Volume 14
Issue 17
10.3390/ma14174895
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Agar Acts as Cathode Microskin to Extend the Cycling Life of Zn//α-MnO2 Batteries

by
Linqing Zuo
1,
Haodong Sun
1,
Xinhai Yuan
1,
Juan Wen
1,
Xi Chen
1,
Shiyu Zhou
1,
Yuping Wu
1,* and
Teunis van Ree
2
1
China State Key Laboratory of Materials-Oriented Chemical Engineering, Institute of Advanced Materials (IAM), School of Energy Science and Engineering, Nanjing Tech University, Nanjing 210009, China
2
Department of Chemistry, University of Venda, Thohoyandou 0950, South Africa
*
Author to whom correspondence should be addressed.
Materials 2021, 14(17), 4895; https://doi.org/10.3390/ma14174895
Submission received: 15 July 2021 / Revised: 23 August 2021 / Accepted: 23 August 2021 / Published: 27 August 2021
Browse Figures
Versions Notes

Abstract

:
The Zn/MnO2 battery is a promising energy storage system, owing to its high energy density and low cost, but due to the dissolution of the cathode material, its cycle life is limited, which hinders its further development. Therefore, we introduced agar as a microskin for a MnO2 electrode to improve its cycle life and optimize other electrochemical properties. The results showed that the agar-coating layer improved the wettability of the electrode material, thereby promoting the diffusion rate of Zn2+ and reducing the interface impedance of the MnO2 electrode material. Therefore, the Zn/MnO2 battery exhibited outstanding rate performance. In addition, the agar-coating layer promoted the reversibility of the MnO2/Mn2+ reaction and acted as a colloidal physical barrier to prevent the dissolution of Mn2+, so that the Zn/MnO2 battery had a high specific capacity and exhibited excellent cycle stability.

1. Introduction

In recent years, the lithium-ion battery has permeated our lives and production and is used in both small electronic appliances and large mechanical equipment [1,2]. However, some issues such as long charging time and flammability of electrolyte solvents restrict its wide application, especially in large-scale energy storage systems (ESSs) that require high safety and reliability [3,4,5,6]. Therefore, some researchers shifted their attention to research on aqueous rechargeable batteries [7,8,9,10,11,12]. Among various aqueous battery systems, aqueous Zn-ion battery (ZIB) is very widely studied, owing to its high theoretical specific capacity (820 mAh g−1), low redox potential (−0.76 V vs. Standard hydrogen electrode, SHE), and low cost of Zn anodes [13,14]. Although it has these attractive merits, improving its cycle life is still a problem that needs to be solved urgently. As an important part of the ZIB, the cathode material is one of the keys to solving its cycling stability. Until now, candidate cathodes for ZIBs have been based mainly on vanadium-based materials, manganese-based materials, Prussian blue analogues, and other metal oxides or metal chalcogenides [13]. Among them, manganese-based materials, especially tunnel-type α-MnO2, are considered promising materials due to their low synthesis cost and high energy density [15]. However, MnO2 suffers from serious capacity decline in aqueous electrolytes, owing to the dissolution of active materials and structural transformation caused by the disproportionation reaction of Mn3+. The addition of MnSO4 to electrolytes can inhibit this side reaction to a certain extent, because additional Mn2+ influences the balance between Mn2+ dissolution and reoxidation [16]. To further improve the cycling performance of MnO2, a common strategy is surface coating by conductive carbon materials or polymer materials, which cannot only enhance the electrical conductivity of MnO2 and ease volume changes, but also prevent Mn dissolution [17]. However, the improvement of cycle life is limited due to the poor reversibility of the MnO2/Mn2+ redox reaction [18]. Recently, Chen’s research group used collagen hydrolysate (CH) as an electrode microskin (EMS) to adsorb/confine dissolved Mn2+ ions, resulting in the reversibility of the redox reaction of MnO2/Mn2+ during the charge and discharge processes, thereby improving cycle performance [19]. This is a simple and effective method to improve the cycle stability of the Zn/MnO2 battery, which is worthy of further promotion and in-depth research.
Agar is a polysaccharide extracted from seaweed and is widely used in the food industry, pharmaceutical industry, chemical industry, bioengineering, and many other fields. Agar used in food can significantly change the quality of food and improve the quality of food [20]. It can be used as a thickener, a coagulant, a suspending agent, an emulsifier, a preservative, and a stabilizer. In addition, agar is also used in the field of electrochemistry as an electrolyte additive to alleviate metal corrosion, with excellent results [21,22,23,24,25]. Due to the above properties and advantages, agar may be promising for use as a cathode microskin for the Zn/MnO2 battery.
Here, we report the use of agar as the EMS of an α-MnO2 electrode to improve the electrochemical performance of a Zn//α-MnO2 battery. The influences of different thicknesses of an agar coating layer on the wettability and resistance of the α-MnO2 electrode and the rate performance, specific capacity, and cycling performance of the Zn//α-MnO2 battery were explored.

2. Experimental Section

2.1. Material Synthesis

2.1.1. Preparation of α-MnO2

α-MnO2 was prepared by a hydrothermal method. Typically, 1 g KMnO4 (Analytical Reagent, AR, Sinopharm Chemical Reagent Co. Ltd., Shanghai, China) and 0.4 g MnSO4 (AR, Sinopharm Chemical Reagent Co. Ltd., Shanghai, China) were dissolved in 50 mL and 22 mL deionized water, respectively. Then, the two solutions were mixed, and the resulting mixture was stirred for 10 min at room temperature to form a clear solution. Afterwards, the solution was transferred to a 100 mL autoclave (Nanjing Wanqing Chemical Glass Ware & Instrument Co. Ltd., Nanjing, China) and reacted at 160 °C for 12 h. After cooling to room temperature, the brownish black product was collected by vacuum filtration and washed with deionized water followed by absolute ethanol (≥99.7%, Wuxi Yasheng Chemical Co. Ltd., Wuxi, China). The final product was dried in an oven (DGG-9240A, Shanghai Senxin Experimental Instrument Co. Ltd., Shanghai, China) at 80 °C for 12 h before use.

2.1.2. Modification of α-MnO2 Electrode by Agar Coating

To prepare the α-MnO2 electrode, α-MnO2, acetylene black (AR, Aladdin, Shanghai, China), and poly(vinylidene fluoride) (PVDF) (AR, Aladdin, Shanghai, China) were mixed with a mass ratio of 7:2:1 in an appropriate amount of in N-methyl-2-pyrrolidinone (AR, Macklin Biochemical Co. Ltd. Shanghai, China), and the mixture was stirred for 3 h. Then, the stirred slurry was coated on a stainless-steel foil (thickness: 0.01 mm, Dongguan Pingjie Metal Material Co., Ltd. Dongguan, China) and dried in a vacuum drying oven (DZG-6050, Shanghai Senxin Experimental Instrument Co. Ltd., Shanghai, China) at 80 °C for 12 h. Finally, the foil was cut into a disc with a diameter of 5 mm for use. The active substance loaded per disc was about 2 mg.
Agar solutions with agar mass fractions of 1% and 2.5% were obtained by mixing agar (AR, Macklin Biochemical Co. Ltd. Shanghai, China) with ultra-pure water at mass ratios of 1:99 and 2.5:97.5, respectively, and the mixtures were heated at 90 °C for 1 h.
Ten microliters of each agar solution were dripped onto the cut α-MnO2 electrodes, which were dried on a hot plate at 60 °C to prepare agar-modified α-MnO2 electrodes. The electrodes coated with 1% and 2.5% agar solutions were denoted as MnO2-1 and MnO2-2, respectively.

2.2. Material Characterization

The structures of the α-MnO2 were determined by X-ray diffractometer (XRD, Rigaku, Smartlab TM, Tokyo, Japan) (Cu Kα; λ = 1.5406 Å). The morphologies of the α-MnO2 and different thicknesses of the agar coating layers were observed using scanning electron microscopy (SEM; JEOL Ltd., JSM-7800F, Tokyo, Japan). For more detailed material analyses, transmission electron microscopy (TEM; JEOL Ltd., JEM-2100F, Tokyo, Japan) was used, Fourier Transform Infrared (FTIR) analyses were performed on a Vertex 70 FTIR spectrometer (Bruker Optik GmbH, Leipzig, Germany).

2.3. Electrochemical Measurements

Both cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) were measured using a Chenhua 660 E electrochemical workstation (CH Instruments Inc, Shanghai, China). The rate and cycling performances were tested on a LAND 2001A battery test system (Wuhan LAND Electronic Co. Ltd., Wuhan, China). A 0.8 mm commercial zinc foil (Kunshan Yizhongtian New Material Co. Ltd., Suzhou, China), a 2 M ZnSO4 + 0.5 M MnSO4 solution, and a glass fiber membrane (Whatman GF/A, Maidstone, England) were used as an anode, an electrolyte, and a diaphragm, respectively. A button battery-packaging machine (Shenzhen Kejing Star Technology Co. Ltd. Shenzhen, China) was used to package CR2025 button batteries. After standing for 1 h, the electrochemical test was performed.

3. Results and Discussion

3.1. Characterization of the Physical Properties of the Prepared α-MnO2

The physical properties of the prepared MnO2 are illustrated in Figure 1. The MnO2 nanorods, with a length of 2–3 μm and a thickness of 100–150 nm, can be clearly observed (Figure 1a–c). The TEM is shown in Figure 1d. A lattice spacing of 0.308 nm was found to match well with the (310) crystal planes of α-MnO2. The XRD patterns conformed to a pure α-MnO2 phase (JCPDS No. 44-0141) [26].

3.2. Characterization of the Agar-Modified Cathodes

The FTIR spectrum of agar is shown in Figure 2a. The absorption band at 3429.89 cm−1 corresponds to the stretching vibration of the hydroxyl groups (O–H) in agar, which participate in the formation of intermolecular and intramolecular hydrogen bonds; the weak absorption band at 1623.49 cm−1 is allocated to the C=O stretching vibration; the band around 1405.69 cm−1 can be attributed to the sulfate ester group in agar; the absorption band at 1053.38 cm−1 corresponds to several C–O–H bending modes; the absorption band at 963.7 cm−1 is attributed to the C–O–C bending mode in 3,6-anhydrogalactose [22]. The FTIR spectra of ager coated MnO2 electrode is shown in Figure S1, which is consistent with that of pure agar. Figure 2b–d shows the top view of the SEM images of the α-MnO2 electrode and electrodes coated with agar. The surface of the α-MnO2 electrode was rough, while the agar-coated electrodes had smooth skins. The thicknesses of the microskins on the electrode surfaces coated with agar solutions of different concentrations were 4.94 μm and 14.1 μm for MnO2-1 and MnO2-2, respectively.
It has been shown that electrode wettability is closely related to the capacity and cycle life of the battery. Generally speaking, improving the wettability of electrode materials can shorten the wetting time, make full use of the electrode capacity and provide better electrochemical performance [27,28]. The surface hydrophilicity tests results of the α-MnO2 electrode and electrodes coated with agar are shown in Figure 3. It can be seen that the contact angle was reduced from 99° to 52° with increasing amounts of agar on the cathode. This means that agar coating may increase the diffusion rate of Zn2+ on the MnO2 electrode surface, reduce the interface impedance and improve the rate performance.

3.3. Electrochemical Performance of Zn//α-MnO2 Batteries

Zn//α-MnO2 batteries were assembled using a 2 M ZnSO4 + 0.5 M MnSO4 aqueous solution as an electrolyte. In order to explore the effect of agar as a cathode microskin on the electrochemical performance of Zn//α-MnO2 batteries, its EIS spectrum was first measured. As shown in Figure 4a, the Zn/MnO2-1 battery showed the lowest charge transfer resistance in the high-frequency area, which may be attributed to the decrease of the cross-sectional impedance of the electrode due to the improvement of its wettability [29,30]. The charge transfer resistance of the Zn/MnO2-2 battery came second, because although the cathode had the best wettability, the agar microskin coating was thicker, which increased the interface resistance. The slope of the low-frequency parts was calculated, as shown in Figure S2. The slopes for the Zn/MnO2 battery, Zn/MnO2-1 battery, and Zn/MnO2-2 battery are 1.01, 2.78, and 1.54, respectively. The slope of the Zn/MnO2-1 battery was the highest, indicating that the diffusion rate of Zn2+ was the highest in the MnO2-1 electrode. In Figure 4b, the CV curves of the three batteries at a scan rate of 0.3 mV s−1 over the potential range of 0.1–1.95 V (vs. Zn2+/Zn) are shown. The CV curves of these three batteries had similar shapes, with two reduction peaks and two oxidation peaks, which can be attributed to the redox processes of Mn4+/Mn3+ caused by the intercalation of Zn2+ into the MnO2 host and the extraction of Zn2+ from the MnO2 host, respectively. Compared with the Zn/MnO2 battery and the Zn/MnO2-2 battery, the Zn/MnO2-1 battery had a higher peak current density, indicating that it had the highest electrochemical activity and capacity [31]. In addition, the Zn/MnO2-1 battery had the lowest polarization, meaning that it had the lowest interface impedance, which is consistent with the EIS test results.
The CV curves of the Zn/MnO2-1 battery at various scan rates from 0.3 to 1 mV s−1 are shown in Figure 5a. With the increasing scan rate, it can be seen clearly that the shapes of the CV curves are consistent, but the peaks in the CV gradually grow wider. According to the equation: log(i) = log(a) + blog(v), where the b values were calculated as 0.43 (R1), 0.67 (R2), 0.43 (O1), and 0.56 (O2) by fitting the linear relationship between log(i) and log(v) (Figure 5b). This clearly shows that the ion diffusion process and surface capacitive effects both contributed to the electrochemical kinetics of the MnO2-1. Figure 5c records the rate performances of the Zn/MnO2 battery, the Zn/MnO2-1 battery, and the Zn/MnO2-2 battery at various current densities. The results showed that the rate performance of the Zn/MnO2-1 battery was the best, followed by that of the Zn/MnO2-2 battery, while the Zn/MnO2 battery performed the worst. The Zn/MnO2-1 battery delivered a capacity of 384.7, 232.8, 179.3, and 133.3 mAh g−1 at current densities of 0.25, 0.5, 1.0, and 2 A g−1, respectively. The corresponding charge and discharge curves are shown in Figure 5d. It can be seen that when the current density was 0.25 A g−1, there were two plateaus on the charge–discharge curve, which are consistent with the CV curve. It is worth noting that as the current density increased, the second plateau gradually disappeared. This may be due to the slow diffusion of Zn2+ at high current density; its capacity contribution mainly comes from H+ insertion/extraction [32]. The specific capacity of the Zn/MnO2 battery at the corresponding current density was much lower than that of the Zn/MnO2-1 battery (Figure S3), which indicated that the agar microskin improved the reversibility of the MnO2/Mn2+ reaction [19]. The specific capacity of the Zn/MnO2-2 battery was higher than that of the Zn/MnO2 battery, but lower than that of the Zn/MnO2-2 battery. This is mainly because the agar microskin of the MnO2-2 electrode was thicker than that of the MnO2-1 electrode, which hindered the transmission speed of Zn2+ to a certain extent.
The cycling performance was studied by continually charging and discharging at 0.5 A g−1. Figure 6a compares the cycling performance of the Zn//α-MnO2 batteries with that of the Zn/MnO2-1 battery exhibiting the best cycling performance with a capacity retention of 95.4% after 500 cycles and with the highest specific capacity, which was substantially higher than the values for most Zn/MnO2 batteries reported to date (Table 1). This superior performance can be attributed mostly to the agar coating. During the charge and discharge processes, agar acted as a colloidal physical barrier to inhibit the dissolution of Mn2+, hence improving the cycling performance of the Zn//α-MnO2 battery. Moreover, due to the improvement of the reversibility of the MnO2/Mn2+ reaction by agar coating, the specific capacities of the Zn/MnO2-1 battery and the Zn/MnO2-2 battery were higher than that of the Zn/MnO2 battery. However, due to the thick coating layer of MnO2-2, the migration rate of Zn2+ in this battery was hindered to a certain extent, and the interface impedance was increased, so that the specific capacity of the Zn/MnO2-2 battery was lower than that of the Zn/MnO2-1 battery. It should be noted that both the Zn/MnO2-1 battery and the Zn/MnO2-2 battery had an activation process during cycling and the specific capacity reached a maximum after about 20 cycles, after which the capacity remained relatively stable. The specific capacity of the Zn/MnO2 battery decayed rapidly over the first 100 cycles and then more slowly. After 500 cycles, the capacity retention rate was only 51.6%. The charge and discharge curves of the Zn/MnO2-1 battery over different cycles are shown in Figure 6b. The charge and discharge curves remained stable over 500 cycles, which also means that the structure of the MnO2-1 electrode remained stable, indicating that the agar coating inhibited the dissolution of Mn2+ and maintained the structural stability of the α-MnO2. Compared with that of the Zn/MnO2 battery, the cycling stability of the Zn/MnO2-2 battery was also greatly improved (Figure S4b). In contrast, the charge–discharge curves of the Zn/MnO2 battery varied greatly during different charge–discharge cycles (Figure S4a). After 100 cycles, the second discharge plateau disappeared, which means that the structure of the α-MnO2 was destroyed.
To further explore the working principle of the MnO2-1 electrode, we investigated the ex situ XRD of the materials in different charge and discharge states during the first cycle (as shown in Figure 7b,c). During the discharge process, new peaks at 33° and 34.7°, which are the characteristic peaks of tunnel-type ZnMn2O4, were observed. During the charge process, the two peaks gradually disappear and return to the initial state. Therefore, the working principle of the MnO2-1 electrode during the charge and discharge processes can be expressed as [44]:
MnO2 + Zn2+ + x × e ⇄ ZnxMnO2 (0 < x < 1).

4. Conclusions

In conclusion, agar was introduced as an EMS for an α-MnO2 electrode. After coating with agar, the wettability of the MnO2 electrode was greatly improved; this increased the diffusion rate of Zn2+ on the surface of the MnO2 electrode and reduced the interface impedance. The impedance was the lowest, when the thickness of the coating layer was 4.94 μm (MnO2-1), so that the assembled Zn/MnO2-1 battery showed excellent rate performance. In addition, because the agar-coating layer promoted the reversibility of the MnO2/Mn2+ reaction, the Zn/MnO2-1 battery showed the highest specific discharge capacity of 384.7 mAh g−1 at a current density of 0.25 A g−1. Moreover, the agar EMS acted as a colloidal physical barrier on the surface, inhibited the dissolution of Mn2+ and maintained the stability of the structure of α-MnO2, so that the Zn/MnO2-1 battery had excellent cycling stability with a high capacity retention of 85.6% after 500 cycles at a current density of 0.5 A g−1.

Supplementary Materials

The following are available online at https://www.mdpi.com/article/10.3390/ma14174895/s1, Figure S1: FTIR spectrum of agar/MnO2, Figure S2: Fitting and calculation of slope in the EIS low frequency region of three batteries, Figure S3: Electrochemical charge–discharge curves at different current densities over the potential range 0.1–1.95 V: (a) MnO2, (b) MnO2-2, Figure S4: Electrochemical charge–discharge curves at a current density of 0.5 A g−1 over the potential range 0.1–1.95 V: (a) MnO2, (b) MnO2-2.

Author Contributions

Conceptualization, L.Z. and H.S.; data curation, L.Z.; formal analysis, L.Z., X.C., H.S.; investigation, X.Y., J.W. and S.Z.; writing—original draft preparation, L.Z.; writing—review and editing, X.C., S.Z., H.S., X.Y., J.W. and T.v.R.; supervision, Y.W., T.v.R.; funding acquisition, Y.W. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the National Key R & D Program of China (2018YFB0104300), National Natural Science Foundation Committee of China (Distinguished Youth Scientists Project of 51425301, U1601214), State Key Lab Research Foundation (ZK201805, ZK201717), and the Jiangsu Provincial Innovation Foundation for Postgraduates (grant No. KYCX20_1072).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

All the data are available within the manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Zeng, X.Q.; Li, M.; Abd El-Hady, D.; Alshitari, W.; Al-Bogami, A.S.; Lu, J.; Amine, K. Commercialization of lithium battery technologies for electric vehicles. Adv. Energy Mater. 2019, 9, 1900161. [Google Scholar] [CrossRef]
  2. Goodenough, J.B.; Park, K.S. The Li-ion rechargeable battery: A perspective. J. Am. Chem. Soc. 2013, 135, 1167–1176. [Google Scholar] [CrossRef]
  3. Etacheri, V.; Marom, R.; Elazari, R.; Salitra, G.; Aurbach, D. Challenges in the development of advanced Li-ion batteries: A review. Energy Environ. Sci. 2011, 4, 3243–3262. [Google Scholar] [CrossRef]
  4. Deng, J.; Bae, C.; Denlinger, A.; Miller, T. Electric vehicles batteries: Requirements and challenges. Joule 2020, 4, 511–515. [Google Scholar] [CrossRef]
  5. Li, W.; Zhu, J.E.; Xia, Y.; Gorji, M.B.; Wierzbicki, T. Data-driven safety envelope of lithium-ion batteries for electric vehicles. Joule 2019, 3, 2703–2715. [Google Scholar] [CrossRef]
  6. Chen, S.R.; Dai, F.; Cai, M. Opportunities and challenges of high-energy lithium metal batteries for electric vehicle applications. ACS Energy Lett. 2020, 5, 3140–3151. [Google Scholar] [CrossRef]
  7. Li, W.; Dahn, J.R.; Wainwright, D.S. Rechargeable lithium batteries with aqueous-electrolytes. Science 1994, 264, 1115–1118. [Google Scholar] [CrossRef]
  8. Wang, G.J.; Zhao, N.H.; Yang, L.C.; Wu, Y.P.; Wu, H.Q.; Holze, R. Characteristics of an aqueous rechargeable lithium battery (arlb). Electrochim. Acta 2007, 52, 4911–4915. [Google Scholar] [CrossRef]
  9. Liu, J.; Hu, J.P.; Deng, Q.; Mo, J.; Xie, H.; Liu, Z.C.; Xiong, Y.F.; Wu, X.W.; Wu, Y.P. Aqueous rechargeable batteries for large-scale energy storage. Isr. J. Chem. 2015, 55, 521–536. [Google Scholar] [CrossRef]
  10. Tang, W.; Zhu, Y.S.; Hou, Y.Y.; Liu, L.L.; Wu, Y.P.; Loh, K.P.; Zhang, H.P.; Zhu, K. Aqueous rechargeable lithium batteries as an energy storage system of superfast charging. Energy Environ. Sci. 2013, 6, 2093–2104. [Google Scholar] [CrossRef]
  11. Yuan, X.H.; Ma, F.X.; Zuo, L.Q.; Wang, J.; Yu, N.F.; Chen, Y.H.; Zhu, Y.S.; Huang, Q.H.; Holze, R.; Wu, Y.P.; et al. Latest advances in high-voltage and high-energy-density aqueous rechargeable batteries. Electrochem. Energy Rev. 2021, 4, 1–34. [Google Scholar] [CrossRef]
  12. Yuan, X.; Ma, F.; Chen, X.; Sun, R.; Chen, Y.; Fu, L.; Zhu, Y.; Liu, L.; Yu, F.; Wang, J.; et al. Aqueous zinc-sodium hybrid battery based on high crystallinity sodium-iron hexacyanoferrate. Mater. Today Energy 2021, 20, 100660. [Google Scholar] [CrossRef]
  13. Xiong, T.; Zhang, Y.X.; Lee, W.S.V.; Xue, J.M. Defect engineering in manganese-based oxides for aqueous rechargeable zinc-ion batteries: A review. Adv. Energy Mater. 2020, 10, 2001769. [Google Scholar] [CrossRef]
  14. Chen, P.; Yuan, X.H.; Xia, Y.B.; Zhang, Y.; Fu, L.J.; Liu, L.L.; Yu, N.F.; Huang, Q.H.; Wang, B.; Hu, X.W.; et al. An artificial polyacrylonitrile coating layer confining zinc dendrite growth for highly reversible aqueous zinc-based batteries. Adv. Sci. 2021, 8, 2100309. [Google Scholar] [CrossRef]
  15. Kim, S.J.; Wu, D.R.; Sadique, N.; Quilty, C.D.; Wu, L.J.; Marschilok, A.C.; Takeuchi, K.J.; Takeuchi, E.S.; Zhu, Y.M. Unraveling the dissolution-mediated reaction mechanism of alpha-MnO2 cathodes for aqueous Zn-ion batteries. Small 2020, 16, 2005406. [Google Scholar] [CrossRef]
  16. Gao, Y.N.; Yang, H.Y.; Bai, Y.; Wu, C. Mn-based oxides for aqueous rechargeable metal ion batteries. J. Mater. Chem. A 2021, 9, 11472–11500. [Google Scholar] [CrossRef]
  17. Liu, N.; Li, B.; He, Z.X.; Dai, L.; Wang, H.Y.; Wang, L. Recent advances and perspectives on vanadium- and manganese-based cathode materials for aqueous zinc ion batteries. J. Energy Chem. 2021, 59, 134–159. [Google Scholar] [CrossRef]
  18. Zhong, C.; Liu, B.; Ding, J.; Liu, X.R.; Zhong, Y.W.; Li, Y.; Sun, C.B.; Han, X.P.; Deng, Y.D.; Zhao, N.Q.; et al. Decoupling electrolytes towards stable and high-energy rechargeable aqueous zinc-manganese dioxide batteries. Nat. Energy 2020, 5, 440–449. [Google Scholar] [CrossRef]
  19. Liu, Y.; Zhi, J.; Sedighi, M.; Han, M.; Shi, Q.Y.; Wu, Y.; Chen, P. Mn2+ ions confined by electrode microskin for aqueous battery beyond intercalation capacity. Adv. Energy Mater. 2020, 10, 2002578. [Google Scholar] [CrossRef]
  20. Lee, W.K.; Lim, Y.Y.; Leow, A.T.C.; Namasivayam, P.; Abdullah, J.O.; Ho, C.L. Biosynthesis of agar in red seaweeds: A review. Carbohydr. Polym. 2017, 164, 23–30. [Google Scholar] [CrossRef]
  21. Lee, W.H.; Choi, S.R.; Kim, J.G. Effect of agar as electrolyte additive on the aluminum-air batteries. J. Electrochem. Soc. 2020, 167, 110503. [Google Scholar] [CrossRef]
  22. Liew, S.Y.; Juan, J.C.; Lai, C.W.; Pan, G.T.; Yang, T.C.K.; Lee, T.K. An eco-friendly water-soluble graphene-incorporated agar gel electrolyte for magnesium-air batteries. Ionics 2019, 25, 1291–1301. [Google Scholar] [CrossRef]
  23. Lu, C.H.; Li, W.Y.; Subburaj, T.; Ou, C.Y.; Kumar, P.S. Influence of bio-derived agar addition on the electrochemical performance of LiFePO4 cathode powders for Li-ion batteries. Ceram. Int. 2019, 45, 12218–12224. [Google Scholar] [CrossRef]
  24. Menzel, J.; Frackowiak, E.; Fic, K. Agar-based aqueous electrolytes for electrochemical capacitors with reduced self-discharge. Electrochim. Acta 2020, 332, 135435. [Google Scholar] [CrossRef]
  25. Chotkowski, M.; Rogulski, Z.; Czerwinski, A. Spectroelectrochemical investigation of MnO2 electro-generation and electro-reduction in acidic media. J. Electroanal. Chem. 2011, 651, 237–242. [Google Scholar] [CrossRef]
  26. Su, D.; Ahn, H.J.; Wang, G. Hydrothermal synthesis of alpha-MnO2 and beta-MnO2 nanorods as high capacity cathode materials for sodium ion batteries. J. Mater. Chem. A 2013, 1, 4845–4850. [Google Scholar] [CrossRef] [Green Version]
  27. Wu, M.S.; Liao, T.L.; Wang, Y.Y.; Wan, C.C. Assessment of the wettability of porous electrodes for lithium-ion batteries. J. Appl. Electrochem. 2004, 34, 797–805. [Google Scholar] [CrossRef]
  28. Jeon, D.H. Wettability in electrodes and its impact on the performance of lithium-ion batteries. Energy Storage Mater. 2019, 18, 139–147. [Google Scholar] [CrossRef]
  29. Zhang, X.T.; Li, J.X.; Ao, H.S.; Liu, D.Y.; Shi, L.; Wang, C.M.; Zhu, Y.C.; Qian, Y.T. Appropriately hydrophilic/hydrophobic cathode enables high-performance aqueous zinc-ion batteries. Energy Storage Mater. 2020, 30, 337–345. [Google Scholar] [CrossRef]
  30. Delay, A.; Infelta, P.P. On the impedance of an interface between a pt electrode and a naf solution. Electrochim. Acta 1990, 35, 1177–1184. [Google Scholar] [CrossRef]
  31. Ruetschi, P.; Giovanoli, R. Cation vacancies in MnO2 and their influence on electrochemical reactivity. J. Electrochem. Soc. 1988, 135, 2663–2669. [Google Scholar] [CrossRef]
  32. Sun, W.; Wang, F.; Hou, S.Y.; Yang, C.Y.; Fan, X.L.; Ma, Z.H.; Gao, T.; Han, F.D.; Hu, R.Z.; Zhu, M.; et al. Zn/MnO2 battery chemistry with H+ and Zn2+ coinsertion. J. Am. Chem. Soc. 2017, 139, 9775–9778. [Google Scholar] [CrossRef] [PubMed]
  33. Huang, A.X.; Chen, J.Z.; Zhou, W.J.; Wang, A.R.; Chen, M.F.; Tian, Q.H.; Xu, J.L. Electrodeposition of MnO2 nanoflakes onto carbon nanotube film towards high-performance flexible quasi-solid-state Zn-MnO2 batteries. J. Electroanal. Chem. 2020, 873, 114392. [Google Scholar] [CrossRef]
  34. Chen, S.G.; Lan, R.; Humphreys, J.; Tao, S.W. Salt-concentrated acetate electrolytes for a high voltage aqueous Zn/MnO2 battery. Energy Storage Mater. 2020, 28, 205–215. [Google Scholar] [CrossRef]
  35. Ghosh, M.; Vijayakumar, V.; Anothumakkool, B.; Kurungot, S. Nafion lonomer-based single component electrolytes for aqueous Zn/MnO2 batteries with long cycle life. ACS Sustain. Chem. Eng. 2020, 8, 5040–5049. [Google Scholar] [CrossRef]
  36. Cao, J.; Zhang, D.D.; Zhang, X.Y.; Wang, S.M.; Han, J.T.; Zhao, Y.S.; Huang, Y.H.; Qin, J.Q. Mechanochemical reactions of MnO2 and graphite nanosheets as a durable zinc ion battery cathode. Appl. Surf. Sci. 2020, 534, 147630. [Google Scholar] [CrossRef]
  37. Zhou, W.J.; Wang, A.R.; Huang, A.X.; Chen, M.F.; Tian, Q.H.; Chen, J.Z.; Xu, X.W. Hybridizing delta-type MnO2 with lignin-derived porous carbon as a stable cathode material for aqueous Zn-MnO2 batteries. Front. Energy Res. 2020, 8, 182. [Google Scholar] [CrossRef]
  38. Huang, Y.; Li, Z.X.; Jin, S.Y.; Zhang, S.D.; Wang, H.L.; Hiralal, P.; Amaratunga, G.A.J.; Zhou, H. Carbon nanohorns/nanotubes: An effective binary conductive additive in the cathode of high energy-density zinc-ion rechargeable batteries. Carbon 2020, 167, 431–438. [Google Scholar] [CrossRef]
  39. Liu, N.N.; Mohanapriya, K.; Pan, J.; Hu, Y.; Sun, Y.Z.; Liu, X.G. A facile preparation of lambda-MnO2 as cathode material for high-performance zinc-manganese redox flow battery. J. Electrochem. Soc. 2020, 167, 040517. [Google Scholar] [CrossRef]
  40. Wang, C.Y.; Wang, M.Q.; He, Z.C.; Liu, L.; Huang, Y.D. Rechargeable aqueous zinc-manganese dioxide/graphene batteries with high rate capability and large capacity. ACS Appl. Energy Mater. 2020, 3, 1742–1748. [Google Scholar] [CrossRef]
  41. Gao, X.; Wu, H.W.; Li, W.J.; Tian, Y.; Zhang, Y.; Wu, H.; Yang, L.; Zou, G.Q.; Hou, H.S.; Ji, X.B. H+ insertion boosted alpha-MnO2 for an aqueous Zn-ion battery. Small 2020, 16, 1905842. [Google Scholar] [CrossRef] [PubMed]
  42. Mao, J.; Wu, F.F.; Shi, W.H.; Liu, W.X.; Xu, X.L.; Cai, G.F.; Li, Y.W.; Cao, X.H. Preparation of polyaniline-coated composite aerogel of MnO2 and reduced graphene oxide for high-performance zinc-ion battery. Chin. J. Polym. Sci. 2020, 38, 514–521. [Google Scholar] [CrossRef]
  43. Palaniyandy, N.; Kebede, M.A.; Raju, K.; Ozoemena, K.I.; le Roux, L.; Mathe, M.K.; Jayaprakasam, R. Alpha-MnO2 nanorod/onion-like carbon composite cathode material for aqueous zinc-ion battery. Mater. Chem. Phys. 2019, 230, 258–266. [Google Scholar] [CrossRef]
  44. Wu, B.K.; Zhang, G.B.; Yan, M.Y.; Xiong, T.F.; He, P.; He, L.; Xu, X.; Mai, L.Q. Graphene scroll-coated alpha-MnO2 nanowires as high-performance cathode materials for aqueous Zn-ion battery. Small 2018, 14, 1703850. [Google Scholar] [CrossRef]
Materials 14 04895 g001 550
Figure 1. Physical properties of the prepared MnO2: (a,b) SEM images; (c,d) TEM images; (e) XRD patterns.
Figure 1. Physical properties of the prepared MnO2: (a,b) SEM images; (c,d) TEM images; (e) XRD patterns.
Materials 14 04895 g001
Materials 14 04895 g002 550
Figure 2. (a) FTIR spectrum of agar; SEM image of α-MnO2 (b,e), MnO2-1 (c,f), and MnO2-2 (d,g).
Figure 2. (a) FTIR spectrum of agar; SEM image of α-MnO2 (b,e), MnO2-1 (c,f), and MnO2-2 (d,g).
Materials 14 04895 g002
Materials 14 04895 g003 550
Figure 3. Contact angle photos of the electrolyte on α-MnO2 (a), MnO2-1 (b), and MnO2-2 (c).
Figure 3. Contact angle photos of the electrolyte on α-MnO2 (a), MnO2-1 (b), and MnO2-2 (c).
Materials 14 04895 g003
Materials 14 04895 g004 550
Figure 4. (a) Electrochemical impedance spectroscopy (EIS) spectra; and (b) cyclic voltammetry (CV) curves of the three batteries at a scan rate of 0.3 mV s−1.
Figure 4. (a) Electrochemical impedance spectroscopy (EIS) spectra; and (b) cyclic voltammetry (CV) curves of the three batteries at a scan rate of 0.3 mV s−1.
Materials 14 04895 g004
Materials 14 04895 g005 550
Figure 5. (a) CV curves of the Zn/MnO2-1 battery at various scan rates over the potential range of 0.1–1.95 V; (b) a linear fit of log(i) as a function of log(v); (c) rate performances of the three batteries; (d) charge–discharge curves of the Zn/MnO2-1 battery at different current densities.
Figure 5. (a) CV curves of the Zn/MnO2-1 battery at various scan rates over the potential range of 0.1–1.95 V; (b) a linear fit of log(i) as a function of log(v); (c) rate performances of the three batteries; (d) charge–discharge curves of the Zn/MnO2-1 battery at different current densities.
Materials 14 04895 g005
Materials 14 04895 g006 550
Figure 6. (a) Cycling performances of the three batteries at a current density of 0.5 A g−1 in the potential range between 0.1 and 1.95 V; (b) electrochemical charge–discharge profiles of MnO2-1.
Figure 6. (a) Cycling performances of the three batteries at a current density of 0.5 A g−1 in the potential range between 0.1 and 1.95 V; (b) electrochemical charge–discharge profiles of MnO2-1.
Materials 14 04895 g006
Materials 14 04895 g007 550
Figure 7. Electrode reaction mechanisms of MnO2-1 in ZIBs. (a) Charge/discharge curves of the MnO2-1 electrode; the dots in the figure indicate that samples at that charge/discharge depth were used for ex situ XRD analysis; (b) ex situ XRD patterns of the MnO2-1 electrode at various charge/discharge states; (c) magnified XRD patterns with 2θ from 25° to 40°.
Figure 7. Electrode reaction mechanisms of MnO2-1 in ZIBs. (a) Charge/discharge curves of the MnO2-1 electrode; the dots in the figure indicate that samples at that charge/discharge depth were used for ex situ XRD analysis; (b) ex situ XRD patterns of the MnO2-1 electrode at various charge/discharge states; (c) magnified XRD patterns with 2θ from 25° to 40°.
Materials 14 04895 g007
Table
Table 1. Electrochemical performance of the MnO2–agar cathode compared with those of different manganese oxide cathodes in recent studies.
Table 1. Electrochemical performance of the MnO2–agar cathode compared with those of different manganese oxide cathodes in recent studies.
CathodeAnodeElectrolyteElectrolyte Voltage (V)Capacity
(mAh g−1)		Retention/CyclesRef.
CNT@MnO2zinc foil2 M ZnSO4/0.2 M MnSO41–1.85105.6 mAh g−1
(3 mA cm−2)		85.72%/1000 cycles[33]
α-MnO2-TiN/TiOzinc foil1 M Zn(OAc)/31 M KOAc0.8–2.0304.6 mAh·g−1
(100 mA g−1)		79.7%/600 cycles[34]
MnCP-Xzinc foil1 M Zn(CF3SO3)20.8–2.0151 mAh g−1 (3 A g−1)89%/500 cycles[35]
MnO2/graphitezinc foil2 M ZnSO4/0.5 M MnSO40.8–1.880 mAh g−1 (1 A g−1)80.8%/1000 cycles[36]
LPC/δ-MnO2zinc foil2 M ZnSO4/0.2 M MnSO41.0–1.85196.1 mAh g–1 (5 A g–1)82%/1000 cycles[37]
MnO2-CNTs/CNHszinc foil2 M ZnSO4/0.1 M MnSO41.0–1.9168.1 mAh g−1 (3 A g−1)96.5%/500 cycles[38]
λ-MnO2zinc foil1 M Li2SO4/1 M ZnSO41.5–2.1128 mAh g−1 (2 C)83%/1,000 cycles[39]
MnO2/GOzinc foil2 M ZnSO4/0.2 M MnSO40.9–1.8190mAh g−1 (3C)91%/cycles[40]
MnO2/carbonzinc foil2 M ZnSO4/0.2 M MnSO40.9–1.8240 mAh g−1 (0.1 A g−1)58.33%/300 cycles[41]
MnO2/rGO/PANIzinc foil2 M ZnSO40.8–1.8100.6 mAh·g−1 (1 A g−1)82.7%/600 cycles[42]
MnO2/OLCzinc foil1 M ZnSO4/0.1M MnSO41.0–1.8168 mAh g−1 (246 mA g−1)93%/100 cycles[43]
MnO2–agarzinc foil2 M ZnSO4/0.5 M MnSO40.1–1.95260.6 mAh g−1 (0.5 A g−1)95.4%/500 cyclesThis work
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Zuo, L.; Sun, H.; Yuan, X.; Wen, J.; Chen, X.; Zhou, S.; Wu, Y.; van Ree, T. Agar Acts as Cathode Microskin to Extend the Cycling Life of Zn//α-MnO2 Batteries. Materials 2021, 14, 4895. https://doi.org/10.3390/ma14174895

AMA Style

Zuo L, Sun H, Yuan X, Wen J, Chen X, Zhou S, Wu Y, van Ree T. Agar Acts as Cathode Microskin to Extend the Cycling Life of Zn//α-MnO2 Batteries. Materials. 2021; 14(17):4895. https://doi.org/10.3390/ma14174895

Chicago/Turabian Style

Zuo, Linqing, Haodong Sun, Xinhai Yuan, Juan Wen, Xi Chen, Shiyu Zhou, Yuping Wu, and Teunis van Ree. 2021. "Agar Acts as Cathode Microskin to Extend the Cycling Life of Zn//α-MnO2 Batteries" Materials 14, no. 17: 4895. https://doi.org/10.3390/ma14174895

APA Style

Zuo, L., Sun, H., Yuan, X., Wen, J., Chen, X., Zhou, S., Wu, Y., & van Ree, T. (2021). Agar Acts as Cathode Microskin to Extend the Cycling Life of Zn//α-MnO2 Batteries. Materials, 14(17), 4895. https://doi.org/10.3390/ma14174895

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop