Next Article in Journal
Residual Bone Height and New Bone Formation after Maxillary Sinus Augmentation Procedure Using Biomaterials: A Network Meta-Analysis of Clinical Trials
Next Article in Special Issue
Adsorption of Phosphate and Ammonium on Waste Building Sludge
Previous Article in Journal
Aesthetic Restorations: The Role of The Dental Hygienist in Professional Maintenance: In Vitro Microbiological Study
Previous Article in Special Issue
Physical, Mechanical and Radiological Characteristics of a Fly Ash Geopolymer Incorporating Titanium Dioxide Waste as Passive Fire Insulating Material in Steel Structures
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 16
Issue 4
10.3390/ma16041374
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Mechanical Properties of Cement Mortar Containing Ground Waste Newspaper as Cementitious Material

by
Jae-In Lee
,
Chae-Young Kim
,
Joo-Ho Yoon
and
Se-Jin Choi
*
Department of Architectural Engineering, Wonkwang University, 460 Iksan-daero, Iksan 54538, Republic of Korea
*
Author to whom correspondence should be addressed.
Materials 2023, 16(4), 1374; https://doi.org/10.3390/ma16041374
Submission received: 6 January 2023 / Revised: 3 February 2023 / Accepted: 3 February 2023 / Published: 6 February 2023
(This article belongs to the Special Issue Convergence & Sustainable Technology in Building Materials)
Browse Figures
Versions Notes

Abstract

:
In recent years, several studies have reported the recycling of by-products generated by the paper industry and their application to the construction industry. A majority of the existing studies used waste paper sludge ash, and considerable energy is consumed in such incineration processes. This may further contribute to air pollution. In this study, we used waste newspaper (WNP), which underwent a simple crushing process without a separate high-temperature treatment process, and we integrated it in cement mortar. We prepared mortars containing 0%, 0.2%, 0.4%, 0.6%, 0.8%, and 1.0% ground WNP as a cement substitute. Subsequently, the fluidity, compressive strength, tensile strength, carbonation depth, drying shrinkage, and microstructure of the mortars were compared and analyzed. The 28-day compressive strength of the mortar samples with WNP was approximately 3.2–16.1% higher than that of the control sample. The 28-day accelerated carbonation depth of the samples with WNP was approximately 1.03–1.61 mm. Furthermore, their carbonation resistance was approximately 5.2–39.4% higher than that of the control sample. Compressive strength, tensile strength, and carbonation resistance were improved by appropriately using ground WNP as a cement substitute in cement mortar. In this study, the appropriate amount of WNP according to the mechanical properties of cement mortar was found to be 0.4–0.8%, and considering the durability characteristics, the value 0.6 was the most ideal.

1. Introduction

In recent years, various efforts have been made to reduce greenhouse gas emissions and environmental load at home and abroad, such as through the use of ecofriendly materials and alternative energy [1,2]. In addition, as countries are promoting carbon-neutral policies, the construction industry must make efforts to reduce greenhouse gas emissions [3]. Portland cement is widely used in the construction industry. It is a powder-type binder that has been used for a long time. It strongly affects environmental pollution, accounting for approximately 5–9% of greenhouse gas emissions generated during cement production [4]. To reduce total cement consumption in the concrete industry, many studies have investigated the application of cementitious materials such as fly ash, blast furnace slag, and silica fume to cement concrete [5,6,7,8,9,10].
Meanwhile, approximately 1.6 million tons of paper sludge, which is a by-product of the paper industry, is generated annually in Korea. This paper sludge contains about 60–70% moisture and causes environmental pollution when it is dumped in landfills, incinerated, and illegally discharged during the treatment process [11].
To solve these problems, several studies have examined the recycling of by-products from the paper industry and their application to the construction industry [12,13,14,15,16,17,18,19,20,21,22]. Sudha et al. [13] reviewed the strength characteristics of concrete mixed with 5%, 10%, 15%, and 20% waste paper sludge ash as a cement substitute. They reported that the compressive strength and tensile strength of concrete increased when it was mixed with up to 10% waste paper sludge ash and decreased thereafter. Shabbir et al. [14] investigated the feasibility of waste paper sludge ash (WPSA) use in concrete. The setting time of cement and the weight of concrete decreased as the mixing ratio of WPSA increased. In addition, WPSA could replace up to 15% of cement by weight. Garcia et al. [15] examined the pozzolanic properties of waste paper sludge. They reported high pozzolanic activity when paper ink-removed sludge was calcined at 700 °C. Additionally, compressive strength increased when 10% of the ink-removed sludge was used as a cement substitute. Hong et al. [16] used paper sludge ash (PSA) to produce powder and then mixed it with concrete. They found that the water absorption and thermal conductivity of the sample with 12% PSA were 84% and 86% of the non-blended sample, respectively. Bui et al. [17] used by-products such as waste paper sludge ash (PSA), fly ash, and silica fume in recycled aggregate concrete. The outcomes of their study reported that PSA improved the mechanical properties of recycled aggregate concrete at an early age.
However, a majority of the existing studies used waste paper sludge ash. In the associated incineration process, a significant amount of energy is consumed, which may further contribute to air pollution. In this study, we prepared waste newspaper (WNP), which underwent a simple crushing process without a separate high-temperature treatment process, and incorporated it into cement mortar. We conducted an experiment to study the applicability of ground WNP as a cement substitute. For this purpose, we prepared mortars containing 0%, 0.2%, 0.4%, 0.6%, 0.8%, and 1.0% ground WNP for use as a cement substitute. We then analyzed and compared the fluidity, compressive strength, tensile strength, carbonation depth, drying shrinkage, and microstructure of the mortars.

2. Experimental Materials and Methods

2.1. Materials

Ordinary Portland cement (Hanil Hyundai Cement, Seoul, Republic of Korea) was used in this study. Natural sand from Namwon with a density of 2.60 g/cm3 and a fineness modulus of 2.45 was used as the fine aggregate. We used WNP available in the Wonkwang University, Iksan-si, Republic of Korea. Based on the outcomes of several preliminary experiments, it was submerged in water for 24 h, dried for 48 h, and then grinded using a grinder.
Table 1 and Table 2 show the chemical composition of the cement and WNP, respectively. Table 3 shows the physical properties of the fine aggregate. Figure 1 and Figure 2 show the shapes and scanning electron microscopy (SEM) images of the cement and ground WNP, and Figure 3 shows the particle size distribution curve of the fine aggregate.

2.2. Mixing Proportions and Testing Methods

Table 4 shows the mixing proportions of the cement mortars used in this study. We selected W/B 50%, which is widely used as a water–binder ratio (W/B) for normal concrete mixtures in Korea. We used ground WNP to replace 0%, 0.2%, 0.4%, 0.6%, 0.8%, and 1.0% of the cement by weight. Cubic specimens with dimensions of 50 mm × 50 mm × 50 mm were prepared via molding for compressive strength testing, and cylindrical specimens with dimensions of ø50 mm × 100 mm were prepared for split tensile strength testing [23] and carbonation tests. In addition, 40 mm × 40 mm × 160 mm specimens were prepared for evaluation of drying shrinkage. We demolded the specimens after 24 h and cured them in a water tank at 20 °C until they reached the required age.
Mortar flow and compressive strength were measured according to KS L 5105 [24], and tensile strength was determined according to KS F 2423 [25]. In the carbonation test, carbonation depth was measured after the carbonation process using a phenolphthalein solution in an accelerated carbonation chamber according to KS F 2584 [26] (Figure 4). In the case of drying shrinkage, we demolded after 24 h in accordance with KS F 2424 [27] and cured in a water tank at 20 ± 3 °C for 1 week. The samples were then preserved in an environment where the temperature was maintained at 20 ± 3 °C and the humidity at 60 ± 5%, and it was measured using a contact gauge. In addition, SEM (AIS1800C, SERON Technologies, Seoul, Republic of Korea) and energy-dispersive X-ray spectroscopy (EDS; OXFORD Instruments, Xplore, Abingdon, UK) were used for microstructural analysis.

3. Results and Discussion

3.1. Mortar Flow

Figure 5 shows the change in mortar flow according to the WNP mixing ratio. In the control sample without WNP, the highest flow was approximately 176 mm. In the case of the samples with WNP, the flow was the highest in the WNP0.2 sample (164 mm). Mortar flow gradually decreased as the WNP mixing ratio increased. The flow of the WNP1.0 sample was the lowest at approximately 123 mm, which was approximately 30.1% lower than that of the control sample.
This was because cellulose, which is the main component of WNP, is a hydrophilic material with high water absorption [28,29]. Thus, it absorbed water during mixing and the flow decreased. The decrease in mortar flow may cause deterioration of workability and poor compaction at construction sites.

3.2. Compressive Strength

Figure 6 shows the change in the compressive strength of the mortars according to the WNP mixing ratio. At an age of 7 days, the highest compressive strength (approximately 36.8 MPa) was observed in the control sample. In the case of the samples with WNP, the highest compressive strength (approximately 34.9 MPa) was observed in the WNP0.4 sample, and the lowest compressive strength (approximately 28.9 MPa) was observed in the WNP 1.0 sample. The 7-day compressive strength of the samples with WNP was approximately 5.1–21.4% lower than that of the control sample.
At an age of 28 days, the compressive strength of the control sample was approximately 38.0 MPa, and that of the WNP0.4 sample was approximately 44.1 MPa, which was approximately 16.1% higher than that of the control sample. The 28-day compressive strength of the WNP0.8 sample was approximately 43.5 MPa, which was approximately 27.9% higher than the 7-day compressive strength. The 28-day compressive strength of all mortar samples with WNP was approximately 3.2–16.1% higher than that of the control sample. In addition, the compressive strength evolution rate of the samples with WNP after 7 days was 19.9–35.9%, which was significantly higher than that of the control sample (3.2%). The compressive strength of the samples with WNP increased because the water–binder ratio decreased as WNP absorbed water during mixing. In addition, the hydration product adhered to the rough cellulose surface and increased the density of the internal structure [30].
In this study, the early compressive strength of the sample that used WNP was lower than that of the control sample, and the strength of the sample increased afterwards. This may be attributed to the fact that initial hydration was delayed due to the high water absorption of WNP and the increase in micropores [16,31]. In addition, the tendency to increase strength may be attributed to the release of absorbed moisture, which thus promotes hydration; hydration products may form on the cellulose surface to fill pores, resulting in a dense structure [30,32]. However, when the amount of WNP used increases, some strength may be lost due to the fiber ball phenomenon of WNP, which is similar to fiber [33].

3.3. Split Tensile Strength

Figure 7 shows the change in the split tensile strength of the mortar according to the WNP mixing ratio after 28 days. The tensile strength of the control sample was approximately 3.28 MPa. The tensile strength of the WNP0.4 sample was approximately 3.29 MPa, which was similar to that of the control sample. The tensile strength of the WNP1.0 sample was approximately 3.55 MPa, which was the highest, and it was approximately 8.2% higher than that of the control sample.
The increase in the tensile strength of mortar samples containing WNP may be attributed to the improvement in adhesion performance between the rough surface of WNP and the cement paste [34,35]. However, in some samples that contain WNP, strength degraded due to the fiber ball phenomenon [33], indicating the need for further research on the correlation between the homogeneous dispersion method and mechanical properties.

3.4. Carbonation Resistance

Figure 8 shows the change in the carbonation depth of the mortar samples according to the WNP mixing ratio. The accelerated carbonation depth of the control sample was the highest at approximately 1.70 mm. The carbonation depth of the WNP0.6 sample was the lowest at approximately 1.03 mm, and it was approximately 39.4% lower than that of the control sample. The carbonation depth of the WNP1.0 sample was approximately 1.61 mm, which was the highest among the samples with WNP. This was due to the relatively low 28-day compressive strength [36] of the WNP1.0 sample, as shown in the compressive strength test results (Figure 5). Carbonation depth did not exhibit a variation trend according to the WNP mixing ratio. In addition, the carbonation depth of all the samples with WNP was lower than that of the control samples. The 28-day accelerated carbonation depth of the samples with WNP was approximately 1.03–1.61 mm, and their carbonation resistance was approximately 5.2–39.4% higher than that of the control sample. This was because cellulose formed an asymmetric structure, which reduced the inflow rate of CO2 through internal crack control, thereby increasing carbonation resistance [37].
Figure 9 shows the correlation between compressive strength and carbonation depth. Carbonation depth tends to decrease as compressive strength increases, and the correlation was not sufficiently high.

3.5. Drying Shrinkage

Figure 10 shows the change in mortar drying shrinkage according to the WNP mixing ratio. The drying shrinkage of the control sample was the lowest at approximately 0.101%. The drying shrinkage of the WNP0.2 and WNP0.8 samples was approximately 0.104%, which was relatively low. The drying shrinkage of the WNP1.0 sample was the highest at approximately 0.116%.
The drying shrinkage of the samples with WNP was higher than that of the control sample because cellulose absorbed moisture and then released the absorbed water over time [38]. According to the existing literature [39,40], approximately 30–40% of cellulose can be extracted from newspaper.

3.6. Microstructural Analysis

Figure 11 shows the microstructural analysis of the samples. From the SEM images, it can be observed that there was no significant difference between the surface of the sample containing WNP and the surface of the control sample.
Table 5 shows the EDS results for component analysis of the samples. The components were detected in the order of Ca, C, Si, and Al in the control sample and C, Si, Al, and Ca in the WNP0.2 and WNP0.8 samples. The amounts of Si and Al in the samples with WNP were larger than those in the control sample.

4. Conclusions

The main results of the study are summarized below.
  • Mortar flow gradually decreased as the WNP mixing ratio increased. This may be attributed to the fact that cellulose, which is the main component of WNP, is a hydrophilic material with high water absorbency. Thus, it absorbed water during mixing and the flow subsequently decreased.
  • The early compressive strength of the sample containing WNP was lower than that of the control sample, and strength increased afterwards. This may be attributed to the fact that initial hydration was delayed due to the high water absorption of WNP and the increase in micropores. In addition, the tendency to increase strength may be caused by the release of absorbed moisture, which thus promotes hydration; hydration products may form on the cellulose surface to fill pores, resulting in a dense structure.
  • The 28-day accelerated carbonation depth of the samples with WNP was approximately 1.03–1.61 mm, and their carbonation resistance was approximately 5.2–39.4% higher than that of the control sample.
  • It was confirmed that compressive strength, tensile strength, and carbonation resistance were improved by utilizing ground WNP as a cement substitute in mortar. In this study, the appropriate amount of WNP according to the mechanical properties of cement mortar was found to be 0.4–0.8%, and considering durability characteristics, 0.6% WNP was the optimal value.
In the future, it is necessary to examine the correlation between the microstructure, mechanical properties, and durability properties of samples with WNP.

Author Contributions

Conceptualization, S.-J.C.; Investigation, S.-J.C. and J.-I.L.; Data Curation, C.-Y.K. and J.-H.Y.; Writing—Original Draft Preparation, S.-J.C. and C.-Y.K.; Writing—Review and Editing, S.-J.C. All authors have read and agreed to the published version of the manuscript.

Funding

This paper was supported by Wonkwang University in 2022.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

The authors gratefully acknowledge Wonkwang University for their financial support.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Lee, J.I.; Bae, S.H.; Kim, J.H.; Choi, S.J. Effect of cementitious materials on the engineering properties of lightweight aggregate mortars containing recycled water. Materials 2022, 15, 1967. [Google Scholar] [CrossRef] [PubMed]
  2. Nowotna, A.; Pietruszka, B.; Lisowski, P. Eco-friendly building materials. IOP Conf. Ser. Earth Environ. Sci. 2019, 290, 012024. [Google Scholar] [CrossRef]
  3. Jang, N.C. Improvements of the Renewable Energy Legislation for the realization of 2050 carbon neutral. Justice 2022, 190, 5–27. [Google Scholar]
  4. Talaei, A.; Pier, D.; Lyer, A.V.; Ahiduzzaman, M.; Kumar, A. Assessment of long-term energy efficiency improvement and greenhouse gas emissions mitigation options for the cement industry. Energy 2019, 170, 1051–1066. [Google Scholar] [CrossRef]
  5. Charith, H.; Chamila, G.; David, W.L.; Sujeeva, S. Performance of high volume fly ash concrete incorporating additives: A systematic literature review. Constr. Build. Mater. 2020, 258, 120606. [Google Scholar]
  6. Mugahed, A.; Solomon, D.; Togay, O. Fly ash-based eco-friendly geopolymer concrete: A critical review of the long-term durability properties. Constr. Build. Mater. 2021, 270, 121857. [Google Scholar]
  7. Quang, D.N.; Khan, M.S.H.; Arnaud, C.; Kim, T. Durability and microstructure properties of low-carbon concrete incorporating ferronickel slag sand and fly ash. J. Mater. Civ. Eng. 2019, 31, 04019152. [Google Scholar]
  8. Erdogan, O.; Mustafa, E.; Halil, I.D. Utilization and efficiency of ground granulated blast furnace slag on concrete properties-A review. Constr. Build. Mater. 2016, 105, 423–434. [Google Scholar]
  9. Dinakar, P.; Kali, P.S.; Umesh, C.S. Design of self-compacting concrete with ground granulated blast furnace slag. Mater. Des. 2013, 43, 161–169. [Google Scholar] [CrossRef]
  10. Ali, R.B.; Hamed, Z.; Mohamad, M.M. Mechanical and durability properties of ternary concretes containing silica fume and low reactivity blast furnace slag. Cem. Concr. Compos. 2012, 34, 663–670. [Google Scholar]
  11. Jung, J.H.; Seo, S.K.; Chu, Y.S. A study on pretreated paper sludge ash for cement admixture. J. Korean Inst. Resour. Recycl. 2016, 25, 58–64. [Google Scholar]
  12. Ko, J.C.; Kim, S.H.; Park, Y.K.; Jeon, J.Y.; Kim, J.H.; Park, J.S. Pyrolysis characteristics of sludge discharged from paper mill process. J. Korea Org. Resour. Recycl. Assoc. 2009, 17, 80–87. [Google Scholar]
  13. Sudha, J.L.; Sagar, D.S.V.S.R.; Ram, R.J. Experimental studies on strength characteristics of concrete with waste paper sludge ash as partial replacement for cement. Int. J. Res. Anal. Rev. 2018, 5, 342–347. [Google Scholar]
  14. Shabbir, F.; Ejaz, N.; Khan, D.; Ahmad, N.; Hussain, J. Investigation of using paper industry waste (hypo sludge) in concrete mix. J. Eng. Appl. Sci. 2015, 34, 7–12. [Google Scholar]
  15. Garcia, R.; Villa, R.V.; Frias, M.; Rojas, M.I.S. The pozzolanic properties of paper sludge waste. Constr. Build. Mater. 2008, 22, 1484–1490. [Google Scholar] [CrossRef]
  16. Hong, S.W.; Robert, B.; Abdulla, A.; Mohamed, S. Hydrophobic concrete using waste paper sludge ash. Cem. Concr. Res. 2015, 70, 9–20. [Google Scholar]
  17. Bui, N.K.; Satomi, T.; Takahashi, H. Influence of industrial by-products and waste paper sludge ash on properties of recycled aggregate concrete. J. Clean. Prod. 2019, 214, 403–418. [Google Scholar] [CrossRef]
  18. Fedorov, V.; Mestnikov, A. Influence of cellulose fibers on structure and properties of fiber reinforced foam concrete. MATEC Web Conf. 2018, 143, 02008. [Google Scholar] [CrossRef]
  19. Wang, Z.; Li, H.; Jiang, Z. Effect of waste paper fiber on properties of cement-based mortar and relative mechanism. Mater. Sci. Ed. 2018, 33, 419–426. [Google Scholar] [CrossRef]
  20. Liu, J.; Lv, C. Research progress on durability of cellulose fiber-reinforced cement-based composites. Int. J. Polym. Sci. 2021, 2021, 1014531. [Google Scholar] [CrossRef]
  21. Lyu, H.S.; Lee, S.S.; Kwon, S.J. Evaluation of workability and strength in concrete with cellulose fibers. J. Rec. Const. Res. Inst. 2020, 8, 198–203. [Google Scholar]
  22. Nasir, M.; Aziz, M.A.; Zubair, M.; Ashraf, N.; Hussein, T.N.; Allubli, M.K.; Manzar, M.S.; Al-Kutti, W.; Al-Harthi, M.A. Engineered cellulose nanocrystals-based cement mortar from office paper waste: Flow, strength, microstructure, and thermal properties. J. Build. Eng. 2022, 51, 104345. [Google Scholar] [CrossRef]
  23. KS F 2403; Standard Test Method for Making and Curing Concrete Specimens. Korean Standards & Certification Information Center: Seoul, Republic of Korea, 2019.
  24. KS L 5105; Testing Method for Compressive Strength of Hydraulic Cement Mortars. Korean Standards & Certification Information Center: Seoul, Republic of Korea, 2007.
  25. KS F 2423; Standard Test Method for Tensile Splitting Strength of Concrete. Korean Standards & Certification Information Center: Seoul, Republic of Korea, 2011.
  26. KS F 2584; Standard Test Method for Accelerated Carbonation of Concrete. Korean Standards & Certification Information Center: Seoul, Republic of Korea, 2015.
  27. KS F 2424; Standard Test Method for Length Change of Mortar and Concrete. Korean Standards & Certification Information Center: Seoul, Republic of Korea, 2015.
  28. Singh, H.; Gupta, R. Influence of cellulose fiber addition on self-healing and water permeability of concrete. Case Stud. Constr. Mater. 2020, 12, e00324. [Google Scholar] [CrossRef]
  29. Salem, R.M.; Al-Salami, A.E. Preparation of waste paper fibrous cement and studying of some physical properties. Civ. Environ. Res. 2016, 8, 42–54. [Google Scholar]
  30. Xuan, M.Y.; Wang, X.Y. Multi-technique investigation regarding the impact of cellulose nanofibers on ultra-high-performance concrete at the macroscopic and microscopic levels. Constr. Build. Mater. 2022, 327, 126936. [Google Scholar] [CrossRef]
  31. Bai, J.; Chaipanich, A.; Kinuthia, J.M.; O’Farrell, M.; Sabir, B.B.; Wild, S.; Lewis, M.H. Compressive strength and hydration of wastepaper sludge ash-ground granulated blastfurnace slag blended pastes. Cem. Concr. Res. 2003, 33, 1189–1202. [Google Scholar] [CrossRef]
  32. Jiang, Z.; Guo, X.; Li, W.; Chen, Q. Self-shrinkage behaviors of waste paper fiber reinforced cement paste considering its self-curing effect at early-ages. Int. J. Polym. Sci. 2016, 2016, 8690967. [Google Scholar] [CrossRef]
  33. Yaro, N.S.A.; Napiah, M.B.; Sutanto, M.H.; Usman, A.; Saeed, S.M. Performance evaluation of waste palm oil fiber reinforced stone matrix asphalt mixtures using traditional and sequential mixing processes. Case Stud. Constr. Mater. 2021, 15, e00783. [Google Scholar] [CrossRef]
  34. Kubba, H.Z.; Nasr, M.S.; Al-Abadaly, N.M.; Dhahir, M.K.; Najim, W.N. Influence of incinerated and non-incinerated waste paper on properties of cement mortar. IOP Conf. Ser. Mater. Sci. Eng. 2019, 671, 012113. [Google Scholar] [CrossRef]
  35. Park, Y.K.; Lee, J.H.; Jeon, I.K.; Kim, H.W.; Yoon, K.W. Evaluation of the basic properties of concrete with types on cellulose fibers. J. Korea Inst. Build. Constr. 2011, 11, 419–425. [Google Scholar] [CrossRef]
  36. Chen, Y.; Liu, P.; Yu, Z. Effect of environmental factors on concrete carbonation depth and compressive strength. Materials 2018, 11, 2167. [Google Scholar] [CrossRef] [PubMed]
  37. Filho, A.S.; Parveen, S.; Rana, S.; Vanderlei, R.; Fangueiro, R. Micro-structure and mechanical properties of microcrystalline cellulose-sisal fiber reinforced cementitious composites developed using cetyltrimethylammonium bromide as the dispersing agent. Cellulose 2021, 28, 1663–1686. [Google Scholar] [CrossRef]
  38. Kawashima, S.; Shah, S.P. Early-age autogenous and drying shrinkage behavior of cellulose fiber-reinforced cementitious materials. Cem. Concr. Compos. 2011, 33, 201–208. [Google Scholar] [CrossRef] [Green Version]
  39. Mei, C.T.; Jiang, L.Y.; Jiang, M.M.; Zhou, X.L.; Huang, H. Modification of cellulose extracted from waste newspaper. IOP Conf. Ser. Earth Environ. Sci. 2019, 295, 032009. [Google Scholar] [CrossRef]
  40. Srasri, K.; Thongroj, M.; Chaijiraaree, P.; Thiangtham, S.; Manuspiya, H.; Pisitsak, P.; Ummartyotin, S. Recovery potential of cellulose fiber from newspaper waste: An approach on magnetic cellulose aerogel for dye adsorption material. Int. J. Biol. Macromol. 2018, 119, 662–668. [Google Scholar] [CrossRef]
Materials 16 01374 g001 550
Figure 1. Photographs of (a) cement and (b) ground waste newspaper (WNP).
Figure 1. Photographs of (a) cement and (b) ground waste newspaper (WNP).
Materials 16 01374 g001
Materials 16 01374 g002 550
Figure 2. Scanning electron microscopy (SEM) images of (a) cement and (b) ground WNP.
Figure 2. Scanning electron microscopy (SEM) images of (a) cement and (b) ground WNP.
Materials 16 01374 g002
Materials 16 01374 g003 550
Figure 3. Particle size distribution of fine aggregates (NS: natural sand).
Figure 3. Particle size distribution of fine aggregates (NS: natural sand).
Materials 16 01374 g003
Materials 16 01374 g004 550
Figure 4. Carbonation depth measurement of (a) splitting samples and (b) the measurement of carbonation depth.
Figure 4. Carbonation depth measurement of (a) splitting samples and (b) the measurement of carbonation depth.
Materials 16 01374 g004
Materials 16 01374 g005 550
Figure 5. Mortar flow.
Figure 5. Mortar flow.
Materials 16 01374 g005
Materials 16 01374 g006 550
Figure 6. Compressive strength.
Figure 6. Compressive strength.
Materials 16 01374 g006
Materials 16 01374 g007 550
Figure 7. Split tensile strength.
Figure 7. Split tensile strength.
Materials 16 01374 g007
Materials 16 01374 g008 550
Figure 8. Carbonation resistance.
Figure 8. Carbonation resistance.
Materials 16 01374 g008
Materials 16 01374 g009 550
Figure 9. Correlation between compressive strength and carbonation depth.
Figure 9. Correlation between compressive strength and carbonation depth.
Materials 16 01374 g009
Materials 16 01374 g010 550
Figure 10. Drying shrinkage.
Figure 10. Drying shrinkage.
Materials 16 01374 g010
Materials 16 01374 g011 550
Figure 11. Microstructural analysis (SEM and energy-dispersive X-ray spectroscopy) results for (a) control, (b) WNP0.2, and (c) WNP0.8 samples.
Figure 11. Microstructural analysis (SEM and energy-dispersive X-ray spectroscopy) results for (a) control, (b) WNP0.2, and (c) WNP0.8 samples.
Materials 16 01374 g011
Table
Table 1. Chemical composition of cement.
Table 1. Chemical composition of cement.
TypeSiO2Al2O3Fe2O3CaOMgOK2OBlaine
(cm2/g)		Density
(g/cm3)
Ordinary Portland cement17.436.503.5764.402.551.1734303.15
Table
Table 2. Chemical composition of WNP.
Table 2. Chemical composition of WNP.
TypeCOSiAlCaK
Ground waste newspaper (WNP)40.638.39.59.02.30.3
Table
Table 3. Physical properties of fine aggregate.
Table 3. Physical properties of fine aggregate.
TypeFineness ModulusDensity
(g/cm3)		Water Absorption (%)
Natural sand (NS)2.452.601.0
Table
Table 4. Mixing proportions of mortars.
Table 4. Mixing proportions of mortars.
MixW/B
(%)		S/a *
(%)		WNP **
(C *%)		Water
(kg/m3)		Cement
(kg/m3)		NS
(kg/m3)		WNP
(kg/m3)
Control50420170340.07390
WNP0.20.2339.30.7
WNP0.40.4338.61.4
WNP0.60.6338.02.0
WNP0.80.8337.32.7
WNP1.01.0336.63.4
* S/a: sand to aggregate ratio, ** WNP: waste newspaper.
Table
Table 5. Energy-dispersive X-ray spectroscopy analysis result.
Table 5. Energy-dispersive X-ray spectroscopy analysis result.
MixElementWeight (%)б
ControlO44.8855.37
Ca24.5512.09
C14.4923.82
Si4.242.98
Al4.012.93
K0.260.13
WNP0.2O38.1240.52
Ca2.821.19
C28.0339.68
Si16.459.96
Al8.815.55
K2.190.95
WNP0.8O39.545.05
Ca4.21.92
C21.432.54
Si16.010.41
Al10.77.25
K1.90.86
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Lee, J.-I.; Kim, C.-Y.; Yoon, J.-H.; Choi, S.-J. Mechanical Properties of Cement Mortar Containing Ground Waste Newspaper as Cementitious Material. Materials 2023, 16, 1374. https://doi.org/10.3390/ma16041374

AMA Style

Lee J-I, Kim C-Y, Yoon J-H, Choi S-J. Mechanical Properties of Cement Mortar Containing Ground Waste Newspaper as Cementitious Material. Materials. 2023; 16(4):1374. https://doi.org/10.3390/ma16041374

Chicago/Turabian Style

Lee, Jae-In, Chae-Young Kim, Joo-Ho Yoon, and Se-Jin Choi. 2023. "Mechanical Properties of Cement Mortar Containing Ground Waste Newspaper as Cementitious Material" Materials 16, no. 4: 1374. https://doi.org/10.3390/ma16041374

APA Style

Lee, J. -I., Kim, C. -Y., Yoon, J. -H., & Choi, S. -J. (2023). Mechanical Properties of Cement Mortar Containing Ground Waste Newspaper as Cementitious Material. Materials, 16(4), 1374. https://doi.org/10.3390/ma16041374

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop