χ − χ0) against temperature for the paramagnetic phase. (c) Zero-field-cooled (ZFC) and field-cooled (FC) magnetic susceptibilities of β-Ni(IO3)2 as a function of temperature at different magnetic field. (d) First derivative of magnetization with respect to the temperature, dM/dT vs. T for β-Ni(IO3)2.
Molecules 26 07210 g005
Molecules 26 07210 g006 550
Figure 6. (a) (red) M(H) data of β-Ni(IO3)2 in μB at T = 2 K, (blue) Brillouin function for J = 1 and T = 2 K. (b) dM/dH curve for β-Ni(IO3)2, showing critical field Hc at ~3 T.
Figure 6. (a) (red) M(H) data of β-Ni(IO3)2 in μB at T = 2 K, (blue) Brillouin function for J = 1 and T = 2 K. (b) dM/dH curve for β-Ni(IO3)2, showing critical field Hc at ~3 T.
Molecules 26 07210 g006
Molecules 26 07210 g007 550
Figure 7. Molar heat capacity over temperature (Cp/T) vs. temperature (T) for β-Ni(IO3)2.
Figure 7. Molar heat capacity over temperature (Cp/T) vs. temperature (T) for β-Ni(IO3)2.
Molecules 26 07210 g007
Table
Table 1. Crystal structure information and refinement parameters for β-Ni(IO3)2 obtained by single crystal X-ray diffraction.
Table 1. Crystal structure information and refinement parameters for β-Ni(IO3)2 obtained by single crystal X-ray diffraction.
Refinement ParameterCrystallographic Data
Chemical formulaNi(IO3)2
ColorYellow
ShapeBlock
Size (mm × mm × mm)0.02 × 0.02 × 0.02
Formula weight (g/mol)408.51
Temperature (K)300
X-ray radiationMo Kα
Wavelength (λ, Å)0.71073
Crystal systemMonoclinic
Space groupP21
Z4
a (Å)10.8067(4)
b (Å)5.1190(2)
c (Å)10.8151(4)
α = γ (°)90
β (°)119.7950(10)
V (Å3)519.20(3)
ρcalc (g/cm3)5.226
No. of reflections collected7093
μ (mm−1)15.582
2θ (°)55
GOF1.141
Flack0.07(5)
R(F) a0.051
Rw(Fo) b0.1046
a R ( F ) = ∑ || F o | − | F o 2 || / ∑ | F o | . b R w ( F o 2 ) = [ ∑ w ( F o 2 − F o 2 ) 2 / ∑ w ( F o 2 ) 2 ] 1 / 2 .
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Oyeka, E.E.; Winiarski, M.J.; Tran, T.T. Study of Integer Spin S = 1 in the Polar Magnet β-Ni(IO3)2. Molecules 2021, 26, 7210. https://doi.org/10.3390/molecules26237210

AMA Style

Oyeka EE, Winiarski MJ, Tran TT. Study of Integer Spin S = 1 in the Polar Magnet β-Ni(IO3)2. Molecules. 2021; 26(23):7210. https://doi.org/10.3390/molecules26237210

Chicago/Turabian Style

Oyeka, Ebube E., Michał J. Winiarski, and Thao T. Tran. 2021. "Study of Integer Spin S = 1 in the Polar Magnet β-Ni(IO3)2" Molecules 26, no. 23: 7210. https://doi.org/10.3390/molecules26237210

APA Style

Oyeka, E. E., Winiarski, M. J., & Tran, T. T. (2021). Study of Integer Spin S = 1 in the Polar Magnet β-Ni(IO3)2. Molecules, 26(23), 7210. https://doi.org/10.3390/molecules26237210